Method for preparing modified hydroxyl ester-based polymer emulsion

A technology of polymer emulsion and hydroxy ester group, applied in the direction of coating, etc., can solve the problems of performance such as adhesion, internal bonding force, tensile strength imbalance, etc., and achieve the effect of long service life, good water resistance and full response

Inactive Publication Date: 2020-01-24
HUBEI UNIV OF TECH
View PDF12 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] At present, waterproof coatings, while ensuring good waterproof performance, other aspects of performance such as adhesion, internal bonding force, tensile strength, etc. are unbalanced, and there is an urgent need for a comprehensive performance balance and better waterproof performance coating products

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing modified hydroxyl ester-based polymer emulsion
  • Method for preparing modified hydroxyl ester-based polymer emulsion

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0065] The raw materials required for the preparation of hydroxyester-based polymer waterproof coatings include the following components:

[0066] 1.3 parts of propylene alcohol;

[0067] 4.5 parts of (meth)n-butyl acrylate;

[0068] 42 parts of methacryl alcohol;

[0069] 380 parts of 2-phenoxyethyl methacrylate;

[0070] 0.09 parts of lauryl peroxide;

[0071] 2.9 parts of azobisisobutyronitrile;

[0072] 6.1 parts of azobisisovaleronitrile;

[0073] 6.2 parts of hydroxyethyl pyrphthalic anhydride dimethacrylate;

[0074] 0.15 parts of sodium methacrylate;

[0075] 0.7 part of graphene oxide;

[0076] 39 parts of copolyether of ethylene oxide and propylene oxide with a mass ratio of 2:1;

[0077] 10.74 parts of super concentrated emulsifier;

[0078] Hexadecane 5.0 parts;

[0079] 1.0 parts of polyvinyl alcohol;

[0080] 6.8 parts of sodium methoxide;

[0081] 7.3 parts of sodium hydroxide solution of 30% solubility;

[0082] The rest is water.

[0083] The tot...

example 2

[0093] The raw materials required for the preparation of hydroxyester-based polymer waterproof coatings include the following components:

[0094] 1.3 parts of methacryl alcohol;

[0095] 4.5 parts of isobutyl (meth)acrylate;

[0096] 42 parts of isopentenol;

[0097] 380 parts of 2-propylheptyl acrylate;

[0098] 0.09 parts of tert-butyl peroxy tert-valerate;

[0099] 2.9 parts of azobisisobutyric acid;

[0100] 6.1 parts of azodicyanovaleric acid;

[0101] 6.2 parts of two (methacryloyloxyethyl) phthalic anhydride esters;

[0102] 0.15 parts of sodium methacrylate;

[0103] 0.7 part of graphene oxide;

[0104] 39 parts of copolyether of ethylene oxide and propylene oxide with a mass ratio of 3:2;

[0105] 10.74 parts of super thick emulsifier;

[0106] 5.0 parts of cetyl alcohol;

[0107] 1.0 parts of polyvinylpyrrolidone;

[0108] 6.8 parts of sodium ethylate;

[0109] 7.3 parts of potassium hydroxide;

[0110] The rest is water.

[0111] The total mass is 1000,...

example 3

[0121] The raw materials required for the preparation of hydroxyester-based polymer waterproof coatings include the following components:

[0122] 3.7 parts of isopentenol;

[0123] 2.4 parts of lauryl (meth)acrylate;

[0124] 26 parts of 4-(ethyleneoxy)-1-butanol;

[0125] 410 parts of methacryloyloxyethyl phthalate monoester;

[0126] 0.17 parts of dicyclohexyl peroxydicarbonate;

[0127] 3.4 parts of dimethyl azobisisobutyrate;

[0128] 3.7 parts of azobisisoheptanonitrile;

[0129] 8.5 parts of hydroxyethyl pyrphthalic anhydride dimethacrylate;

[0130] 0.08 parts of sodium methacrylate;

[0131] 0.5 part of graphene oxide;

[0132] 26 parts of copolyether of ethylene oxide and propylene oxide with a mass ratio of 1:1;

[0133] 12.25 parts of super concentrated emulsifier;

[0134] 6.5 parts of octadecyl methacrylate;

[0135] 1.3 parts of hydroxypropyl cellulose;

[0136] 5.7 parts of ethanolamine;

[0137] 8.4 parts of sodium carbonate;

[0138] The rest is ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for preparing a modified hydroxyl ester polymer emulsion. Required raw materials comprise the following components in parts by mass: 1.0-4.2 parts of a hydrophilic small monomer for emulsification, 1.7-4.5 parts of a hydrophobic small monomer for emulsification, 18-51 parts of a hydroxyl small monomer, 0.05-0.26 part of an emulsion initiator, 2.2-5.4 parts of an initiator a, 3.5-6.6 parts of an initiator b, 380-450 parts of an ester small monomer, 6.2-9.3 parts of a crosslinking agent, 0.06-0.28 part of a chain transfer agent, 0.5-1.0 part of graphene oxide, 15-40 parts of polyether, 5-10 parts of a neutralizer, 5-10 parts of a pH regulator, 2.0-6.5 parts of an emulsifier promoter, 0.4-1.3 parts of a liquid film enhancer and the balance of water, wherein the total parts by mass are 1000, and the solid content is 50%. The waterproof coating disclosed by the invention is suitable for cement mixing; due to a large number of hydroxyl groups, calcium ions can be stably complexed, calcium ion hydrolysis can be effectively inhibited, the cement strength can be increased, and the waterproof effect can be improved; due to hydrogen bonds in molecules of the hydroxyl groups, the internal binding force of the polymer can be improved, and the adhesion of the polymer with a matrix can be improved through a good hydrophilic effect; due to addition of the graphene oxide, the tensile strength of a polymer emulsion in film formation can be remarkably improved; and the water resistance can be also improved to a certain extent.

Description

technical field [0001] The invention belongs to the technical field of building waterproof materials, in particular to a preparation method of a modified hydroxy ester-based polymer emulsion. Background technique [0002] Waterproof coatings are widely used in building waterproof materials due to their simple construction, high film strength and good waterproof effect. Hydroxyl ester-based polymer waterproof coatings are mainly composed of hydroxyl small monomers and ester-based small monomers. A waterproof coating with excellent performance can be applied to a wide range of waterproof markets. [0003] The waterproof market can be divided into three parts: tooling, home decoration, and leak repair. Tooling waterproofing refers to the waterproof design and construction applied to large-scale construction projects, and the amount is relatively large; home improvement waterproofing refers to small-scale waterproofing construction for commercial housing, private buildings and o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D129/06C09D133/08C09D7/61C08F2/00C08F2/24C08F2/38C08F216/08C08F220/18C08F220/20
CPCC08F2/001C08F2/24C08F2/38C08F216/08C08F220/18C08L2205/03C09D129/06C09D133/08C09D7/61C08L71/02C08L29/04C08K3/042C08F220/20C08F216/04
Inventor 王迎斌刘飞宏贺行洋苏英
Owner HUBEI UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities