Modified epoxy resin adhesive and its preparation process

A technology of epoxy resin and modified resin, applied in the direction of epoxy resin glue, adhesive, adhesive type, etc., can solve the problems of environmental pollution, inability to meet the curing time and long curing time of packaging materials, etc.

Inactive Publication Date: 2005-09-21
徐良衡
View PDF0 Cites 17 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The currently used epoxy resin encapsulation adhesive requires a relatively long curing time (>18 hours) and a high curing temperature (>150°C), which cannot meet the requirements of short curing time and medium and low temperature encapsulation on the production line.
Moreover, the main packaging adhesive colloid contains bromine, which pollutes the environment.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Modified epoxy resin adhesive and its preparation process
  • Modified epoxy resin adhesive and its preparation process
  • Modified epoxy resin adhesive and its preparation process

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0053] The molecular structural formula of reactant 4-(4-aminobenzyl)aniline is as follows:

[0054]

[0055] reaction process:

[0056] Add 29.7 g (0.15 mol) of ambenzylaniline and 17.6 g (0.1 mol) of 1-chlorodecane into a glass reactor, add 80 ml of 15% NaOH alkaline solution, and stir at 1500 rpm. The reaction temperature was 90°C, and after rising to the reaction temperature, the reaction was carried out for 3 hours. After the reaction, extract with cyclohexane and remove the solvent by rotary distillation to obtain the product as a colorless or light yellow transparent liquid. Viscosity 320mp, curing conditions: curing above 60°C, no effect at low temperature.

Embodiment 2

[0058] The structural formula of reactant 4-(2-aminoethyl)-1-methylcyclohexylamine is as follows:

[0059]

[0060] reaction process:

[0061] The reactant 4-(2-aminoethyl)-1-methylcyclohexylamine 46.9g (0.3mol) and 12.1g (0.1mol) were added to the glass reactor, and 15% Na 2 CO 3 100ml, stir quickly. The reaction temperature is 120°C, and the reaction is 6h. After the reaction, it was extracted with n-hexane. After three times, the solvent was removed by rotary distillation to obtain a light yellow transparent viscous liquid. The viscosity is 280mp. Low temperature has no effect, and it can be cured when the temperature is raised to 45°C.

[0062] Surface active treatment of II fillers

Embodiment 3

[0063] The surface treatment of embodiment 3 silica powder

[0064] In 50ml organosiloxane solution, add 4.5% methanol solution of fused silicon micropowder (the maximum diameter of silicon micropowder should be less than 10μm), stir vigorously at 5000rpm to promote the full dispersion of silicon micropowder in the system, then heat up to reflux, and stir at a medium speed , Reaction time 1h, continue to heat up and steam methanol. Control the temperature within 80-100°C, and react within this temperature range for 20 hours. After the surface treatment is completed, excess siloxane is distilled off under reduced pressure. The system was cooled to room temperature. After separation and drying, wash and filter repeatedly with distilled water or deionized water, dehydrate with absolute ethanol, and grind into fine powder after vacuum drying to obtain 2.6 g of surface-treated fused silica powder filler.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Densityaaaaaaaaaa
Densityaaaaaaaaaa
Login to view more

Abstract

The invention discloses a thermosetting multi-component modified epoxy binder for using in the middle between IC cores and insulating underlay base boards and its preparation process, which belongs to the electronic device packaging technical field. The said binding agent is made of combined modified epoxide resin, latent curing agent, filler and addition auxiliary agent in a correct proportion, wherein the combined modified epoxide resin is made of bisphenol ethylene oxide resin as the main resin, alicyclic rings and naphthalene epoxide resin as the modified resin, the said latent curing agent is aromatic terminal group amine or alicyclic ring terminal group amine, the said filler is inorganic powder prepared by tensioactive treatment, the said addition auxiliary agent contains toning agent, accelerating agent, flame retardant and phenols curing agent. The said binding agent in the invention has many advantages such as high glass transition temperature, high adhesive property, high heat resistance, middle-and-low graded curing temperature and short curing time.

Description

technical field [0001] The invention belongs to the technical field of packaging materials for electronic devices, and in particular relates to a thermosetting multi-component modified epoxy resin adhesive used between an IC chip and an insulating substrate substrate and a preparation method thereof. technical background [0002] Silicone polymers and epoxy resins are commonly used packaging materials for electronic devices in the electronics industry. Silicone material has the advantages of low temperature flexibility (Tg=120°C), low surface energy, high temperature resistance, weather resistance, corrosion resistance, good hydrophobicity, and high dielectric strength, but it also has poor mechanical properties and wear resistance. , solvent resistance, poor adhesion, high cost and other shortcomings. Epoxy resin has the advantages of excellent mechanical properties, chemical solvent resistance, oxygen permeability resistance, water resistance, good bonding performance, ea...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09J163/00
Inventor 徐良衡王群英高芸
Owner 徐良衡
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap