98 results about "Glass-coated wire" patented technology

Glass-coating is a process invented in 1924 by G. F. Taylor and converted into production machine by Ulitovski for producing fine glass-coated metal filaments only a few micrometres in diameter. In this process, known as the "Taylor-wire" or "microwire process" or "Taylor-Ulitovski process", the metal to be produced in microwire form is held in a glass tube, typically a borosilicate composition, which is closed at one end. This end of the tube is then heated in order to soften the glass to a temperature at which the metal part is in liquid state and the glass can be drawn down to produce a fine glass capillary containing a metal core. In recent years the process was converted to continuous one by continuously feeding the metal drop with new material. Although this process is simple enough it requires a lot of factors to be met at the same time. The continuous flow of metal that is being coated by the glass has to be melted at the same temperature as the glass otherwise there may be consistency problems which could lead to a change in the properties of the wire. This means that metals that have a high melting temperature can not be used because it may prove difficult to match the high melting point of the metal to a high melting point in a glass. The rate at which the metal wire is pulled also has to be monitored due to the fact that a fluctuation in the speed of pulling may cause a difference of width in the wire. Not only does the wire need to be pulled at the same rate but it also needs to be cooled in a stable environment, which is normally conducted by moving the wire through a stream of cooled water or oil. However. there are some apparatuses that can bypass some of these problems by heating the glass and the metal in separate chambers which allows for the use of metals with high melting points. Around the 1950s the Taylor-Ulitovski process was changed to a continuous feeding process of the materials in order to make these wires on a mass production scale.