Composite coating with adjustable release performance of active ingredients and preparation method of composite coating

An active ingredient and composite coating technology, which is applied in the field of composite coatings with adjustable release performance of active ingredients and their preparation, can solve the problems of small influence of active ingredients and difficulty in construction, and achieves small influence, guaranteed safety, and preparation method. simple effect

Pending Publication Date: 2022-03-29
NINGBO INST OF MATERIALS TECH & ENG CHINESE ACADEMY OF SCI +1
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The invention provides a preparation method of a composite coating with adjustable release performance of active components, which has good repeatability, high safety, little influence on active components, can combine the excellent characteristics of different polymers, and solve the problem of solvents between different polymers The problem that the system is difficult to construct, the prepared composite coating with adjustable release performance of active ingredients can realize the release of active ingredients at different rates

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] (1) Use 200mL 50% ethanol aqueous solution as a solvent, add 15g polylactic acid (particle size 30-100μm) and 5g polycaprolactone (particle size 15-55μm) to obtain a mixed polymer suspension, then add 0.5g gentamicin sulfate Mycin, to prepare a mixed solution.

[0039] (2) Substrate surface cleaning: the substrate is made of stainless steel sheets, cleaned with acetone, alcohol, and deionized water in sequence, and then dried with nitrogen gas for later use; substrate surface roughening: the cleaned substrate surface is roughened by sandblasting, In order to increase the surface roughness of the substrate and improve the bonding strength of the coating, the parameters of the sandblasting process are: air pressure 0.8MPa, sandblasting time 20s, and the number of sand shot used for sandblasting is 50 mesh;

[0040] (3) Utilize the flame spraying process to spray the mixed solution of step (1) on the substrate surface after processing, and the condition of flame spraying i...

Embodiment 2

[0042] (1) Use 200mL of 50% ethanol aqueous solution as solvent, add 5g polylactic acid (particle size 30-100 μm) and 15g polycaprolactone (particle size 15-55 μm) to obtain a mixed polymer suspension, and then add 0.5g sodium sulfate Damycin, to prepare a mixed solution.

[0043](2) Cleaning of the substrate surface: the substrate is made of glass, washed with acetone, alcohol, and deionized water in sequence, and then blown dry with nitrogen for use; roughening of the substrate surface: the surface of the substrate after cleaning is roughened by sandblasting, to Increase the surface roughness of the substrate and improve the bonding strength of the coating. The parameters of the sandblasting process are: air pressure 0.8MPa, sandblasting time 20s, and the number of sand shot used for sandblasting is 50 mesh;

[0044] (3) Utilize the flame spraying process to spray the mixed solution of step (1) on the substrate surface after processing, and the condition of flame spraying is...

Embodiment 3

[0046] (1) Using 200mL 50% ethanol aqueous solution as solvent, add 10g polylactic acid (particle size 30-100μm) and 10g perfluoropropyl perfluorovinyl ether-polytetrafluoroethylene copolymer (particle size 30-100μm) to get mixed Add 0.5 g of gentamicin sulfate to the polymer suspension to prepare a mixed solution.

[0047] (2) Substrate surface cleaning: the substrate is made of stainless steel sheets, cleaned with acetone, alcohol, and deionized water in sequence, and then dried with nitrogen gas for later use; substrate surface roughening: the cleaned substrate surface is roughened by sandblasting, In order to increase the surface roughness of the substrate and improve the bonding strength of the coating, the parameters of the sandblasting process are: air pressure 0.8MPa, sandblasting time 20s, and the number of sand shot used for sandblasting is 50 mesh;

[0048] (3) Utilize the flame spraying process to spray the mixed solution of step (1) on the substrate surface after ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of a composite coating with adjustable release performance of active ingredients. The preparation method comprises the following steps: (1) preparing a mixed solution from at least two macromolecules and at least one active ingredient; (2) cleaning and roughening the surface of the matrix; and (3) spraying the mixed solution obtained in the step (1) on the surface of the treated matrix by using a flame spraying process to prepare the composite coating with the adjustable release performance of the active components, the active components comprise an antibacterial agent, an anticoagulant, an antiplatelet drug, an angiogenesis inhibitor, a hemostatic, an antitumor agent, an immunosuppressive agent and an osteoinducer. The method is good in repeatability, high in safety and small in influence on the active ingredients, the problem that a solvent system between different macromolecules is difficult to construct is solved, the excellent characteristics of different macromolecules can be combined, and the prepared composite coating with the adjustable release performance of the active ingredients can achieve release of the active ingredients at different rates.

Description

technical field [0001] The invention relates to the technical field of composite coatings, in particular to a composite coating with adjustable release performance of active ingredients and a preparation method thereof. Background technique [0002] The lack of antibacterial, biological activity, and osteoinductivity of conventional medical materials greatly limits its application, so surface functional modification is usually required. There are many types of polymer materials, various mechanical properties, stable physical properties, and various biocompatibility, so they are widely used in the preparation of surface functional modification coatings. However, because the slow-release properties of different polymer coatings are very different, and the solubility properties in different solvents are different, the conventional blending and compounding method after dissolution is severely restricted, and it is difficult to release a wide variety of polymer materials. Extens...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): A61L31/16A61L31/10B05D7/24B05D1/08B05D3/00
CPCA61L31/16A61L31/10B05D7/24B05D1/08B05D3/002A61L2300/404A61L2300/406A61L2300/606C08L67/04C08L23/0892C08L29/10C08L27/18Y02A50/30
Inventor 张波涛潘永红叶磊陈秀勇黄晶吴双杰周平李华
Owner NINGBO INST OF MATERIALS TECH & ENG CHINESE ACADEMY OF SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com