The invention relates to a furnace body lining
brick for the vertical furnace of a
sintering pelletizing machine, and particularly relates to a preparation method of a
silicon carbide abrasion-resistant fire-resistant furnace body lining
brick. The preparation method comprises the following steps of blending; mixing; carrying out
machine pressure forming; firing at high temperature; and adding
antioxidant metallic
silicon powder by taking
phosphate as a bonding agent, taking
sodium tripolyphosphate or
sodium hexametaphosphate as a deflocculant and taking
oxalic acid or
citric acid as a inhibiting agent, wherein a main material comprises waste high-
voltage electric porcelain or
bauxite chamotte, electric melting brown fused
alumina or
bauxite chamotte, electric melting brown fused
alumina or
bauxite chamotte, SiC granules, fine SiC
powder and fine high-quality clay
powder, the grain size of the waste high-
voltage electric porcelain or the bauxite chamotte is 1-3 mm, the grain size of the electric melting brown fused
alumina or the bauxite chamotte is less than 1 mm, the grain size of the electric melting brown fused alumina or the bauxite chamotte is more than or equal to 300 meshes, and the grain size of the fine high-quality clay powder is more than or equal to 300 meshes. According to the furnace body lining
brick, the usage temperature interval is 1100-1400 DEG C, the
compressive strength is more than 60 Mpa, the apparent
porosity is lower than 15%, the abrasion-resistant value is less than 5 cm<3>, and the
thermal shock stability is tested through a
water cooling method more than 20 times.