Hydroxyalkyl cationic guar gum and its preparation method and application

A hydroxyalkyl cation and a technology for preparing hydroxyalkyl cation are applied in the directions of adding non-fiber pulp, textile and paper making, fiber raw material processing, etc., and can solve the problems of no disclosed method, low degree of product substitution, complex synthesis steps, etc., To achieve the effect of reducing energy consumption, shortening reaction time and shortening reaction cycle

Inactive Publication Date: 2007-05-30
SOUTH CHINA UNIV OF TECH
View PDF3 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the main problems of these patented technologies are that the synthesis steps are complicated, the degree of product substitution is low, and the method of using it as a pulp retention and drainage aid is not disclosed.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] 50 grams of unpurified guar collagen powder were dispersed into a mixed solution of 80 grams of industrial alcohol and 50 grams of water, added to a common three-necked bottle, ventilated with nitrogen, stirred at room temperature for 10 minutes, and added 10 grams of aqueous sodium hydroxide (hydrogen Sodium oxide concentration 25%) was soaked and alkalized for 1.5 hours, dripped 24 gram of 3-chlorine at room temperature, the solution of 2-hydroxypropyltrimethylammonium chloride and 10.5 gram of water, the time of adding was 20 minutes, then warming up to 55 degrees, after 3.5 hours of reaction, the material was transferred to the autoclave, and 5 grams of hexadecyl benzyl dimethyl ammonium chloride was added. gram of sodium hydroxide solution (concentration is 60%), and the reaction temperature spontaneously rises from room temperature to 40 degrees to react for 5 hours, cool down, and adjust the pH value to 8.5 with concentrated hydrochloric acid. The material is fil...

Embodiment 2

[0037] Disperse 50 grams of unpurified guar collagen powder into a mixture of 400 grams of isopropanol and 40 grams of water. After the materials are mixed, add them to a three-necked flask, ventilate nitrogen, stir at room temperature for 10 minutes, and add 50 grams of potassium hydroxide aqueous solution (concentration of potassium hydroxide 10%) was soaked and alkalized for 0.5 hour, added dropwise the solution of 10 gram epoxypropyltrimethylammonium chloride and 10 gram water at room temperature, and the time of adding was 20 minutes, then be warming up to 60 degree, After reacting for 3.0 hours, the material was transferred to the autoclave, and 5 grams of hexadecylbenzyldimethylammonium chloride was added. Under nitrogen and vacuum conditions, 10 grams of propylene oxide was inhaled, and the reaction temperature spontaneously increased from the chamber to 10 grams. The temperature was raised to 50°C and reacted for 1.5 hours, then the temperature was lowered to 35°C, and...

Embodiment 3

[0039] Disperse 50 grams of unpurified guar collagen powder into a mixture of 60 grams of tert-butanol and 60 grams of water. After the materials are mixed, add them to a three-necked bottle, vent nitrogen, stir at room temperature for 10 minutes, and add 30 grams of potassium hydroxide solution (concentration of potassium hydroxide 25%), soak and alkalinize at room temperature for 45 minutes, add dropwise 30 grams of homemade 3-chloro-2-hydroxypropylpyridine hydrochloride (light yellow transparent solution, effective concentration 70%), dropwise For 20 minutes, then at a temperature of 35 degrees, after reacting for 6 hours, the material was transferred to a high-pressure reactor, and 5.0 grams of cetylbenzyldimethylammonium chloride was added, and under nitrogen and vacuum conditions, Inhale 50 grams of propylene oxide, and the reaction temperature spontaneously rises from room temperature to 60 degrees to react for 4 hours, cool down, and adjust the pH value to 7.8 with citr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

A process for preparing the cationic hydroxyalkyl guar gum includes such steps as dispersing the raw powder of guar gum in the aqueous solution of low-carbon alcohol, adding high-alkaline catalyst, immersing, adding cationic etherifying agent, cationic graft reaction, adding phase-transfer catalyst and alkoxy etherifying agent, hydro-xyalkylating reaction, neutralizing and filtering. It can be used as the retention aid or filter aid of paper pulp.

Description

technical field [0001] The invention relates to the field of retention and drainage aids for paper pulp, specifically uses guar gum as a raw material to prepare waste paper pulp, wood pulp and straw pulp systems and retention and drainage aids in the process of making high-grade functional paper, especially relates to hydroxyalkyl cations Guar gum one-step slurry preparation method. Background technique [0002] At present, modified starch and cationic polyacrylamide (CPAM) are generally used as retention and drainage aids in the paper industry, but domestic starch raw materials come from different sources, there are many types, and the proportions of amylose and amylopectin are different, which seriously affects its modification. The stability of product quality limits its popularization and application. Larger domestic paper mills had to use wet-end additives produced by large foreign companies, resulting in increased paper costs. On the other hand, cationic polyacrylami...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D21H21/10D21H17/21
Inventor 万小芳李友明汪晓军宋林林
Owner SOUTH CHINA UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com