39results about How to "Overcome the disadvantages of poor mechanical properties" patented technology

The invention discloses a preparation method of a modified diaphragm for a lithium-ion secondary battery as well as a prepared modified diaphragm and a preparation device and is aimed to solve the problem of lithium battery modified diaphragms in the prior art. The method concretely comprises the following steps of: (1), evenly dispersing special fiber or oxide and a binder into an organic solvent to prepare composite mixed liquid, and adding a cosolvent into the organic solvent; (2) evenly spraying the composite mixed liquid obtained in the step (1) on a polyolefin base membrane to form a primary composite membrane through an electrostatic spinning method; and (3), drying the primary composite membrane obtained in the step (2) and recycling the solvent, and then finally obtaining the finished product. The preparation method is convenient to operate and environmental friendly, can realize large-scale production and has strong feasibility.

The invention belongs to the technical field of membranes and in particular relates to a porous material-polymer gas separation composite membrane. The composite membrane comprises a separation layer and a supporting layer, wherein a porous material-polymer hybrid membrane is adopted as the separation layer; one of a porous flat plate and a tubular or hollow fiber membrane is adopted as the supporting layer; the porous material of the separation layer is metal-organic frame materials (MOFs) with large specific surface area and high gas adsorption. The MOFs are added into the separation layer so that the gas permeation and selectivity of the membrane are obviously improved; the separation layer and the supporting layer are compounded so that the membrane keeps good mechanical property, and the separation layer is allowed to exist in a compact or asymmetric structure. The composite membrane provided by the invention has high gas separation property, good mechanical property and wide industrial application prospect.

The invention discloses a high-performance tracking-resistant silicone rubber and a preparation method thereof. The tracking-resistant silicone rubber is prepared from the following raw materials in parts by mass: 100 parts of methylvinyl silicone rubber, 20-45 parts of fumed silica, 4-15 parts of hydroxy silicone oil, 0.3-1 part of hydrogen-containing silicone oil, 0.5-5 parts of nitrogenous silane, 0.1-2 parts of platinum compound and 0.5-4 parts of hexane 2,5-dimethyl-2,5-di-tert-butyl peroxide. The preparation method comprises the following steps: uniformly compounding the methylvinyl silicone rubber, fumed silica, hydroxy silicone oil and hydrogen-containing silicone oil in a kneader at room temperature, and carrying out heat treatment to obtain the silicone rubber basic rubber; and uniformly compounding the basic rubber and the other components in an open mill, and carrying out sectional vulcanization. The silicone rubber has excellent tracking resistance and mechanical properties, and can be used in the field of high-voltage insulation. The method has the advantages of accessible raw materials and simple processing technique, and is convenient for large-scale production.

The invention discloses water-based wood paint modified by vegetable oil and a preparation method of the water-based wood paint. The water-based wood paint is prepared from, by weight, 60-85 parts of aliphatic series modified polyurethane dispersoid, 1-3 parts of hardness-enhancing resin, 7-12 parts of water, 1-3 parts of wax emulsion, 2-5 parts of coalescing agents, 0.2-0.7 part of wetting dispersant, 0.1-0.5 part of flatting agents, 0.2-0.7 part of deforming agents, 1-2 parts of antifreezing agents and 0.3-0.7 part of thickening agents. According to the water-based wood paint modified by the vegetable oil and the preparation method of the water-based wood paint, formula adjustment is utilized, the environment-friendly type water-based hardness-enhancing resin is matched, and the hardness-enhancing resin comprises solvent-free water-based modified aldehyde ketone resin dispersoid. The water-based wood paint can reach or exceeds oil-based wood paint in physical and chemical technical index, and all comprehensive properties are excellent.

The invention belongs to the field of lignin-based hydrogel functional materials and discloses double-network lignin hydrogel as well as a preparation method and application thereof. The preparation method disclosed by the invention comprises the following steps: constructing a first network lignin hydrogel system in an alkaline solution by virtue of chemical cross-linking, and soaking the first network lignin hydrogel in an acidic solution, and producing a hydrophobic effect by utilizing lignin in the first network, thereby forming the double-network lignin hydrogel. The double-network ligninhydrogel prepared by the method has high mechanical strength, and the preparation method is simple, low in raw material cost, reproducible, green and environment-friendly. Moreover, the double-network lignin hydrogel has high ionic conductivity, and when the hydrogel serves as electrolyte for assembling a supercapacitor, extra ionic solution soaking is not needed, use of an extra diaphragm is notneeded, and the thickness and weight of the supercapacitor are effectively reduced. The specific capacitance value of the obtained capacitor is higher than the specific capacitance value of a conventional hydrogel electrolyte type flexible supercapacitor. In addition, the double-network lignin hydrogel has excellent charge and discharge cycle stability, compression resistance and bending resistance.

The invention which belongs to the material preparation field discloses an aliphatic / aromatic copolyester and a preparation method thereof. According to the aliphatic / aromatic copolyester, the molecular weight is greater than 20000, the ultimate strength is greater than 10MPa and lower than 60MPa, the breaking elongation rate is greater than 5% and lower than 3000%, Tg is greater than -70DEG C and lower than 40DEG C, Tm is greater than 50DEG C and lower than 270DEG C, and the biodegradation rate is greater than 30%. According to the preparation method of the aliphatic / aromatic copolyester, fusion polycondensation and ring opening polymerization are simultaneously carried out on an aromatic polyester monomer and an annular aliphatic polyester monomer in the presence of a catalyst to obtain the aliphatic / aromatic copolyester with irregularly distributed aromatic units and aliphatic units. The aliphatic / aromatic copolyester has the advantages of excellent mechanical performance, high molecular weight, realization of the complete biodegradation, and the like.

The invention provides a quick-molding self-healing hydrogel and a preparation method thereof. The preparation method comprises the following steps: by taking polyvinyl alcohol as a raw material, firstly, reacting the polyvinyl alcohol with glycidyl methacrylate to synthesize methacrylated polyvinyl alcohol, and then, carrying out esterification reaction on carboxyl on succinic anhydride and hydroxyl on the methacrylated polyvinyl alcohol to prepare carboxylated methacrylated polyvinyl alcohol; preparing a precursor mixed solution, mixing the precursor mixed solution with an iron tartrate solution containing ferric ions, and carrying out ultraviolet polymerization molding to prepare the quick-molding self-healing hydrogel with a physicochemical double-crosslinked single-network structure.The hydrogel has the advantages of being high in forming speed and excellent in self-healing performance, and has excellent mechanical properties.

The invention discloses a hybrid polymer electrolyte which comprises a metal salt and a cross-linked polymer formed by taking octamercapto polysilsesquioxane as an inner core and polyethylene glycol dimethacrylate as a cross-linking arm. The chemical structural formula of the cross-linked polymer is shown in the specification, wherein n is an integer from 4 to 113. The invention further disclosesa preparation method of the hybrid polymer electrolyte and an application of the hybrid polymer electrolyte. The hybrid polymer electrolyte is prepared based on the thiol-ene reaction initiated by theultraviolet light, and a photosensitizer does not need to be added in the preparation method. A POSS structure and a PEGDMA structure in the polymer electrolyte are combined, so that the polymer electrolyte can effectively overcome the defects of worse mechanical property and low conductivity of the traditional polymer electrolyte compared with the traditional polymer electrolyte.

The invention belongs to the technical field of chemical separation and environmental protection, and relates to a preparation method for a hydrophilic oil-water separation membrane imitating a cobwebstructure. The preparation method comprises the steps that multi-walled carbon nanotubes which are mutually intertwined are broken through inorganic acid at high temperature so as to obtain multi-walled carbon nanotube dispersion liquid, centrifuging and separating are carried out, and then supernate is taken; and 2-5 g of super-long MnO2 nanowires are added into per liter of water, mixed suspension liquid is stirred for 5-24 hours, the multi-walled carbon nanotube dispersion liquid and the super-long MnO2 nanowire dispersion liquid are mixed according to the volume ratio of 1:3-5:1 and thenare stirred, finally the multi-walled carbon nanotube / super-long MnO2 nanowire mixed solution is subjected to vacuum filtration in a vacuum filtration device with a commercial filtration membrane fixed so as to obtain a oil-water separation membrane imitating the cobweb structure, a hydrophilic filter membrane is peeled off, and drying is carried out so as to obtain the hydrophilic oil-water separation membrane imitating the cobweb structure. According to the preparation method, the super-long MnO2 nanowires are mutually intertwined so as to form a large-aperture supporting network, the multi-walled carbon nanotubes and the supporting network are mutually intertwined so as to form a small-aperture network structure, so that the cobweb structure is effectively imitated, and the purpose of enhancing the mechanical strength of the multi-walled carbon nanotube membrane is achieved.

The invention relates to a preparation method of a multi-responsive self-healing self-adhesive hydrogel. According to the invention, polyvinyl alcohol / borax is used as a main body structure of the hydrogel, and bacterial cellulose is added to improve the mechanical properties of the hydrogel. Tannic acid rich in benzenediol groups is used as a monomer for providing hydrogel adhesion, and a quinone structure obtained by oxidation of the tannic acid and an amino group of cystamine dihydrochloride are subjected to a Schiff base or Michael addition reaction to introduce disulfide bonds, so the hydrogel is endowed with redox responsiveness. The hydrogel is prepared through a boric acid ester bond, a hydrogen bond, pi-pi stacking and the like, and the defects that traditional polyvinyl alcohol hydrogel is poor in mechanical property, lack of tissue adhesion and the like are overcome. The hydrogel has good biocompatibility, multiple responsiveness, excellent mechanical property, self-adhesion and the like, so the application range of the hydrogel is expanded.

The invention belongs to the technical field of silicone rubber, and discloses a tracking-resistant silicone rubber, and a preparation method and application thereof, the tracking-resistant silicone rubber is mainly prepared from the following raw materials: polysilazane, a platinum complex, basic silicone rubber, white carbon black, silicone oil and a vulcanizing agent. According to the invention, a small amount of polysilazane and platinum complex is added, and the structural formula of polysilazane is as follows: (R1R2Si-NH) x (R3R4Si-NH) y, x and y are both integers of 0-300, and x and y are not 0 at the same time; R1, R2, R3 and R4 independently represent any one of H, CH3 and CmH2m + 1 respectively, and m is an integer between 1-7; and when the mass ratio of platinum atoms in the total formula raw materials is 5-15 ppm, the tracking resistance of the obtained silicone rubber finished product can reach 1A 4.5 grade, the system compatibility is good, the mechanical property is excellent, and the defect of poor mechanical property of the current tracking-resistant silicone rubber is overcome. The preparation method is simple, raw materials are easy to obtain, the application prospect is good, and thetracking-resistant silicone rubber is suitable for being applied to the field of high-voltage insulation.

The invention relates to black date fudge and a preparation method thereof, and belongs to the technical field of production of functional food. The black date fudge consists of 90-100 parts of black date, 0.4-0.6 part of konjac powder, 0.4-0.6 part of k-carrageenan, 0.3-0.45 part of citric acid and an appropriate amount of water. The preparation method specifically comprises the five steps of preparation of black date juice, preparation of konjac glucomannan mixed gel, boiling, condensation forming and drying. The black date fudge prepared through the method is sweet and tasty, nutrient-rich and convenient to carry, and has the effects of replenishing blood, resisting fatigue and relaxing bowel.

The invention discloses a high efficiency and continuous oil-water separation device, and belongs to the technical field of functional material application. The device comprises an oil collecting tank, a mechanical pump and an oil collecting device. The collecting tank is of a cube frame structure, metal substrate loaded with hydrophobic film is fixed on five surfaces of the cube frame, the five surfaces of the cube frame are in full contact with the oil and water mixture, and the sixth surface is an opening. The oil inlet of the mechanical pump is connected with the oil collecting tank through a pipeline, the oil outlet of the mechanical pump is connected with the oil collecting device through a pipeline. The high efficiency and continuous oil-water separation device overcomes such defects of polymer membrane that the processing amount is small, the separation speed is slow, and the wastewater can only be processed in batches. The continuous separation of oily wastewater can be conducted, and the high efficiency and continuous oil-water separation device provides a possibility of the application of membrane separation technology in oily wastewater treatment in actual life.

The invention discloses a preparation technology of a cotton paper double-sided adhesive tape. The preparation technology comprises the following steps: cutting modified cotton paper into a required size to serve as a base material, coating the surfaces of two sides of the base material of the adhesive tape with an adhesive to form a double-sided adhesive layer, adhering release paper to the adhesive layer to form a release paper layer, and rolling the release paper layer to obtain the cotton paper double-sided adhesive tape. The modified cotton paper is adopted as the base material of the double-sided adhesive tape, so the defect of poor mechanical properties of traditional cotton paper can be overcome; the modified cotton paper has high hydrophobicity and good biodegradability, so the effects of high mechanical properties and high hydrophobicity are achieved on the basis of meeting the environmental protection requirement; the soybean protein adhesive adopted in the invention has a high adhesive property, and can be stably attached to the surface of the modified cotton paper to increase the adhesive property; and the obtained cotton paper double-sided adhesive tape has the advantages of environmental friendliness, good mechanical properties, strong hydrophobic property and high adhesive property, and has a wide application prospect.

The invention belongs to the field of supercapacitors and discloses a flexible and solid supercapacitor, a preparation method and application thereof. The supercapacitor comprises a positive electrode, a negative electrode and an electrolyte interposed therebetween, wherein the electrolyte is double-network lignin hydrogel, and both the positive and negative electrodes are conductive electrodes. The double-network lignin hydrogel as the electrolyte in the present invention not only has high mechanical strength property, but also has a simple preparation method, low raw material cost, renewability, green environmental protection, and high ionic conductivity; when the hydrogel is used as the electrolyte to assemble the supercapacitor, additional soaking of an ionic solution is not required and additional use of a diaphragm is not needed, thereby effectively reducing the thickness and weight of the supercapacitor. The obtained capacitor specific capacitance value is higher than the current hydrogel electrolyte type flexible supercapacitor specific capacitance value. In addition, the supercapacitor has very good charging and discharging cycle stability, compression resistance and bending resistance.

The invention discloses a preparation method of high-strength and heat-resistant liquid crystal polymer spunbond nonwoven fabric. A liquid crystal polymer and an aid are sent into spunbond production equipment and subjected to melt extrusion, lateral blowing cooling, slit airflow drafting, lapping and hot rolling, and the spunbond nonwoven fabric is prepared. The liquid crystal spunbond nonwoven fabric with high strength and high heat resistance is prepared by means of the properties, including easiness in orientation, excellent mechanical performance, outstanding heat stability, chemical reagent resistance and the like, of the liquid crystal polymer, the problems that conventional spunbond nonwoven fabric has low strength and poor heat resistance are solved, and the high-strength and heat-resistant liquid crystal polymer spunbond nonwoven fabric can be widely used for the field with higher requirements for strength and heat resistance.

A sponge pavement and a preparation method thereof are provided, wherein the preparation method comprises the following steps: preparing a permeable concrete base layer; preparing a high-porosity titanium cement layer on the water-permeable concrete base layer, wherein the method for preparing the titanium cement comprises adding phosphate and dispersant to titanium salt aqueous solution, adding Portland cement, stirring, adding foaming agent and foam stabilizer after forming slurry, and fully stirring to form the titanium cement layer with high porosity on the base layer of the water-permeable concrete; forming a photocatalyst spraying layer of titanium dioxide on the titanium cement layer with high porosity. The preparation method of the sponge pavement overcomes the shortcomings of poormechanical properties of the permeable concrete and the shortcomings of the prior photocatalyst such as low photocatalytic degradation efficiency of VOC and NOx, short lasting time, etc., improves the retention amount and depth of the photocatalyst spraying, and obviously improves the long-term efficiency of the photocatalyst catalysis effect.

The invention relates to the technical field of the polyurethane foam hard plastics, and more specifically relates to a polyurethane hard plastic foam composition. The polyurethane hard plastic foam composition provided by the invention is composed of the following main raw materials in parts by weight: 75-90 parts of combined polyether, 2-5 parts of dimethyl ether, 2-5 parts of glass fibers, 4-10 parts of mullite and 2-5 parts of silicon carbide fine powder. The polyurethane hard plastic foam composition is capable of overcoming the shortcoming of poor mechanical properties of the existing polyurethane hard foam plastic, and has excellent strength and tenacity in addition to the previous properties such as high temperature resistance and fire resistance.

The invention discloses a post-operative anti-adhesion film material and a preparation method thereof. It belongs to the technical field of biomedical materials. The invention uses degradable biological materials such as konjac glucomannan and carboxymethyl cellulose with good biocompatibility. Sodium is the basic raw material, and the two are mixed to prepare a mixed sol. The modified sol is obtained through acid solution modification and microwave technology, and then the konjac glucomannan / carboxymethyl cellulose sodium composite is prepared by tape casting. Degradable membrane material to prevent adhesion after surgery. The degradation rate of the membrane material can be controlled by the double cross-linking degree of konjac glucomannan and carboxymethyl cellulose sodium. Not only the preparation process is simple and the cost is low, but also the Degradable membrane materials have good biomechanical properties. Cell experiments and animal experiments show that this membrane material can be widely used in the body and is an ideal degradable postoperative anti-adhesion material.

The invention belongs to the field of supercapacitors and discloses a flexible and solid supercapacitor, a preparation method and application thereof. The supercapacitor comprises a positive electrode, a negative electrode and an electrolyte interposed therebetween, wherein the electrolyte is double-network lignin hydrogel, and both the positive and negative electrodes are conductive electrodes. The double-network lignin hydrogel as the electrolyte in the present invention not only has high mechanical strength property, but also has a simple preparation method, low raw material cost, renewability, green environmental protection, and high ionic conductivity; when the hydrogel is used as the electrolyte to assemble the supercapacitor, additional soaking of an ionic solution is not required and additional use of a diaphragm is not needed, thereby effectively reducing the thickness and weight of the supercapacitor. The obtained capacitor specific capacitance value is higher than the current hydrogel electrolyte type flexible supercapacitor specific capacitance value. In addition, the supercapacitor has very good charging and discharging cycle stability, compression resistance and bending resistance.

The invention provides composite hydrogel dressing. The composite hydrogel dressing comprises a base material layer and a gel layer which is covered on the base material layer, wherein the base material layer is a net-like high-density polyethylene layer; and the gel layer is a PEG (Polyethylene Glycol) based hydrogel layer. The invention further provides a method for preparing the composite hydrogel dressing. The method comprises the following steps of: (a), enabling the polyethylene glycol and acrylic acid to generate esterification reaction in an organic solvent, and carrying out water separating treatment to obtain polyethylene glycol diacrylate; (b), dissolving the polyethylene glycol diacrylate in water, and uniformly mixing the obtained aqueous solution with an initiator to obtain a mixed solution; and (c), coating the mixed solution on the net-like high-density polyethylene layer to obtain the composite hydrogel dressing through gelation. The composite hydrogel dressing can be used for preparing medicinal wound dressing with excellent performances, which is sufficiently combined with the better mechanical performances of the high-density polyethylene materials with the characteristics of the PEG-based hydrogel. The preparation method of the composite hydrogel dressing is simple in method, easy to operate, safe and environment-friendly, and good in application prospect.

The invention relates to a modification method of collagen.The modification method comprises the following steps that 1, the collagen is dissolved into an acetate solution to prepare a saturated collagen solution; 2, a proteolytic enzyme is added into the saturated collagen solution, and reacting under heating is performed for 1-3 hours at the temperature of 40 DEG C-50 DEG C; 3, a chitosan acetic acid solution and a catalyst are added into a product generated in the step 2, and reacting under heating is performed for 0.5-2 hours at the temperature of 40 DEG C-50 DEG C, wherein the catalyst is prepared from, by mass, 15%-25% of Sm2O3, 25%-35% Eu2O3 and 45%-60% Gd2O3.By adding the chitosan acetic acid solution and the catalyst into the saturated collagen solution generated through reacting of the proteolytic enzyme, the collagen reacts with the chitosan acetic acid to generate a crosslinking substance, therefore, the jelly strength of the collagen is improved, the defect that the mechanical property of the collagen is poor is overcome, and the collagen can be applied to the food and medicine fields.

The invention discloses a preparation method of collagen polypeptide nano-sphere grafted hydration titanium oxide adsorption material, which comprises the following steps of: crushing and hydrolyzingthe waste collagen of tanning to obtain the hydrolyzed collagen polypeptide, taking the hydrolyzed collagen polypeptide and using a gel-sol method to obtain collagen polypeptide nanosphere suspension;adding the collagen polypeptide nano-ball suspension into a container, then adding montmorillonite agent and the titanic acid salt solution, stirring for 2-5 hours, adjusting the pH to 3-4 by using ahomogenizer, sealing the container, placing the container in a shaking table, reacting for 2-5 hours at the temperature of 40-45 DEG C, standing for 1-10h at room temperature, centrifugally separating, removing the supernatant, and freeze-drying the residual to obtain the collagen polypeptide nanospheres grafted hydration titanium oxide adsorption material. The method overcomes the defect that the hydration titanium oxide exhibits poor mechanical property since the application of hydrated titanium oxide in the field of inorganic absorption. The prepared collagen polypeptide nano-ball graftedhydration titanium is used for specific recovery treatment of uranyl ions by utilizing high adsorption capacity and high selectivity of hydrated titanium to uranyl ions.

The invention discloses a preparation method of a high-strength lignin hydrogel with adjustable mechanical properties, specifically: firstly, adding a polymer monomer into a solvent A, and then adding an initiator, lignin and a crosslinking agent , stir to dissolve completely, and obtain a polymer monomer solution; put the polymer monomer solution in N 2 React in an atmosphere to obtain a polymer long-chain solution, and then evaporate the polymer long-chain solution to dryness to obtain a polymer solid; then add lignin to solvent B to obtain a lignin solution, and then add it to the polymer Dissolving in the solid matter, and evaporating the solvent after complete dissolution; finally adding the obtained lignin xerogel to deionized water for swelling to obtain a high-strength lignin hydrogel. The high-strength lignin hydrogel prepared by the method overcomes the disadvantages of poor mechanical properties of the traditional lignin hydrogel, the tensile stress can reach 0.1-5.0 MPa, and the strain can reach 200%-2000%.

The invention provides a waterproof and anti-icing fly ash / PVC composite plate and its preparation method and application. The preparation method uses nitric acid acidification - silane coupling agent modification - stearic acid modification three-step combined method to modify the fly ash, and then mixes the modified fly ash and resin PVC for pressing , to prepare a fly ash / PVC composite sheet with excellent hydrophobic and ice-repelling properties and mechanical properties. The preparation method can effectively utilize fly ash waste resources from a wide range of sources, and prepare it into a composite sheet for application in the field of hydrophobic and ice-repellent, with simple preparation steps, low cost, green environmental protection, and excellent hydrophobic and ice-repellent properties and mechanical properties It can improve its mechanical properties and hydrophobic and ice-repellent properties while reducing the preparation cost of pure PVC waterproof and ice-resistant sheets. The composite sheet has great application prospects in the field of hydrophobic and ice repellent.

A method for preparing multi-responsive self-healing self-adhesive hydrogels. Polyvinyl alcohol / borax was used as the main structure of the hydrogel, and bacterial cellulose was added to improve the mechanical properties of the hydrogel. Tannic acid rich in catechol groups is used as a monomer to provide hydrogel adhesion, and the quinone structure obtained by oxidation of tannic acid undergoes Schiff base or Michael addition to the amino group of cystamine dihydrochloride The reaction introduces disulfide bonds, endowing the hydrogel with redox responsiveness. The hydrogel is prepared through borate bonds, hydrogen bonds, π-π stacking, etc., which overcomes the shortcomings of traditional polyvinyl alcohol hydrogels such as poor mechanical properties and lack of tissue adhesion. The hydrogel has good biocompatibility, multi-responsiveness, excellent mechanical properties and self-adhesion, etc., thereby expanding the application range of the hydrogel.

The invention relates to a modification method of collagen.The modification method comprises the following steps that 1, the collagen is dissolved into an acetate solution to prepare a saturated collagen solution; 2, a proteolytic enzyme is added into the saturated collagen solution, and reacting under heating is performed for 1-3 hours at the temperature of 40 DEG C-50 DEG C; 3, a chitosan acetic acid solution and a catalyst are added into a product generated in the step 2, and reacting under heating is performed for 0.5-2 hours at the temperature of 40 DEG C-50 DEG C, wherein the catalyst is prepared from, by mass, 15%-25% of Sm2O3, 25%-35% Eu2O3 and 45%-60% Gd2O3.By adding the chitosan acetic acid solution and the catalyst into the saturated collagen solution generated through reacting of the proteolytic enzyme, the collagen reacts with the chitosan acetic acid to generate a crosslinking substance, therefore, the jelly strength of the collagen is improved, the defect that the mechanical property of the collagen is poor is overcome, and the collagen can be applied to the food and medicine fields.

The invention discloses a high-performance anti-tracking silicone rubber and a preparation method thereof. In parts by mass, the raw material composition of the anti-tracking silicone rubber is: 100 parts of methyl vinyl silicone rubber, 20-45 parts of fumed silica, 4-15 parts of hydroxyl silicone oil, 0.3-1 part of hydrogen-containing silicone oil, 0.5-5 parts of nitrogen-containing silane, 0.1-2 parts of platinum compound and 0.5-4 parts of 2,5-dimethyl-2,5-di-tert-butylperoxyhexane. During preparation, mix methyl vinyl silicone rubber, fumed silica, hydroxyl silicone oil, and hydrogen-containing silicone oil in a kneader at room temperature, and heat-treat to obtain a silicone rubber base rubber; mix the base rubber and other components of the formula Mix evenly on the open mill, and then vulcanize in stages. The silicone rubber of the invention has excellent tracking resistance and mechanical properties, and can be applied in the field of high-voltage insulation; and the raw materials are easy to obtain, the processing technology is simple, and it is convenient for large-scale production.

The invention discloses a method for preparing a hydrophobic flame-retardant polyurethane coating. The method comprises the following steps: 1. weighing various raw materials; 2. mixing the raw materials evenly to obtain a mixture; The organic silicon continues to react to obtain a prepolymer; 4. Add water dropwise to emulsify, vacuumize to remove the solvent, and obtain a hydrophobic flame-retardant polyurethane coating. The invention can improve the utilization efficiency of cyclodextrin and rosin, a natural renewable resource, introduce a rigid ring structure into polyurethane, and overcome the shortcomings of poor water resistance, heat resistance and surface properties of existing water-based polyurethane coatings. The flame retardant segment is introduced into the polyurethane skeleton structure to synthesize intrinsic flame retardant polyurethane coatings, which overcomes the shortcomings of poor mechanical properties of additive flame retardant polyurethanes, and uses organic silicon modification to further overcome the shortcomings of poor water resistance of waterborne polyurethane coatings, and obtains Stable storage of polyurethane coatings, improve the comprehensive performance of polyurethane coatings.