Self-lubricating metal ceramic bearing with high bending resisting strength and preparing method of self-lubricating metal ceramic bearing

A cermet and strength technology, applied in metal processing equipment, coating, transportation and packaging, etc., can solve the problems of affecting the service life of bearings, failing to meet the bearing strength requirements, affecting the strength of cermets, etc., to prevent fracture and reduce the interface. effect, the effect of improving bond strength

Inactive Publication Date: 2016-03-09
ANHUI SILVER BALL BEARING
View PDF2 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, the metal and ceramic phases are directly sintered, and its boundary effect will affect the strength of the cermet, thereby affecting the service life of the bearing
The ratio of raw materials given in the article cannot meet the strength requirements of the bearing under high load conditions, and needs to be improved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0013] A self-lubricating cermet bearing with high bending strength, made of the following raw materials in parts by weight (kg): iron citrate 2.3, basic nickel carbonate 3.1, cuprous iodide 1.1, water 25, ammonia water, TiH 2 2.9, TiC5, Mo 2 C3, WC3, LaB 6 0.9, germanium dioxide 0.6, nano boron fiber 0.6, lubricant 0.7, C1, W8.6, Mo6.1, V3.1, Fe65.

[0014] The preparation method of the self-lubricating cermet bearing with high bending strength comprises the following steps:

[0015] (1) Add ferric citrate and cuprous iodide into water in a nitrogen atmosphere, heat to 60°C, stir at 90 rpm for 1.5 hours, add TiC, Mo 2 C, WC, LaB 6 , germanium dioxide, and nano-boron fiber, stirred for 1 hour, then added basic nickel carbonate and stirred for 3 hours, adjusted the pH value to 6 with ammonia water, heated to 90°C and kept stirring for 2 hours to obtain a gel;

[0016] (2) Heating the gel to 150°C and maintaining the temperature until no smoke is produced, then stopping the ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
hardnessaaaaaaaaaa
porosityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a self-lubricating metal ceramic bearing with high bending resisting strength. The bearing is prepared from raw materials including, by weight, 2.3-2.4 parts of ferric citrate, 3.1-3.5 parts of basic nickel carbonate, 1.1-1.3 parts of cuprous iodide, 25-30 parts of water, a proper amount of ammonium hydroxide, 2.9-3 parts of TiH2, 5-5.6 parts of TiC, 3-4 parts of Mo2C, 3-4 parts of WC, 0.9-1.1 parts of LaB6, 0.6-0.8 part of germanium dioxide, 0.6-0.8 part of nanometer boron fibers, 0.7-0.9 part of a lubricating agent, 1-1.1 parts of C, 8.6-9 parts of W, 6.1-6.3 parts of Mo, 3.1-3.3 parts of V and 65-66 parts of Fe. By means of the Mo2C, the WC, the LaB6, the germanium dioxide and the nanometer boron fibers, the thermal resistance and bending resisting strength of the bearing are improved, the bearing has the characteristics of high hardness, high strength and high tenacity, and cracking is prevented.

Description

technical field [0001] The invention relates to the technical field of cermet bearings, in particular to a self-lubricating cermet bearing with high bending strength and a preparation method thereof. Background technique [0002] The development of modern science and technology has higher and higher requirements on the friction, wear and lubrication performance of materials under high temperature conditions. The research and development of self-lubricating composite materials has become an important research hotspot in the field of tribology. Metal or ceramic-based self-lubricating materials are composite materials formed by adding solid lubricants into metal or ceramic matrix as components, and their tribological properties depend on the precipitation and dispersion distribution of solid lubricant contained in the matrix during the friction process. However, there are few solid lubricants that can withstand high sintering temperature without losing lubricating properties, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C49/08C22C49/14C22C47/14C22C101/20
CPCC22C47/14C22C49/08C22C49/14B22F2998/10B22F1/17B22F2003/023B22F1/10B22F3/1035
Inventor 余寅生
Owner ANHUI SILVER BALL BEARING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com