Anionic functionalized fluorine-containing polymer and preparation method thereof

An anionic and functionalized technology, applied in the field of anion-functionalized fluoropolymer and its preparation, can solve the problems of insignificant hydrophilic effect, limited application scope of fluoropolymer materials, etc., and achieve strong negative charge performance and cation exchange The effect of adsorption performance

Active Publication Date: 2016-10-05
ZHEJIANG UNIV
View PDF6 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Chinese patent (CN 1223271A) discloses a copolymer of fluorinated olefin and maleic anhydride, maleic acid, dichloromaleic anhydride or dichloromaleic acid. Maleic anhydride in this fluorine-containing copolymer belongs to the anionic copolymerization unit It can provide hydrophilicity for fluoropolymers, but the monomer component is only 0.03-5mol%, and the hydrophilic effect is not obvious
Significantly limits the range of applications for fluoropolymer materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Anionic functionalized fluorine-containing polymer and preparation method thereof
  • Anionic functionalized fluorine-containing polymer and preparation method thereof
  • Anionic functionalized fluorine-containing polymer and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0147] Synthesis of anion-functionalized fluoropolymer P1:

[0148]Add 2000ml deionized water, additive polyvinyl alcohol (PVA) 1.2g, additive hydroxypropyl methylcellulose (HPMC) 0.4g, initiator peroxydicarbonate bis(2-ethylhexyl) in the stainless steel reaction kettle (EHP) 1g, evacuated and filled with nitrogen repeatedly 3 times, then added 1500g of vinylidene fluoride, 27.19g of hydroxyethyl acrylate and 4.85g of allyl 2-bromo-2-methylpropionate, pre-dispersed and stirred at room temperature for 30 minute. The temperature was raised to a polymerization temperature of 47° C. to carry out a polymerization reaction. React for 12 hours, stop heating when the pressure drop in the kettle reaches 0.2MPa, let it volatilize naturally for 15 minutes, let air in for 5 minutes, vacuumize and fill with nitrogen three times, then add sodium bicarbonate until the pH is 8, add 22.03g of sodium acrylate , copper 5g, cuprous chloride 5g, 2,2'-bipyridine (bpy) 16g, then temperature contro...

Embodiment 2

[0167] Synthesis of anion-functionalized fluoropolymer P2:

[0168] P2 synthetic process with reference to embodiment 1. The formula is shown in Table 1 and the process parameters are shown in Table 2.

[0169] The P2 structure and performance characterization methods are the same as those described in Example 1. The general formula of the P2 structural formula is the same as that of P1, and the parameters in the general formula are shown in Table 3;

Embodiment 3

[0171] Synthesis of anion-functionalized fluoropolymer P3:

[0172] The synthesis process of P3 refers to Example 1. The formula is shown in Table 1 and the process parameters are shown in Table 2.

[0173] The P3 structure and performance characterization methods are the same as those described in Example 1. The general structure of P3 is the same as that of P1, and the parameters in the general formula are shown in Table 3; the molecular weight, molecular weight distribution and content of anion functionalized monomer components in the polymer of P3 are shown in Table 4.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Number average molecular weightaaaaaaaaaa
Login to View More

Abstract

The invention discloses an anionic functionalized fluorine-containing polymer and a preparation method thereof. The functionalized fluorine-containing polymer is prepared through the following steps: subjecting a chlorine-containing monomer, a graftable active monomer and a hydrophilic functionalized monomer as copolymerization monomers to polymerization in an aqueous-phase dispersion system so as to obtain an active precursor polymer with a main chain containing an active side group for atom transfer radical polymerization, initiating an anionic functionalized polymer to interface atom transfer radical polymerization on a solid-liquid interface in an alkaline environment by utilizing the active side group so as to form the anionic functionalized fluorine-containing polymer containing an anionic type side chain. According to the invention, the anionic type side chain contains sulfonic groups and carboxylic groups and has strong electronegativity, so the polymer has strong hydrophilic performance and cation exchange adsorption performance, can be independently used for preparation or is mixed with other resins for preparation of highly-hydrophilic separating membrane products, gel electrolytes, adhesives, battery separators, cation exchange adsorption materials and flexible packaging materials, greatly broadens the application scope of vinyl chloride polymers, and has good application prospects.

Description

technical field [0001] The invention belongs to the field of polymer materials, and in particular relates to an anion functionalized fluorine-containing polymer and a preparation method thereof. Background technique [0002] Fluorine atoms have strong electronegativity, low polarizability, weak van der Waals force and high bond energy (485.3kJ / mol) of C-F bond, which makes fluoropolymers have outstanding heat resistance, solvent resistance, acid and alkali corrosion resistance, Excellent weather resistance, flame retardancy, and unique low surface energy, etc. Fluorine-containing polymers are mainly divided into fluorine-containing olefin polymers and fluorine-containing acrylate polymers. [0003] Polyvinylidene fluoride (PVDF) is non-toxic and odorless, and its appearance is translucent or white powder or granules. Ultraviolet radiation and aging resistance; the molecular chains of PVDF are closely arranged, the crystallinity is high, the hydrophobicity is large, and the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08F259/08C08F220/06C08F220/58C08F222/02C08F228/02C08F212/14C08L51/00
Inventor 朱宝库王纳川银雪姚之侃方立峰周名勇崔月许云秋包永忠朱利平
Owner ZHEJIANG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com