The invention discloses a low-temperature high-strength microcrystalline glass vitrified bond used for preparing grinding tools made of superhard material diamond and cubic boron nitride. The components and the weight percentage are that SiO2 takes 40-70%, B2O3 takes 5-25%, Al2O3 takes 2-5%, Na2O takes 2-15%, K2O takes 2-5%, MgO takes 2-4%, CaO takes 2-4%, Li2O takes 1-10%, ZrO2 takes 2-5% and Sb2O3 takes 2-5%. The microcrystalline glass is abtaind by sintering the powder, the temperature of sintering-crystallization is 700-900 DEG C, the thermal expansion coefficient is 4-10*10-6 / DEG C and the bending strength can reach 160-200MPa. The grinding tool prepared by the combination of the microcrystalline glass and the powders of diamond and cubic boron nitride can satisfy the using speed of 160m / s or more. The invention has the advantages of low sintering temperature of the bond, low thermal expansion coefficient and high strength.