Bauxite and brucite concrete tubular pipe and preparation method therefor

A technology for concrete pipe piles and bauxite, which is applied in solid waste management, sustainable waste treatment, climate sustainability, etc. Detrimental pore and defect content, transformation-promoting, bonding surface densification effects

Inactive Publication Date: 2015-11-18
六安市永发新型建材有限责任公司
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Concrete structure is one of the most widely used structures. About 70% of the housing construction and 50% of bridge structures in China use concrete structures. With the increase of the service time of these engineering structures, the durability damage of concrete materials and structures is becoming more and more serious. The more attention is paid, many engineering structures often cause functional degradation or even structural damage due to durability, which brings unnecessary losses to society. Concrete carbonation is one of the important durability indicators of concrete. Due to carbon dioxide in the atmosphere and concrete The reaction of the alkaline substances in the concrete makes the concrete appear neutral, which is called the carbonization of the concrete. Carbonization makes the steel bars in the concrete structure lose the protection of the passivation film, which easily makes the steel bars rust, and then destroys the structure. With the continuous advancement of the industrialization process, the emission of carbon dioxide has increased greatly, which has a negative impact on the durability of concrete structures while producing the greenhouse effect;

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] A magnesite concrete pipe pile, which is composed of the following raw materials in parts by weight:

[0022] Dinonyl naphthalene sulfonate barium 3, bauxite 20, calcium phosphate 1, sodium thiosulfate 0.2, brucite wool 3, n-methylpyrrolidone 10, ordinary portland cement 640, yellow sand 400, gravel 300 , Polycarboxylate superplasticizer 15, polyethylene wax 20, dibenzoyl peroxide 0.2, maleic anhydride 6, polyethylene glycol monomethyl ether 2, ethyl cellulose 4, sp-800.7-2, waste rubber Powder 70.

[0023] A preparation method of aluminum magnesium stone concrete pipe pile, comprising the following steps:

[0024] (1) Add the above-mentioned polyethylene wax to No. 3 white oil that is 3 times its weight, add dibenzoyl peroxide and maleic anhydride, keep stirring at 140°C for 3 hours, cool the discharge to room temperature, and add to In acetone with 2 times the weight of the cooling material, fully stir, filter, dry, mix with polyethylene glycol monomethyl ether, add...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
compressive strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a bauxite and brucite concrete tubular pipe which is prepared from the raw materials in parts by weight: 2-3 parts of dinonyl barium naphthalenesulfonate, 13-20 parts of bauxite, 1-2 parts of calcium phosphate, 0.1-0.2 part of sodium thiosulfate, 3-7 parts of brucite amianthine, 7-10 parts of n-methyl pyrrolidinone, 500-640 parts of common silicate cement, 300-400 parts of yellow sand, 200-300 parts of gravels, 7-15 parts of a polycarboxylic acid based superplasticizer, 16-20 parts of polyethylene wax, 0.1-0.2 part of dibenzoyl peroxide, 5-6 parts of maleic anhydride, 2-3 parts of polyethylene glycol monomethyl ether, 4-7 parts of ethyecellulose, 0.7-2 parts of sp-80 and 50-70 parts of waste rubber powder. By doping ethoxylated rubber fiber, the inner pore structure of the concrete can be effectively improved to form a lot of close pores so as to prevent capillary pores from forming a continuous cut-through netty structural system, thereby forming an anti-carbonizing zone which plays a reinforcing effect in inhibiting invasion of carbon dioxide.

Description

technical field [0001] The invention relates to an aluminum-magnesite concrete pipe pile, in particular to an aluminum-magnesite concrete pipe pile and a preparation method thereof. Background technique [0002] Concrete structure is one of the most widely used structures. About 70% of the house construction and 50% of bridge structures in China use concrete structures. With the increase of the service time of these engineering structures, the durability damage of concrete materials and structures is becoming more and more serious. The more attention is paid, many engineering structures often cause functional degradation or even structural damage due to durability, which brings unnecessary losses to society. Concrete carbonation is one of the important durability indicators of concrete. Due to carbon dioxide in the atmosphere and concrete The reaction of alkaline substances in the concrete makes the concrete appear neutral, which is called the carbonization of concrete. Carb...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/04C04B18/22C04B16/06C04B24/26C04B14/30C04B14/36
CPCY02W30/91
Inventor 陈荣发
Owner 六安市永发新型建材有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products