246results about How to "Reduce the amount of water added" patented technology

The invention discloses a monolithic cellular catalyst for SCR smoke denitration, which adopts TiO2 powder as a substrate. The catalyst is added with active ingredients and additive at the same time. The active ingredients comprise TiO2, WO3, MoO3, V2O5, ZrO2 and MnO2. The additive comprises water reducer, binder, pore-forming agent, extrusion assistant and glass fiber. The invention further discloses a preparation technology for the monolithic cellular catalyst for SCR smoke denitration, comprising the following steps: dry mixing, kneading and pugging to obtain a mud section with good plasticity and a compact structure; extruding to obtain the blank of the monolithic cellular catalyst; drying and baking to obtain the monolithic cellular catalyst for SCR smoke denitration. The invention has simple preparation technology, greatly reduces the water quantity during the kneading process through adding the water reducer which is adopted as one active ingredient, reduces the maintaining conditions of the catalyst after being formed, and improves the strength, abrasion resistance and yield for forming the catalyst.

The invention relates to a pavement/bridge deck concrete fast mending material and application thereof. The mending material comprises the following raw materials by weight: 20 to 30 parts of sulphoaluminate cement, 8 to 10 parts of ordinary Portland cement 52.5, 5 to 10 parts of polymer powder, 0.5 to 1.5 parts of aluminium sulphate, 1 to 2 parts of water glass, 0.1 to 1 part of organic silicon, 1 to 2 parts of gypsum, 2 to 3 parts of slag, 0.1 to 0.5 part of silica micropowder, 0.5 to 1 part of an HPCA high-performance concrete expansive material, 3 to 5 parts of fly ash, 20 to 30 parts of washed-out and dried sand, 25 to 30 parts of corundum, 3 to 5 parts of composite fiber, 1 to 3 parts of a polycarboxylate superplasticizer, 0.1 to 0.5 part of boric acid, 0.1 to 0.3 part of sodium gluconate, and 0.2 to 1 part of lithium carbonate. The mending material is high in early strength, and has the advantages that traffic can be opened fast only 1 to 2 hours after mending is completed, so as to reduce traffic jams, and effectively reduce the generation of traffic accidents.

The present invention belongs to the technical field of 3D printing materials, and relates to a 3D printing gypsum ink, and the 3D printing gypsum ink is prepared from the following components by weight: 60% to 93% of gypsum powder, 2% to 20% of filler, 4% to 18% of a modifying solvent and 0.5% to 5% of a coagulant. The present invention also discloses a preparation method of the 3D printing gypsum ink, and all the raw materials are mixed and stirred evenly to obtain the 3D printing gypsum ink. The problems of low strength, poor mobility, coarse particles, poor toughness and high cost in the prior art can be solved, and an economical 3D printing forming material with industrial potential, high speed, good precision and low use cost is developed.

The invention discloses a continuous casting monolithic stopper and a method of manufacture thereof.The monolithic stopper comprises a stopper body, a steel core inserted into the stopper body and a head connected to the lower end of the stopper body, the surface of the steel core is provided with an anchor, the surface of the monolithic stopper is coated with Al2O3 coating; the stopper body is made by casting castables comprising mullite, the head is made by casting castables comprising corundum and sintered mullite, and the monolithic stopper is manufactured by monolithic casting.The stopper obtained herein is good in monolithicity, is free of brick joint and head shedding problems of sleeve brick stoppers, has good thermal shock resistance, high strength and good resistance to molten steel scour erosion, is simple to manufacture and low in cost, and is suitable for stopping a tundish nozzle under low continuous casting, high-oxygen steel continuous casting and skid flow control.

The invention discloses a steel ladle cover light mullite castable material including an aggregate and a matrix and including the components in parts by weight: the aggregate comprising 30-70 parts of light mullite balls, and the matrix comprising 0-15 parts of tabular corundum, 0-15 parts of mullite particles, 5-15 parts of an alumina micro powder, 5-15 parts of a mullite micro powder, 0-8 parts of a silicon micro powder, 5-15 parts of a binder, and 0.1-0.4 part of a water reducer. The invention also discloses a preparation method of the steel ladle cover light mullite castable material, wherein the preparation method comprises the following steps: firstly, mixing the matrix parts evenly; and then adding the light mullite balls, and then mixing evenly and packing. The steel ladle cover light mullite castable material has the advantages of simple production, high production efficiency, convenient field construction, low volume density, low thermal conductivity coefficient, excellent thermal shock resistance, high strength, and good high temperature volume stability and the like, and has the use temperature reaching up to 1550 DEG C.

The invention discloses a high-temperature walking beam furnace beam and column insulation lining slag-adhesion-preventing coating. The coating comprises the raw materials of, by weight: 55-60% of the bauxite clinker, 5-10% of magnesium aluminate spinel, 5-10% of calcined anthracite, 2-5% of flake graphite, 3-6% of silicon carbide, 4-6 % of alpha-Al2O3 powder, 4-6% silica micro-powder, 5-7% of calcium aluminate cement, 0.5-1.5% of metal silicon powder, 2.5-3.5% of water-soluble epoxy resin and water-soluble curing agent, 0.05-0.10% of explosion-proof fiber, 0.1-0.15% of sodium hexametaphosphate, 0.05-0.10% of an organic reducing agent, and 0. 04-0.07% of an organic silane coupling agent. With the slag-adhesion-preventing coating, the comprehensive targets are achieved, that service lives of the furnace beam and the column insulation lining are prolonged, furnace energy consumption and insulation lining surface slag adhesion amount are reduced, furnace maintenance cost is reduced, and high-temperature-oriented silicon steel production efficiency is improved.

The rice bran producing process of regulating the moisture content of rice bran to 15-24 % includes spreading sieved rice bran in a container, setting the container inside one special moisture maintainer, microwave heating for 2.5-3.5 min to 101-120 deg.c and final natural cooling. The special moisture maintainer consists of one horizontal hollow shelf and one cover with pendulous splinters. The present invention is superior in that heating rice bran in a special moisture maintainer to form stable steam environment is favorable to deactivation of enzyme in rice bran, reduce water and microwave power consumption.

The invention, belonging to the field of ornaments, relates to a method for producing a gypsum relief product, comprising the following steps: (1) preparing slurry, (2) making a die, (3) grouting, and (4) surface protection of the product. The step of preparing slurry comprises the following steps: 1, material preparation: high strength gesso a, redispersible polymer powder b, peach gum c, sodium tetraborate d, chopped fiber e, and water f; 2, preparation method: mixing f, b, c, d, and e with the weight ratio of f to b to c to d to e of 1000 to (40-50) to (3-5) to (2-3) to (15:20) to obtain a mixed emulsion g, and mixing a with g with the weight ratio of a to g of 1 to 1 to obtain slurry h. The gypsum relief product disclosed herein has the advantages of high surface hardness, scratch resistance, good toughness, impact resistance, strong weatherability, water resistance, and light weight.

The invention discloses a castable for a ladle deslagging plate, and a preparation method and an applicable of the castable. The castable for the ladle deslagging plate comprises the following components in parts by weight: 50-70 parts of mullite, 10-20 parts of andalusite, 10-20 parts of bauxite powder, 3-5 parts of pure calcium aluminate cement, 4-6 parts of aluminum oxide micropowder, 3-5 parts of silicon carbide micropowder and 2-3 parts of compound additive, wherein the compound additive is a combination of two or more of organic fiber, steel fiber, and sodium tripolyphosphate or sodium hexametaphosphate. When the castable is cast on the outer surface of the ladle deslagging plate, the service life of the ladle deslagging plate can be prolonged and the preparation cost can be reduced; and the preparation method of the castable for the ladle deslagging plate is simple, and easy to operate.

The invention belongs to the field of unshaped refractory materials and in particular relates to an iron trough castable containing 70% or above of high-aluminum aggregates. The iron trough castable comprises the components in percentage by mass: 70-74% of high-aluminum aggregates, 2-3% of spherical asphalt, 1.6-2% of calcium aluminate cement, 5.5-7.5% of alumina micropowder, 2.5-3.5% of compositesilicon dioxide micropowder, 12-13% of composite silicon carbide powder, 1-1.2% of composite antioxidant, 0-0.1% of anti-explosion fibers and 0.12-0.2% of dispersant. By combining with a plurality ofimprovement means, the addition amount of the high-aluminum aggregates can be effectively increased (the addition amount can reach 70% or above), and the water addition amount used when the castableis prepared is reduced; and proved by actual industrial applications, the use effect of the iron trough castable in a non-impact region of a main trough reaches the use effect of a common corundum iron trough castable, so that the production cost of the iron trough castable and the whole contracting cost of an iron trough can be greatly reduced.

The invention provides a preparation method of an iron runner castable containing graphene oxide, comprising the following steps: step 1: premixing materials, and mixing raw materials and auxiliary materials evenly, wherein the raw materials contain dense corundum, white corundum, carborundum, alpha-Al2O3 micropowder, silicon dioxide micropowder, aluminate cement, ball pitch and monatomic silicon powder, and the auxiliary materials comprise a water reducer and explosion-proof fiber; step 2, adding graphene oxide solution and an antioxidant for the graphene oxide. By applying the technical scheme, the preparation method has the following effects: (1) preparation steps are simplified, and are suitable for industrial production; (2) the added graphene oxide can reduce the usage amount of common carbonaceous materials such as the ball pitch, and the production of poisonous and carcinogenic gas can be reduced when the iron runner castable is used in a high temperature environment; (3) the content of carbon in the castable can be effectively increased by the addition of the graphene oxide, the additive quantity of water and the porosity of the iron runner castable can be reduced, and the structural strength, thermal shock resistance and corrosion resistance of the iron runner castable are enhanced.

The invention discloses a long-service-life iron runner castable for hot repair. The long-service-life iron runner castable for hot repair comprises the following components in percentage by mass: 56%-64% of brown fused alumina, 5%-13% of silicon carbide, 2%-3% of ball pitch, 1.5%-2.5% of calcium aluminate cement, 8%-12% of alumina micro-powder, 1.5%-2.5% of silicon dioxide micro-powder, 11%-13% of silicon carbide powder, 1%-2% of a composite antioxidant, 0.1%-0.3% of metal aluminum powder, less than 0.1% of explosion-proof fibers, 0.2%-0.4% of a dispersing agent and 0.08% of a coagulant. Thenovel coagulant is used for the iron runner castable, thus, the metal aluminum powder in the iron runner castable produces hydrogen ahead of time, the gas is generated to open an exhaust hole when thecastable is not cured, then, the castable is matched with the suitable metal aluminum powder and the low-melting-point explosion-proof fibers, and it ensures that the castable has excellent high-temperature usability while meeting the condition of construction.

The invention discloses a microporous high-penetration-resistance high-aluminum casting material, and a preparation method and an application method thereof. The casting material is prepared from the following components in parts by weight: 51-95 parts of aggregate, 23.5-41.5 parts of powder, 3-6 parts of composite dewetting agent and 0.02-0.4 part of composite water reducing agent, wherein the aggregate is superfine bauxite chamotte; and the powder contains 180-mesh superfine bauxite fine powder, 800-mesh superfine bauxite fine powder, CA-70 cement, alpha-Al2O3 micro powder and SiO2 micro powder. A lining cast by the microporous high-penetration-resistance high-aluminum casting material provided by the invention is low in porosity, small in pore size of air pores and high in resistance to aluminum alloy liquid-state or vapor-state element penetration and corrosion; the aluminum alloy melt penetration resistance is improved; the mechanical strength is high, the high-temperature volume is stable, and the thermal shock resistance is favorable; and nodulation and bulge phenomena at the three-phase juncture can be effectively avoided.

The invention relates to a wear-resistant and thermal shock-resistant lining for an air supply branch pipe of an iron-making blast furnace and a preparation method thereof. The wear-resistant and thermal shock-resistant lining comprises the following raw materials in percentage by weight: 20.65-31.85 percent of substrate, 65-72 percent of aggregate, 0.05-0.15 percent of explosion-proof fiber, 3-7 percent of a bonding agent and 0.1-0.2 percent of a dispersing agent. The preparation method of the wear-resistant and thermal shock-resistant lining comprises the following steps: mixing the raw materials with a certain weight of water into pouring material; after pouring, curing and carrying out thermal treatment to prepare the lining for the air supply branch pipe. In the wear-resistant and thermal shock-resistant lining, the substrate is composed of andalusite fine powder with 200 meshes, corundum fine powder, alpha-Al2O3 micro powder and SiO2 micro powder; the aggregate is composed of clay clinker particle and andalusite particle with a grain size grade of 3-0.074 mesh. The wear-resistant and thermal shock-resistant lining and the preparation method thereof have the benefits that in the use process, mullite converted from the andalusite can form a weaving structure with the other raw materials and can play bridging and toughening roles, so that the thermal shock resistance of raw material products is improved; the expansion effect of the mullite is durable, the volume stability is good, and the service life of the lining is long.

The invention discloses a round granule ore fertilizer pelleting process which comprises the following steps: I) preparing raw materials; II) performing stirring mixing; III) performing pelleting; IV) screening wet granules; V) performing first-stage drying; VI) performing second-stage drying; VII) cooling; VIII) screening a finished product; IX) packaging the finished product. The invention further discloses a pelleting device with the process. The pelleting device comprises a mixing machine, a disc pelleting machine, a staged rotary screen, a rotary drying machine, a vibration fluid bed dryer, a rotary cooling machine and a vibration screen. The round granular ore fertilizer pelleting process is high in pelleting disc balling yield, low in granule crushing rate in the drying procedure, high in yield of the whole system, advanced in pelleting process, low in drying cost, small in water amount, high in granule strength of a round granule ore fertilizer product, good in sphericity degree and high in market acceptance degree.

The invention relates to an improved process for producing sodium thiosulfate in the field of the chemical industry. The improved process uses alkali waste water deoxidized by an aromatic nitro compound sodium sulfide as a raw material and comprises the process steps of sulfur oxidization, introduction of sulfur dioxide into the alkali waste water, heat filtration, sulfur treatment, concentration,active carbon decoloration, filtration, crystallization and separation. The improved process is characterized in that the technological processes of the sulfur oxidization and the introduction of sulfur dioxide into the alkali waste water comprise the following steps: crushing solid sulfurs and then inputting the crushed sulfur into a combustion furnace; introducing air into the furnace so as toensure that the sulfur powder is oxidized into a sulfur dioxide gas; imputing the sulfur dioxide gas into a reaction kettle to react with sodium hydrate and sodium sulfide in the alkali waste water soas to generate sodium sulfite; and then obtaining the finished product of the sodium thiosulfate through the process steps of the heat filtration, the sulfur treatment, the concentration, the decoloration, the filtration, the crystallization and the separation. The process saves energy resources and reduces the cost.