Modified cerium dioxide acid and alkali-resistant type strippable high molecular anti-rust film

A cerium dioxide, acid and alkali resistant technology, applied in anti-corrosion coatings, fire-retardant coatings, anti-fouling/underwater coatings, etc., can solve problems such as limiting the application field of anti-rust films

Inactive Publication Date: 2017-05-10
江海涛
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In Guo Jun's article "The Development of PVA Water-Soluble Polymer Peelable Antirust Film", he added antirust agent and other additives to polyvinyl alcohol, heated it in a water bath until it was completely dissolved, and then used the coating fluid to dissolve it completely. The extension method uniformly coats it on the metal surface, heats and dries it in a drying oven to form a film, and uses the neutral salt spray test, water solubility test and electron microscope test to characterize the performance of the polyvinyl alcohol antirust packaging film. The results show that the PVA antirust film not only has good antirust performance, but also has good peelability and water solubility, which meets the characteristics of green packaging and has good application prospects. However, the article uses polyvinyl alcohol and polyvinyl alcohol The combination of ethylene glycol is used as the carrier film-forming agent of the anti-rust film. Both polyvinyl alcohol and polyethylene glycol have good water solubility, and the prepared anti-rust film is not easy to dissolve in cold water at 40°C, but it is not easy to dissolve in cold water at a constant temperature. In the hot water heated to above 40°C in the water bath, it can be observed that the polyvinyl alcohol film will gradually soften first, then the film will become thinner, and finally dissolve completely, indicating that the antirust film is water-soluble and belongs to high-temperature water-soluble The film can be recycled, and it can be transported at room temperature or below 40°C to play a good anti-rust effect, which greatly limits the application field of the anti-rust film. It must be modified to improve its corrosion resistance, oil resistance, High temperature resistance and water resistance, etc., expand the application field, so that it can meet the anti-rust and anti-corrosion requirements under various conditions

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0015] A modified ceria acid and alkali resistant peelable polymer antirust film, which is prepared from the following raw materials in parts by weight (kg): aluminum isopropoxide 6.8, silane coupling agent KH792 0.2, orthosilicate tetra Ethyl ester 12, sorbitan trioleate 0.9, polyethylene glycol 2, methylvinyldiethoxysilane 3.7, polyvinyl alcohol 15, borax 1.8, cerium oxide 0.5, oleic acid 0.2, silane Joint agent KH560 0.1, polyetheramine 1.2, acrylamide 2, triethanolamine 3, benzotriazole 3, p-phenylenediamine 1, sodium benzoate 2, sodium lauryl sulfate 1, fatty acid polyoxyethylene ester amount, Right amount of nitric acid, right amount of hydrochloric acid, right amount of absolute ethanol, right amount of deionized water.

[0016] The modified ceria acid and alkali-resistant peelable polymer antirust film is prepared by the following specific steps:

[0017] (1) Mix aluminum isopropoxide and deionized water at a molar ratio of 1:100, reflux and stir in a water bath envir...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a modified cerium dioxide acid and alkali-resistant type strippable high molecular anti-rust film, which is prepared from the following raw materials including aluminum isopropoxide, a silane coupling agent KH792, tetraethoxysilane, sorbitan trioleate, polyglycol, methylvinyldiethoxysilane, polyvinyl alcohol, borax, cerium dioxide, oleic acid, a silane coupling agent KH560, polyetheramine, acrylamide, trolamine, benzotriazol, para-phenylene diamine, sodium benzoate, sodium dodecyl sulfate, a proper amount of polyoxyethylene fatty acid, a proper amount of nitric acid, a proper amount of hydrochloric acid, a proper amount of absolute ethyl alcohol and a proper amount of de-ionized water. A prepared anti-rust agent can form a layer of thin anti-rust film on a workpiece with anti-rust requirements; the film can be manually torn away; the strippable performance is good; the operation is simple; in addition, the prepared anti-rust film has high heat resistance, high acid and alkali corrosion resistance, oil resistance, water resistance and long anti-rust time, and is worthy of being popularized.

Description

technical field [0001] The invention relates to the technical field of metal surface treatment agents, in particular to a modified ceria acid and alkali resistant peelable polymer antirust film. Background technique [0002] According to statistics, every year in the world, steel products with a total weight equivalent to 10-20% of the annual metal content cannot be used due to corrosion, rust and other reasons. Therefore, people have adopted various anti-rust methods to avoid rust. Cut your losses. There are various kinds of antirust agents, among which sodium nitrite has been favored and widely used because of its excellent antirust performance and low price. , a lot of research and development work has been carried out at home and abroad, and a variety of alkyl, alkoxy, halo, naphthoic acids and their derivatives, nitrobenzoic acids, and borates, borates and molybdenum have been prepared. A new type of water-soluble rust inhibitor that replaces sodium nitrite with mater...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D129/04C09D5/08C09D5/20C09D5/14C09D7/12
CPCC09D129/04C08L2201/08C08L2205/025C08L2205/03C09D5/08C09D5/14C09D5/18C09D5/20C09D7/61C09D7/62
Inventor 江海涛
Owner 江海涛
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products