2281results about "Non-woody plant/crop pulp" patented technology

Cellulose nanofibers have been processed from renewable feedstock in particularly from natural fibers, root crops and agro fibers, wherein the pulp was hydrolysed at a moderate temperature of 50 to 90 degree C., one extraction was performed using dilute acid and one extraction using alkali of concentration less than 10%; and residue was cryocrushed using liquid nitrogen, followed by individualization of the cellulose nanofibers using mechanical shear force. The nanofibers manufactured with this technique have diameters in the range of 20-60 nm and much higher aspect ratios than long fibers. Due to its lightweight and high strength its potential applications will be in aerospace industry and due to their biodegradable potential with tremendous stiffness and strength, they find application in the medical field such as blood bags, cardiac devices, valves as a reinforcing biomaterial.

Disclosed is a cellulose nonwoven fabric containing cellulose fibers having a maximum fiber diameter of not more than 1500 nm and a crystallinity determined by solid state NMR techniques of not less than 60%. The porosity of the cellulose nonwoven fabric is not less than 40% and not more than 99%.

A composite sheet material includes, in an exemplary embodiment a porous core that includes at least one thermoplastic material and from about 20 weight percent to about 80 weight percent of natural fibers based on a total weight of the porous core. The natural fibers include at least one of kenaf fibers, jute fibers, flax fibers, hemp fibers, cellulosic fibers, sisal fibers, and coir fibers.

Fibrous structures that exhibit improved consumer recognizable properties, especially a VFS of greater than about 11 g / g, and to methods for making such fibrous structures are provided.

The invention belongs to a technical field of chemical fiber, in particular to a preparation method of cellulose pulps of reed or straw and the like. The method comprises the following steps of: firstly, carrying out steam explosion treatment on reed or straw raw materials in steam explosion treatment equipment, secondly, washing raw materials of reed or straw and the like after steam explosion treatment with water, and soaking the washed materials in an organic solvent for treatment to finish cellulose pulping technology. The technology utilized by the invention has obvious advantages of shortening the technological process, saving energy, protecting the environment (the organic solvent can be recycled by distilling to reutilize), and being beneficial to clean production and environmental protection.

A method to prepare, pulp, and bleach cannabis bast and hurd fibers to allow for the fiber to be incorporated into absorbent cellulosic structures on a wet-laid paper machine while keeping the pectin within the fibers. The wet laid paper machine can use the ATMOS, NTT, ETAD, TAD, or UCTAD method to produce the absorbent cellulosic structure. Absorbent cellulosic structures are produced with the cannabis bast and hurd fibers or with the bast fibers alone with the hurd fibers being combined with paper mill sludge or dust to form a fuel pellet.

The invention discloses a method for manufacturing high-breathability non-woven wallpaper body paper and a product. The existing non-woven wallpaper has the disadvantages that the hand feel thereof is not soft enough, the principal plane stereoscopic impression is not strong and the opacity degree is low. The method of the invention comprises the following steps: beating plant fiber containing chemical wood pulp until the beating degree is 20-30OSR, and mixing with non-plant fiber containing chemical fiber; adding chemical addition agent into the mixed fiber; manufacturing the mixed fiber containing the chemical addition agent into body paper semi-finished products by utilizing a fourdrinier wire or inclined wire paper machine; mixing pigment, chemical addition agent and adhesive to form coating liquor, carrying out dip coating on the body paper semi-finished products inside or outside the machine; and drying and finishing the body paper subject to dip coating, and rolling the body paper to form finished paper of body paper, thus obtaining non-woven wallpaper which contains continuous fiber, has high breathability, and can be directly printed. The principal plane has natural lines; and the finished paper has the advantages of soft hand feel, good processability, excellent shape stability, rich color, distinct image and strong stereoscopic impression.

A composite web and process for manufacture from post-industrial scrap wherein the fibers are pre-opened and cut to an average fiber length of about 4 mm. A scrap fiber component and a cellulosic component of such fibers are blended into a fiber furnish. The scrap fiber component includes at least 15% synthetic fibers and may include a blend of natural fibers, high melting point synthetic fibers, and low melting point synthetic fibers. The cellulosic component may include post-industrial cotton fibers which may be refined before blending with the scrap fiber component. The fiber furnish is processed into an intermediate web such as by a drylaid or a wetlaid nonwoven process. The intermediate web is saturated with a latex binding agent and pressed and / or dried to form a composite web capable of further processing into molded or formed consumer or industrial products. The process is capable of producing a high basis weight composite web.

According to one embodiment of the invention, a system for processing biomass includes a water-impermeable bottom liner, a gravel layer supported by the bottom liner, a drain pipe disposed within the gravel layer, a biomass input device operable to deliver biomass over the gravel layer to form a biomass pile, a lime input device operable to deliver lime to the biomass for pretreating the biomass, a distribution pipe elevated above the gravel layer, and a pump operable to circulate water through the biomass pile by delivering water to the distribution pipe and receiving water from the drain pipe after it has traveled through the biomass pile.According to another embodiment, a method for biomass pretreatment with alkali, conducted at ambient pressure for approximately 4-16 weeks at temperatures ranging from approximately 25° C. to 95° C. Biomass may be lignocellulosic biomass and may be rendered suitable for enzymatic digestion or pulp production.

A multi-ply absorbent product having a wet scrubbing resistance greater than 120 revolutions and a basis weight of between 30 and 50 grams per square meter. A heated adhesive is applied between two single plies / webs, the multiple plies are embossed according to particular parameters, and the embossed webs are compressed with a marrying roll. The adhesive is heated to a temperature of between approximately 32 degrees C. to 66 degrees C. for application between the multiple plies. For each ply, the embossed area generally occupies between approximately 5 to 15% of the total surface area of a surface of the ply, the depth of embossment of the surface is generally between approximately 0.28 and 0.43 centimeters deep, and the embossment of the surface is generally between approximately 0.04 to 0.08 square centimeters in size.

The enzymatic straw material pulping process includes three stages of mechanical pre-treatment, enzyme treatment and chemical pulping or chemical-mechanical pulping. After being pretreated mechanically in a pulp grinder, the straw material is treated with hemicellulase liquid or mixed enzyme liquid comprising hemicellulase and lignin peroxidase at pH 3.5-6.5 and 40-60 deg.c for 1-10 hr. In chemical pulping, the material is presoaked with waste pulp-making liquor before extruding out wastes liquor and digested; and in chemical-mechanical pulping, the material is first treated with EDTA, NaOH and H2O2 at 40-80 deg.c for 30-120 min and then ground to form the pulp. The present invention is used in papermaking enterprises with straw as material and has the advantages of low pollution load, high, paper pulp quality, easy-to-process waste liquor, etc.

The present invention relates to a paper pulp prepared by using rice straw and wheat straw as raw material. The breaking length of said paper pulp is 4500-8100 km. and its tearing strength is 180-280 mN. Besides, said invention also provides its preparation method and concrete steps.

The present invention discloses a method for preparing high-hardness pulp by using graminoid plant as raw material and its cooking process. The hardness of said high-hardness pulp is equal to Kappa number 24-50. The described cooking method includes the following steps: preparing graminoid plant raw material, soaking said raw material, feeding said raw material into a cooker, adding cooking liquor into said cooker, introducing steam to make heating operation to attain the requird pressure, then heat-insulating to the required time.

The present invention discloses a bleached chemical pulp prepared by using graminoid plant as raw material and its preparation method. Said invention is characterized by that it utilizes a high-hardness pulp which is obtained by using cooking process and whose permanganate number is 16-28 and equal to Kappa number 26-50 and makes said high-hardness pulp undergo the processes of pulp-washing and bleaching treatment so as to obtain the invented bleached chemical pulp whose breaking length is 4500-8000 m and folding endurance is 20-70 times.

The invention discloses a method for preparing a fiber wallboard through a wet process. The method comprises the following steps: 1) pulping: mixing non-wood type natural plant fiber pulp with gramineous plant pulp according to a dry weight ratio of 1:0-1.5 and adding water into the raw materials to dilute the pulp; 2) storing the pulp: placing the obtained mixture pulp into a pulp storage pond and adding water for dilution; 3) carrying out suction filter and formation: inputting the pulp obtained from the previous step into a die cavity for cold-pressing, dehydration and formation so as to obtain a wet blank; and 4) carrying out hot-pressing formation and drying; transferring the wet blank into a hot-pressing mould for hot pressing, removing water generated during the hot pressing, and obtaining the fiber wallboard. The fiber wallboard obtained by using the method has the characteristics of environment-friendliness and high strength.

The invention relates to a comprehensive utilization method for grass straws. Firstly, cellulose in the straws is utilized to pulp to serve as a raw material of paper pulp; during the pulping, lignin is dissolved in a stewing liquor to become a main constituent of a solid in a black liquor; the lignin is fully refined through the stewing and has easy degradation, and crops are easy to absorb, so the black liquor becomes a good organic fertilizer; at the same time, a fulvic acid with considerable quantity can be formed under conditions of high temperature and high pressure during the pulping, so the black liquor can be prepared into a high-quality fulvic acid fertilizer; the aim of comprehensive utilization of the grass straws is achieved through the steps, and the good economic benefit can be obtained thanks to the fact that the paper pulp and the fulvic acid fertilizer are expensive.

A layered fibrous structure having a machine direction, cross machine direction, and Z-direction. The fibrous structure also has a consumer side and first and second layers in the Z-direction where the first layer has a plurality of trichomes. The trichomes make up greater than about 0.1%, by weight, of the fibrous structure.

Disclosed is a multi-layer paper suitable as a material for preparing heat-sensitive stencil printing masters. The multi-layer paper is produced by combining a plurality of thin paper layers by paper making. The multi-layer paper has a peel strength of 10 N / m or less and may be delaminated into at least two tissue sheets.

Provided is a process for producing biomass-based product from straw hemicellulose and utilizing the components thereof thoroughly. Steam-explosion and acid-hydrolysis are combined in the pre-treatment of straw in the process, thus a higher concentration of a sugar liquid can be obtained, and furfural and acetic acid can be recovered. The hemicellulose obtained by the pre-treatment can be used directly as ferment materials for producing butanol, succinic acid, butylene glycol, lactic acid, hydrogen and firedamp, which reduces the cost of these biomass-based products. The cellulose and lignin obtained by extracting the straw with an alkaline solution can produce products, such as sodium hydroxymethyl cellulose etc. In the process, all components in the straw can be utilized thoroughly and waste and pollutant will not be produced.

A process for producing a pulp from cellulose-containing material, wherein the material is reacted with formic acid as the solvent, and cooked at approximately the boiling temperature of the solvent, whereby return condensation is used. Annual plants, deciduous or coniferous wood can be used as the cellulose-containing material. In one variant of the process, the cellulose-containing material is only slightly warmed, whereby backflow cooling is used, and then a precisely predetermined quantity of hydrogen peroxide is slowly added to the liquid at a constant rate. This process variant can be repeated at a lower cooking temperature. The pulp thus obtained is preferably utilized in the production of cellulose, and in particular in the production of paper or cardboard. It is proposed that the lignin, which is isolated from the cellulose-containing material, have further applications, whereby such lignin is, after the pulp has been separated from the solvent, itself precipitated out in water. The lignin thus obtained can be used as a new building material, as a filler material or as an output substance to be used in the manufacture of aromatic products.

A tampon pledget includes crosslinked cellulose fibers having microstructures treated to provide improved absorbency and higher wet strength. The fibers are treated with a crosslinking agent to provide at least one of a molecular weight between crosslinks of from about 10 to 200 and a degree of crystallinity of from about 25% to 75%. The crosslinking agent includes citric acid in 1% by weight. The crosslinking agent may further include sodium hypophosphite in 1% by weight. In another embodiment, the crosslinking agent may be a difunctional agent including a glyoxal or a glyoxal-derived resin. In still another embodiment, the crosslinking agent is a multifunctional agent including a cyclic urea, glyoxal, polyol condensate. The crosslinking agent is added in an amount from about 0.001% to 20% by weight based on a total weight of cellulose fibers to be treated and, preferably, in an amount of about 5% by weight.

The invention relates to a comprehensive utilization method of straw raw materials. The method is characterized by comprising the following steps: a, carrying out solid-liquid separation on steam-exploded straws, using an alkaline cooking method to process solid bodies of the steam-exploded straws, and extracting good xylogens from an alkaline extract liquor by an acid-out method; b, carrying out enzymolysis on the extracted residues in the step a to obtain zymolytic residues and a zymolytic liquid, wherein the zymolytic residues are used for preparing pulps; and c, after the steam-exploded straws in the step a are detoxificated, mixing a zymolytic liquid with the zymolytic liquid in the step b and adding nitrogen sources to butylicum fermentation. The method has the advantages that sources of raw materials are wide; the separation of celluloses (continuous fibers and staple fibers), hemicelluloses, xylogens and the like in the straws is realized, thus sufficiently realizing the value of each component; and the celluloses are divided into the continuous fibers which are difficult to realize enzymolysis and the staple fibers which are easy to realize enzymolysis, thus reducing the usage amount and cost of the cellulase, improving the comprehensive utilization value of the straws and solving the source problem of raw materials in industrialization production of the butylicum fermentation.

A compact laminated assembly based upon a saturation grade paper made using a grass fiber or grass / wood fiber blend, instead of the conventional wood fibers from trees. A plurality of the grass paper sheets are substantially impregnated using a thermosetting resin and stacked in a superimposed relationship. The assembled stack of resin impregnated paper sheets are heat and pressure consolidated into a substantially homogenous monolithic mass with the thermosetting resin being substantially completely cured. A film of a substantially completely cured solid powder coating composition is laminated to at least a portion of an outer surface of the compact laminated assembly.

Methods and apparatus for manufacturing vacuum forming a produce container using a fiber-based slurry. The slurry includes a moisture barrier comprising alkylketene dimer in the range of about 4% by weight, and a cationic liquid starch component in the range of 1%-7% by weight.