The invention relates to a
polypropylene foaming material for opening aperture and a preparation method thereof, which pertains to the polymeric material field and aims at solving the disadvantages of the existing foaming material for opening aperture of high technological cost, difficulty in
recovery, environmental
pollution and complicated operation. The foaming material of the invention consists essentially of
polypropylene resin composition, and the composition consists of
polypropylene A with a melt flow velocity of 0.01 to 10g / 10min,
polyethylene B with an Mw of 600,000 to 5,000,000, a compatilizer C and a normal additive; the additive accounts for no more than 10 weight percent, and B accounts for 1 to 40 weight percent while C accounts for 0 to 5 weight percent in the mixture of A, B and C. The composition is heated over the molten temperature thereof in the invention, a physical
foaming agent with 1 to 20 percent of the melt in weight is injected under the pressure larger than the pressure of the melt, then the mixture is exposed under the environment with a pressure lower than the pressure of the composition melt, thus the polypropylene foaming material for opening aperture is prepared. The invention has the advantages of low cost, simple operation, no
pollution, uniform and unblocked foam pores, and the opening percentage of at least 50 percent.