The invention discloses a high-strength self-lubricating metal ceramic bearing. The high-strength self-lubricating metal ceramic bearing is prepared from, by weight, 2.3-2.4 parts of ferric citrate, 3.1-3.5 parts of basic nickel carbonate, 25-30 parts of water, an appropriate amount of ammonium hydroxide, 2.9-3 parts of TiH2, 1.1-1.3 parts of nanocarbon, 15-15.4 parts TiC, 0.7-0.9 part of lubricant, 1-1.1 parts of C, 3.9-4.1 parts of Cr, 5.8-6 parts of W, 5.1-5.3 parts of Mo, 3.1-3.3 parts of V and 65-66 parts of Fe. Ferric citrate and basic nickel carbonate are used for carrying out coating modification on TiC, the bonding strength of a ceramic phase and a metal phase is improved, and the strength and the toughness of the bearing are greatly improved. Nanocarbon, ferrocene acetyenic ketone and ferric alginate are adopted, so that the lubricating performance and compactness in the pressing process are improved, the pore connectivity of sintered materials is good, the show porosity is improved, and the wear resistance of the bearing is extremely good.