A kind of impact-resistant polyethylene plastic pipe and its preparation method

A polyethylene plastic pipe and impact-resistant technology, applied in the field of composite materials, can solve the problems of easy cracking, difficult processing and molding, poor stress resistance, etc., and achieve the effects of short production cycle, overcoming processing and molding difficulties, and excellent mechanical properties.

Active Publication Date: 2022-05-24
河北鸿翔电讯器材有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to provide an impact-resistant polyethylene plastic pipe and its preparation method, which not only overcomes the defects of ultra-high molecular weight polyethylene pipes, such as difficulty in processing and forming, poor stress resistance, and easy cracking, but also retains the traditional ultra-high molecular weight polyethylene pipe. The excellent impact strength of polyethylene pipes also improves wear resistance and creep resistance, and endows them with antibacterial properties. The preparation method is hygienic, non-toxic and pollution-free, and is suitable for large-scale promotion and production

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of impact-resistant polyethylene plastic pipe and its preparation method
  • A kind of impact-resistant polyethylene plastic pipe and its preparation method
  • A kind of impact-resistant polyethylene plastic pipe and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0063] Example 1: An impact-resistant polyethylene plastic pipe:

[0064] The present embodiment provides an impact-resistant polyethylene plastic pipe, by weight, composed of the following raw materials:

[0065]

[0066] The present embodiment also provides a method for preparing an impact-resistant polyethylene plastic pipe, which specifically includes the following steps:

[0067] 1) Preparation of polyethylene wax grafted polysiloxane:

[0068] 1.1) Add 10 parts by weight of polyethylene wax (molecular weight 4500) to 15 parts by weight of n-heptane / xylene mixed solution (mixing volume ratio is 1:0.6), under nitrogen protection, stir at 90°C for 20min to make it The dispersion is uniform, and the stirring speed is 400r / min;

[0069] 1.2) Mix 0.15 parts by weight of hydroxyethyl methacrylate and 0.05 parts by weight of benzoyl peroxide, then add the mixed solution to the solution in step 1) at a rate of 0.1 mL / s, at a rate of 300 r / min. The reaction was stirred for 2...

Embodiment 2

[0083] Example 2: Another impact resistant polyethylene plastic pipe:

[0084] This example provides another impact-resistant polyethylene plastic pipe. The components and formulation methods are basically the same as those in Example 1. The difference is that in this example, step 1 of preparing polyethylene wax grafted polysiloxane is used. ), the molecular weight of polyethylene wax is 1500.

Embodiment 3

[0085] Example 3: Another impact resistant polyethylene plastic pipe:

[0086] This example provides another impact-resistant polyethylene plastic pipe. The components and formulation methods are basically the same as those in Example 1. The difference is that in this example, step 1 of preparing polyethylene wax grafted polysiloxane is used. ), the molecular weight of polyethylene wax is 3000.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
crystallinityaaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of composite materials, in particular to an impact-resistant polyethylene plastic pipe and its preparation method, which uses ultra-high molecular weight polyethylene as the main raw material, and modifies its surface through ultraviolet radiation crosslinking technology, and adds Polyethylene wax grafted with polysiloxane and quaternized nano-ceramic powder processing aids to prepare polyethylene plastic pipes, not only overcomes the defects of ultra-high molecular weight polyethylene pipes, such as difficulty in processing, poor stress resistance, and easy cracking, but also retains The excellent impact strength of traditional ultra-high molecular weight polyethylene pipes is improved, the wear resistance and creep resistance are also improved, and antibacterial properties are endowed. The preparation method is hygienic, non-toxic and pollution-free, and is suitable for large-scale promotion and production.

Description

technical field [0001] The invention relates to the technical field of composite materials, in particular to an impact-resistant polyethylene plastic pipe and a preparation method thereof. Background technique [0002] With the rapid development of society and the continuous progress of science and technology, the application ratio of polymer materials in agricultural and industrial production continues to increase, and the application of plastic pipes is becoming more and more extensive. Ultra-high molecular weight polyethylene (UHMWPE) is a linear structure polyethylene with a viscosity average molecular weight of more than 1.5 million, a crystallinity of 65-85%, and a density of 0.92-0.96g / cm 3 . The extremely high relative molecular weight endows it with extraordinary performance and becomes a new thermoplastic engineering plastic with excellent performance. It has the incomparable wear resistance, impact resistance, self-lubrication, corrosion resistance, low temperat...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L51/06C08L87/00C08K9/04C08K9/06C08K3/22C08F255/02C08F220/14C08F2/50
CPCC08L51/06C08F255/02C08F2/50C08L2203/18C08K2201/011C08K2003/2227C08K2003/2241C08L2201/08C08L87/005C08K9/04C08K9/06C08K3/22C08F220/14
Inventor 何立志
Owner 河北鸿翔电讯器材有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com