Instant dry adhesive and preparation method thereof

An adhesive and instant-drying technology, applied in the direction of non-polymer adhesive additives, adhesives, non-polymer organic compound adhesives, etc., can solve poor adhesion, water resistance, impact resistance and high temperature resistance Problems such as poor corrosion resistance

Inactive Publication Date: 2021-12-10
深圳市燊凝科技有限公司
View PDF2 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the existing instant-drying adhesives not only have the disadvantages of poor water resistance, impact resistance, high temperature resistance, and corrosion resistance, but also have the disadvantage of poor adhesion when applied in aqueous media.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0035] The raw materials for the preparation of the instant adhesive include: 55-80 parts of ethyl α-cyanoacrylate, 10-40 parts of thickener, 0.05-0.3 parts of plasticizer, 1-3 parts of organic solvent, 0.5 parts of graphene ~5 parts, and 0.5~5 parts of carbon nanotubes.

[0036] In at least one embodiment, the thickener is methyl methacrylate-ethyl acrylate copolymer, polymethacrylate, polyvinyl acetate, polyacrylate, polyvinyl acetal, and polyvinyl acetate at least one of esters. The thickener can undergo radical polymerization reaction with ethyl α-cyanoacrylate to increase the viscosity of the instant adhesive.

[0037] In at least one embodiment, the plasticizer is dioctyl phthalate, dimethyl phthalate, diethyl phthalate, dibutyl phthalate, and dioctyl phthalate at least one of . The plasticizer can weaken the physical effect of polymer intermolecular force, so that the instant adhesive has better toughness and mechanical strength.

[0038] In at least one embodiment,...

Embodiment 1

[0079] The raw materials for the preparation of the instant-drying adhesive of Example 1 are provided. In parts by weight, the raw materials for the preparation of the instant-drying adhesive of Example 1 include: 78.5 parts of α-ethyl cyanoacrylate, methyl methacrylate-ethyl acrylate 10.2 parts of ester copolymer, 0.2 parts of dioctyl ester, 1 part of ethylene carbonate, 0.2 parts of sulfur dioxide, 0.6 parts of hydroquinone, 0.1 part of benzophenone tetracarboxylic dianhydride, 4.2 parts of silicon dioxide, 2 parts of graphene , 3 parts of carbon nanotubes;

[0080] Add α-ethyl cyanoacrylate, methyl methacrylate-ethyl acrylate copolymer, dioctyl ester, ethylene carbonate, sulfur dioxide, and benzophenone tetracarboxylic dianhydride into the reaction kettle, mix well, and set at 70 React at a temperature of -80°C for 120 minutes to obtain the primary colloid;

[0081] After adding hydroquinone and silicon dioxide to the primary colloid, distilling under reduced pressure at a...

Embodiment 2

[0085] The raw materials for the preparation of the instant-drying adhesive of Example 1 are provided. In parts by weight, the raw materials for the preparation of the instant-drying adhesive of Example 1 include: 74.6 parts of α-ethyl cyanoacrylate, methyl methacrylate-ethyl acrylate 14.1 parts of ester copolymer, 0.2 parts of dioctyl ester, 1 part of ethylene carbonate, 0.2 parts of sulfur dioxide, 0.6 parts of hydroquinone, 0.1 part of benzophenone tetracarboxylic dianhydride, 4.2 parts of silicon dioxide, 3 parts of graphene , 2 parts of carbon nanotubes;

[0086] Add α-ethyl cyanoacrylate, methyl methacrylate-ethyl acrylate copolymer, dioctyl ester, ethylene carbonate, sulfur dioxide, and benzophenone tetracarboxylic dianhydride into the reaction kettle, mix well, and set at 70 React at a temperature of -80°C for 120 minutes to obtain the primary colloid;

[0087]After adding hydroquinone and silicon dioxide to the primary colloid, distilling under reduced pressure at a ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides an instant-dry adhesive and a preparation method thereof. The instant-dry adhesive is prepared from the following raw materials in parts by weight: 55 to 80 parts of alpha-ethyl cyanoacrylate, 10 to 40 parts of thickening agent, 1 to 3 parts of organic solvent, 0.5 to 5 parts of graphene and 0.5 to 5 parts of carbon nano tube. The invention also provides a preparation method of the instant-dry adhesive. The instant-dry adhesive has the advantages of being high in water resistance, impact resistance, high temperature resistance and corrosion resistance, and also has good binding power during construction in a water medium.

Description

technical field [0001] The invention relates to the technical field of chemical materials, in particular to an instant adhesive and a preparation method of the instant adhesive. Background technique [0002] The existing instant-drying adhesive has the advantages of wide bonding surface and strong bonding ability, and is considered to be one of the most important room temperature curing adhesives. However, the existing instant-drying adhesive not only has the disadvantages of poor water resistance, impact resistance, high temperature resistance, and corrosion resistance, but also has the disadvantage of poor cohesive force when applied in an aqueous medium. Contents of the invention [0003] The main purpose of the present invention is to provide an instant-drying adhesive, which aims to provide strong water resistance, impact resistance, high temperature resistance, and corrosion resistance, and also has better adhesion when applied in water medium. Strong instant drying...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09J4/04C09J4/06C09J11/04
CPCC09J4/06C09J11/04
Inventor 何顺民别会利何卓凝
Owner 深圳市燊凝科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap