775results about "Shaping conveyors" patented technology

Structural cement panel for resisting transverse and shear loads equal to transverse and shear loads provided by plywood and oriented strain board, when fastened to framing for use in shear walls, flooring and roofing systems. The panels provide reduced thermal transmission compared to other structural cement panels. The panels employ one or more layers of a continuous phase resulting from curing an aqueous mixture of calcium sulfate alpha hemihydrate, hydraulic cement, coated expanded perlite particles filler, optional additional fillers, active pozzolan and lime. The coated perlite has a particle size of 1-500 microns, a median diameter of 20-150 microns, and an effective particle density (specific gravity) of less than 0.50 g/cc. The panels are reinforced with fibers, for example alkali-resistant glass fibers. The preferred panel contains no intentionally added entrained air. A method of improving fire resistance in a building is also disclosed.

A multi-layer process for producing structural cementitious panels, includes, (a.) providing a moving web; (b.) one of depositing a first layer of loose fibers upon the web and (c.) depositing a layer of settable slurry upon the web; (d.) depositing a second layer of loose fibers upon the slurry; (e.) embedding said second layer of fibers into the slurry; and (f.) repeating steps (c.) through (e.) until the desired number of layers of settable fiber-enhanced slurry in the panel is obtained. Also provided are a structural panel produced by the present process, an apparatus suitable for producing structural cementitious panels according to the present process, and a structural cementitious panel having multiple layers, each layer created by depositing a layer of settable slurry upon a moving web, depositing fibers upon the slurry and embedding the fibers into the slurry such that each layer is integrally formed with the adjacent layers.

A mold-resistant gypsum panel includes a core of an interlocking matrix of calcium sulfate dihydrate crystals, a facing material on at least one side of the panel and a salt of pyrithione dispersed through both the core and the facing materials. A method of making a mold-resistant gypsum product is also provided. A slurry of calcined gypsum, water and a water-soluble pyrithione salt is formed, then deposited on a sheet of facing material. The slurry on the facing material is shaped into a panel and maintained under conditions sufficient for the calcined gypsum to react with the water to form a core comprising an interlocking matrix of set gypsum crystals. Heating of the panel causes evaporation of the water that did not react with the calcined gypsum.

A tray (100) or container (478) which may be hermetically sealed having a flange (116), rim (124), handle (258), rib, bottom surface (500), sidewall (114), or other portion that is encapsulated by or formed from injection-molded material.

Described herein is a monolithic flooring system that includes cove elements that are shaped to provide a transition between floor and wall such that a floor coating may be installed over the cove elements and sub-flooring to create a unitary floor-cove covering making for a surface that is more sanitary and easier to clean. Also described are various shaped cove elements that enable creation of a good transition between wall and floor. The cove elements are preferably made of material similar to the sub-floor, for instance a cementitious material. The floor coating is preferably a resinous material.

A fabrication method of forming curved thermoplastic composite laminate parts with tailored and varying thickness in a continuous process. Automated equipment or hand lay-up are used to collate parts or components into a multi-layer stack. Each stack contains all plies, including ply build-up areas, tacked in the proper location to maintain orientation and location. Ply consolidation tooling contains all necessary part features and is coordinated to the customized multiple ply stacks to form a single integrated thermoplastic composite laminate potentially having areas of differing thickness from the multiple ply stacks.

A process and apparatus for making a shingle, together with the shingle made thereby, is provided, in which one or more thermoplastic materials are extruded or co-extruded to form an extrudate, with the extrudate being cut into a preliminary shingle shape, which is allowed to dissipate heat, and then is delivered to a compression mold, wherein the preliminary shingle shape is compression molded to substantially its final dimensions and is then discharged from the mold and allowed to cool.

The present invention is directed to micro- and nano-scale imprinting methods and the use of such methods to fabricate supported and/or free-standing 3-D micro- and/or nano-structures of polymeric, ceramic, and/or metallic materials. In some embodiments, a duo-mold approach is employed in the fabrication of these structures. In such methods, surface treatments are employed to impart differential surface energies to different molds and/or different parts of the mold(s). Such surface treatments permit the formation of three-dimensional (3-D) structures through imprinting and the transfer of such structures to a substrate. In some or other embodiments, such surface treatments and variation in glass transition temperature of the polymers used can facilitate separation of the 3-D structures from the molds to form free-standing micro- and/or nano-structures individually and/or in a film. In some or other embodiments, a “latch-on” assembly technique is utilized to form supported and/or free-standing stacked micro- and/or nano-structures that enable the assembly of polymers without a glass transition temperature and eliminate the heating required to assemble thermoplastic polymers.

A process for producing fiber-reinforced structural cementitious panels made of at least one layer of fiber reinforced cementitious slurry, the process for each such layer of slurry including providing a moving web; depositing a first layer of individual, loose fibers upon the web; depositing a layer of settable slurry upon the deposited first layer of individual, loose fibers; depositing a second layer of individual, loose fibers upon the deposited layer of settable slurry; and actively embedding both layers of individual, loose fibers into the layer of slurry to distribute the fibers throughout the slurry.

A method for making an encapsulated stent-graft having an essentially tubular configuration with a central longitudinal lumen and having a first diameter and a second diameter, wherein the first diameter is larger than the second diameter. The stent-graft may include a self-expanding stent and a first and second tube of biocompatible material between which the stent is positioned. The stent-graft may also include an interlayer member between the first and second tube. The method generally includes applying pressure and heat to a stent-graft assembly to form a monolithic layer of biocompatible material around the stent.

Tubular casting processes, such as dip-coating, may be used to form substrates from polymeric solutions which may be used to fabricate implantable devices such as stents. The polymeric substrates may have multiple layers which retain the inherent properties of their starting materials and which are sufficiently ductile to prevent brittle fracture. Parameters such as the number of times the mandrel is immersed, the duration of time of each immersion within the solution, as well as the delay time between each immersion or the drying or curing time between dips and withdrawal rates of the mandrel from the solution may each be controlled to result in the desired mechanical characteristics. Additional post-processing may also be utilized to further increase strength of the substrate or to alter its shape.

A monolithic noise suppression device comprising a monolithic, integral baffle housing module. The module comprising, in turn, at least no welded joints or seams between the various components that make up the core of the module and no welded joints or seams between the core, or any structures that make up the core, and the various interior surfaces and/or structures that make up the body of the module. The module is preferably plastic and manufactured using a layered printing process. The monolithic, integral baffle housing module may include various other features that enhance performance, reduce manufacturing cost, facilitate customization and eliminate restrictions on disposability as compared to conventional noise suppression devices. The monolithic noise suppression device may further comprise a first stage noise suppression device to be used in conjunction with the monolithic, integral baffle housing module.