A kind of green fluorescent powder excited by ultraviolet/near ultraviolet light and preparation method thereof

A technology of green phosphor and near-ultraviolet light, applied in chemical instruments and methods, luminescent materials, inorganic chemistry, etc., can solve the problems of low luminous efficiency of phosphor, complex process, high synthesis cost, etc., and achieve simple and easy preparation method line, abundant sources, and low production cost

Active Publication Date: 2019-10-22
XUZHOU NORMAL UNIVERSITY
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Existing phosphors have low luminous efficiency and narrow excitation wavelength
Chinese invention patent CN101497789A discloses a kind of nitride green fluorescent powder and its preparation method, the SrCO 3 、BaCO 3 or a combination of both and Si(NH) 2 and Eu 2 o 3 Perform ball milling and mixing for 2-3 hours to obtain a mixture, then sinter the mixture at a temperature of 1400-1500° C. for 3-4 hours and then pulverize it. The pulverized product is washed 2-3 times with deionized water and isopropanol respectively. Then dry at a temperature of 90-100°C for 16-24 hours to obtain the dried product, and finally sieve the dried product to obtain a nitride green phosphor. The process is relatively complicated, not easy to operate, and the synthesis cost is high.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of green fluorescent powder excited by ultraviolet/near ultraviolet light and preparation method thereof
  • A kind of green fluorescent powder excited by ultraviolet/near ultraviolet light and preparation method thereof
  • A kind of green fluorescent powder excited by ultraviolet/near ultraviolet light and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] Preparation of Ba 9.999 Eu 0.001 al 2 o 13 : According to the chemical formula Ba 9.999 Eu 0.001 al 2 o 13 The stoichiometric ratio of each element in is weighed respectively Raw materials: europium oxide Eu 2 o 3 : 0.001g, barium carbonate BaCO 3 : 9.849g, aluminum oxide Al 2 o 3 : 0.517g, ground and mixed evenly in an agate mortar, pre-calcined in air atmosphere, the pre-calcined temperature is 600°C, the pre-calcined time is 10h, then cooled to room temperature with the furnace, and the sample is taken out; the first pre-calcined The raw materials were thoroughly mixed and ground in the same way again, and the second pre-calcination was carried out in the air atmosphere. The pre-calcination temperature was 1000°C, the pre-calcination time was 1h, and then cooled to room temperature, and the sample was taken out; Grinding and mixing evenly, calcining in a reducing atmosphere, the calcining temperature is 1300°C, the calcining time is 1h, and then cooled to ...

Embodiment 2

[0042] Preparation of Ba 9.5 Eu 0.5 al 2 o 13 : According to the chemical formula Ba 9.5 Eu 0.5 al 2 o 13 The stoichiometric ratio of each element in is weighed respectively Raw material: europium nitrate Eu(NO 3 ) 3 ·6H 2 O: 0.44 grams, barium oxide BaO: 8.03 grams, aluminum nitrate Al (NO 3 ) 3 9H 2 O: 3.75 grams, mixed evenly in an agate mortar, pre-calcined in an air atmosphere, the pre-calcined temperature is 1000 ° C, the pre-calcined time is 8h, and then cooled to room temperature with the furnace, the sample is taken out, and the pre-calcined raw material is again Thoroughly grind and mix uniformly, calcined in reducing atmosphere, calcined temperature is 1100°C, calcined for 12 hours, and then cooled to room temperature to obtain powdery green fluorescent powder.

[0043] The X-ray powder diffraction pattern, excitation spectrum, luminescence spectrum, luminescence decay curve, and SEM image of the sample prepared in this example are consistent with those ...

Embodiment 3

[0045] Preparation of Ba 9 EuAl 2 o 13 : According to the chemical formula Ba 9 EuAl 2 o 13 The stoichiometric ratio of each element in is weighed respectively Raw materials: europium oxide Eu 2 o 3 : 1.76 grams, barium oxide BaO: 11.74 grams, aluminum nitrate Al(NO 3 ) 3 9H 2 O: 3.75 grams, mixed and ground in an agate mortar evenly, then pre-calcined in an air atmosphere, the pre-calcined temperature is 750°C, the pre-calcined time is 6h, and then cooled to room temperature with the furnace, the sample is taken out, and the pre-calcined raw material Mix well and grind evenly by the same method again, calcining in a reducing atmosphere at a calcining temperature of 1200°C for a calcining time of 4 hours, and then cool to room temperature to obtain a powdery green fluorescent powder.

[0046] The X-ray powder diffraction pattern, excitation spectrum, luminescence spectrum, luminescence decay curve, and SEM image of the sample prepared by the technical scheme of this e...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a green fluorescent powder excited by ultraviolet / near ultraviolet light and a preparation method thereof. The chemical formula is Ba 10‑ 10x Eu 10x Al 2 o 13 , where the active ion is europium ion Eu 2+ , x is Eu 2+ Doping Ba 2+ The molar ratio of bits, 0.0001≤x≤0.25. The phosphor powder prepared by the present invention has the advantages of wide excitation wavelength, uniform particle dispersion, excellent thermal stability and physical and chemical stability, no interaction with packaging materials, semiconductor chips, etc., and is easily absorbed by ultraviolet-near ultraviolet (300-420nm) High-efficiency excitation of light in the wavelength band, high luminous intensity, high luminous efficiency, and pure fluorescence chromaticity; during preparation, the compounds containing the elements required for the synthesis of luminescent materials are mixed in proportion, prepared by high-temperature solid-phase method or chemical synthesis method, and prepared by multiple calcinations , the process is simple, easy to operate, the source of raw materials is abundant, and the production cost is low.

Description

technical field [0001] The invention relates to a fluorescent material and a preparation method thereof, in particular to a green fluorescent powder excited by ultraviolet / near ultraviolet light and a preparation method thereof, belonging to the technical field of luminescent materials. Background technique [0002] White light-emitting diode (LED) is an energy conversion device that can directly convert electrical energy into visible light energy. It is a new type of lighting display device and a green and environmentally friendly lighting source. White light-emitting diode lighting equipment has the advantages of low working voltage, power saving, stable performance, small size, energy saving and environmental protection, no heat radiation, long life, strong anti-vibration and impact resistance, etc., and is widely used in indicator lights, backlights, cameras, etc. , decoration, mobile phone, indoor commercial atmosphere lighting and city night scene, stage lighting, exhi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09K11/80C01F17/00
CPCC01F17/34C01P2002/72C01P2004/03C01P2006/60C09K11/7734
Inventor 乔学斌
Owner XUZHOU NORMAL UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com