Alloy co-infiltration dacromet and sealing layer composite coating preparation method

A composite coating and sealing layer technology, used in metal material coating technology, coatings, anti-corrosion coatings, etc., can solve problems such as insufficient surface hardness and chromium pollution, and achieve uniform thickness, good anti-corrosion performance, and high surface hardness. Effect

Active Publication Date: 2019-02-15
HEBEI CHENYANG INDAL & TRADE GROUP CO LTD
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Dacromet, also known as Dacromet rust, high-gram rust, zinc-chromium film, etc., refers to coating the metal substrate with a liquid treatment solution containing zinc flakes, aluminum flakes, chromic anhydride, ethylene glycol, etc. After baking, a layer of non-decorative coating film with excellent corrosion resistance is formed on the surface of the metal substrate. The disadvantage is that the surface hardness is insufficient
In addition, since chromium plays a key role in Dacromet coating metal anti-corrosion technology, chromium exists every moment in the processing and application of Dacromet, from raw material storage and transportation to slurry preparation, Dacromet There is a possibility of chromium pollution in the coating and curing, and finally to use

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment 1

[0036] The preparation method of alloy co-infiltration, Dacromet and sealing layer composite coating provided by the present embodiment comprises the following steps:

[0037] Step 1. Weigh the following co-penetrating agent raw materials in parts by mass: 100 parts of zinc powder, 15 parts of aluminum powder, 85 parts of aluminum oxide powder, 20 parts of nickel powder, 3 parts of cerium oxide powder, 0.6 part of ammonium chloride, The particle diameter of above-mentioned raw material is 300 orders;

[0038] Step 2. Mix the zinc powder, aluminum powder, alumina powder, nickel powder and cerium oxide powder weighed in step 1 evenly, heat to 150-200°C, keep warm for 30-50 minutes, cool to room temperature and then mix with After the ammonium chloride is mixed evenly, the co-penetration agent is prepared;

[0039] Step 3: Stack the plate-shaped metal parts with clean surface treatment into stacks with similar height and width, and lay a layer of infiltration agent prepared in s...

specific Embodiment 2

[0053] The preparation method of alloy co-infiltration, dacromet and sealing layer composite coating provided by this embodiment, the specific steps are the same as in specific embodiment 1, and different from specific embodiment 1 are:

[0054] In step 1, the co-infiltration agent raw materials are: 100 parts of zinc powder, 10 parts of aluminum powder, 100 parts of alumina powder, 30 parts of nickel powder, 5 parts of cerium oxide powder, and 0.8 part of ammonium chloride;

[0055] In step five, Dacromet antiseptic raw materials are:

[0056] Component A: 10 parts of zinc flakes and aluminum flakes, wherein the ratio of zinc flakes and aluminum flakes is 2:1; 55 parts of deionized water, 2.0 parts of fatty alcohol polyoxyethylene ether;

[0057] Component B: 10 parts of amorphous compound molybdate compound, 15 parts of barium salt, 0.6 part of hydrogen peroxide, and 1 part of polyethylene glycol;

[0058] In step six, after mixing and stirring the components A and B weighe...

specific Embodiment 3

[0062] The preparation method of alloy co-infiltration, dacromet and sealing layer composite coating provided by this embodiment, the specific steps are the same as in specific embodiment 1, and different from specific embodiment 1 are:

[0063] In step 1, the co-penetrating agent raw materials are: 100 parts of zinc powder, 20 parts of aluminum powder, 80 parts of alumina powder, 10 parts of nickel powder, 2 parts of cerium oxide powder, and 0.5 part of ammonium chloride;

[0064] In step five, Dacromet antiseptic raw materials are:

[0065] Component A: 10 parts of zinc flakes and aluminum flakes, wherein the ratio of zinc flakes and aluminum flakes is 2:3; 60 parts of deionized water, 0.5 parts of fatty alcohol polyoxyethylene ether;

[0066] Component B: 10 parts of amorphous compound molybdate compound, 5 parts of barium salt, 0.8 part of hydrogen peroxide, and 3 parts of polyethylene glycol;

[0067] In step six, after mixing and stirring the components A and B weighed ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
Vickers hardnessaaaaaaaaaa
Vickers hardnessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a method for preparing a composite coating of alloy co-infiltration, dacromet and sealing layer, which comprises the following steps: weighing the co-infiltration agent raw materials, mixing them uniformly to prepare the co-infiltration agent; treating the clean plate metal The pieces are stacked into stacks with similar height and width, and a layer of co-infiltration agent is laid between adjacent plate-shaped metal parts, and then packed into bundles and put into the co-infiltration furnace; Dacromet anti-corrosion raw materials are weighed, mixed and After stirring evenly, adjust the pH; place the plate-shaped metal parts in the coating liquid dipping cage, then impregnate the Dacromet anti-corrosion coating liquid, rotate and drain, send it to the online drying equipment for baking, and cool to room temperature; Cardanol glycidyl ether is used to prepare a curing agent at room temperature; the pre-preparation component and the curing reaction component are prepared, and the pre-preparation component and the curing reaction component are mixed uniformly to obtain a sealing liquid, and the rotating plate metal parts are subjected to Spraying; drying in a tunnel oven and then placed at room temperature for 24 hours.

Description

technical field [0001] The invention relates to the technical field of composite anticorrosion on the surface of metal parts, in particular to a method for preparing a composite coating of alloy co-infiltration, dacromet and sealing layer. Background technique [0002] Every year, the world's steel corrosion loss accounts for more than 10% of the total steel output, and the economic loss caused by corrosion in industrially developed countries accounts for more than 2% to 4% of the total output value of the national economy; research and develop advanced anti-corrosion technology to reduce economic losses caused by corrosion Prolonging the service life of steel and other metal materials and equipment is of great significance to promoting the development of advanced technology, cutting-edge science and defense industry, as well as the sustainable and coordinated development of the national economy and social environment. [0003] Multi-element alloy co-infiltration is a new ty...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D1/00C09D5/10C09D163/00C23C10/30
CPCC09D1/00C09D5/103C09D5/106C09D163/00C23C10/30
Inventor 晋华明
Owner HEBEI CHENYANG INDAL & TRADE GROUP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com