Water-based acrylic polyurethane top-coat

An acrylic polyurethane and water-based acrylic technology, applied in the field of coatings, can solve the problems of water resistance, chemical resistance, abrasion resistance and weather resistance, etc., and achieve the effect of improving anti-corrosion performance, being widely used, and saving resources.

Inactive Publication Date: 2016-03-09
TIANHENG PAINT CO LTD
View PDF3 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the water-based industrial coatings currently used in floor coatings, metal anti-rust paints and ship coatings in my country are not ideal in terms of water resistance, chemical resistance, abrasion resistance and weather resistance.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] Embodiment 1: a kind of water-based acrylic polyurethane topcoat, is made according to following weight ratio by following raw material: water-based acrylic resin 150Kg, deionized water 200Kg, defoamer 1Kg, titanium dioxide 180Kg, neutralizer 1Kg, trimer Aluminum phosphate 2Kg, precipitated barium sulfate 100Kg, rheology additive 10Kg, flash corrosion inhibitor 2Kg, talcum powder 25Kg, leveling agent 1Kg, catalyst 0.5Kg, antioxidant 2Kg, nano-magnesium sulfide 1Kg, ultraviolet absorber 1Kg.

Embodiment 2

[0015] Embodiment 2: A kind of water-based acrylic polyurethane topcoat is made according to the following weight ratio by following raw materials: water-based acrylic resin 200Kg, deionized water 300Kg, defoamer 3Kg, titanium dioxide 200Kg, neutralizer 3Kg, trimer Aluminum phosphate 6Kg, precipitated barium sulfate 150Kg, rheology additive 20Kg, flash corrosion inhibitor 4Kg, talcum powder 25Kg, leveling agent 3Kg, catalyst 2Kg, antioxidant 4Kg, nano-magnesium sulfide 4Kg, ultraviolet absorber 4Kg.

Embodiment 3

[0016] Embodiment 3: a kind of water-based acrylic polyurethane topcoat is made according to following weight ratio by following raw material: water-based acrylic resin 170Kg, deionized water 250Kg, defoamer 2Kg, titanium dioxide 190Kg, neutralizer 2Kg, trimer Aluminum phosphate 4Kg, precipitated barium sulfate 125Kg, rheological additive 15Kg, flash corrosion inhibitor 3Kg, talcum powder 25Kg, leveling agent 2Kg, catalyst 1.5Kg, antioxidant 3Kg, nano-magnesium sulfide 3Kg, ultraviolet absorber 2Kg.

[0017] The above water-based acrylic resin is made from the following raw materials: n-butyl acrylate (BA), styrene (ST), acrylic acid (AA), methacrylic acid (MAA), methyl methacrylate (MMA), N-methylol Acrylamide (NMA), Potassium Persulfate (K2S2O8), OP-10 and Sodium Alkyl Sulfate, Neutralizer, Propylene Glycol and Deionized Water.

[0018] The above-mentioned neutralizing agent is made by mixing butanol, triethanolamine and tributyl phosphate.

[0019] The above rheological ad...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

Water-based acrylic polyurethane top-coat is prepared from the following raw materials by a weight proportion: 150-200 parts of water-based acrylic resin, 200-300 parts of deionized water, 1-3 parts of defoamer, 180-200 parts of titanium dioxide, 1-3 parts of neutralizing agent, 2-6 parts of aluminium triphosphate, 100-150 parts of precipitated barium sulphate, 10-20 parts of rheological assistant, 2-4 parts of flash rusting inhibitor, 25 parts of talcum powder, 1-3 parts of flatting agent and 0.5-2 parts of catalyst; the top-coat is characterized by also being prepared from 2-4 parts of antioxidant, 1-4 parts of nanometer magnesium sulfide and 1-4 parts of ultraviolet light absorber. The water-based acrylic polyurethane top-coat is non-pollution, better in water resistance, chemical resistance, abrasive resistance and weather fastness, long in service life and high in hardness.

Description

Technical field: [0001] The invention relates to a coating, in particular to a water-based acrylic polyurethane topcoat. Background technique: [0002] With the continuous progress of society, the awareness of environmental protection in various countries continues to increase. However, the widely used solvent-based coatings contain a large amount of volatile organic compounds (VOC), which are toxic, flammable, pollute the atmosphere, and cause harm to the environment and human body. Therefore, in order to reduce the pollution of these organic solvents to the environment, my country has included water-based coatings in the future development direction of industrial coatings. However, the water resistance, chemical resistance, abrasion resistance and weather resistance of the water-based industrial coatings currently used in floor coatings, metal antirust paints and ship coatings in my country are not ideal. Invention content: [0003] The object of the present invention ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D133/08C09D125/14C09D175/04C09D5/08C09D5/18C09D7/12
CPCC09D133/08C08K3/22C08K5/521C08K13/02C08K2003/222C08K2201/011C09D5/08C09D5/18C09D7/61C09D7/63C09D125/14C09D175/04
Inventor 刘道海
Owner TIANHENG PAINT CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com