Moisture absorption and perspiration fiber and preparation method thereof

A moisture-absorbing and sweat-wicking fiber, the same technology, applied in fiber processing, melt spinning, stretch spinning, etc., can solve the problems affecting the smooth progress of fiber spinning, inconsistent pressure drop, and difference in fiber extrusion speed. The effect of improving strength, improving compatibility, and excellent heat resistance stability

Active Publication Date: 2018-05-15
JIANGSU HENGLI CHEM FIBER
View PDF6 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Since the polyester melt is a non-Newtonian fluid and is a viscoelastic fluid, it will undergo elastic deformation and form a certain pressure while viscous flowing in the spinneret hole. Therefore, the polyester melt will flow out of the spinneret hole A certain pressure drop is generated, and the shape, size, length and relationship between the spinneret holes will have a great impact on the pressure drop. Existing research generally only considers the same shape or cross-sectional area of ​​the spinneret holes are equal, but the influence of shape, size and length is not involved, which will cause the pressure drop of the polyester melt to flow out from the different shapes of the spinneret holes of the same spinneret, so that the fibers with different cross-sections There is a difference in the extrusion speed between them, which affects the smooth progress of the fiber spinning process

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Moisture absorption and perspiration fiber and preparation method thereof
  • Moisture absorption and perspiration fiber and preparation method thereof
  • Moisture absorption and perspiration fiber and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0062] A moisture-absorbing and sweat-wicking fiber, the preparation method of which is as follows:

[0063] (1) preparation of oiling agent for oiling;

[0064] Mix 2-hydroxymethyl-12-crown-4 with potassium dodecyl phosphate, trimethylolpropane laurate and sodium hexadecylsulfonate at room temperature and add to 12# mineral oil and uniformly stirred at 40°C for 2.5h to obtain an oil agent; the addition amount of each component is as follows in parts by weight: 5 parts of 12# mineral oil; 95 parts of 2-hydroxymethyl-12-crown-4; 12 9 parts of potassium alkyl phosphate; 2 parts of sodium hexadecyl sulfonate. The content of crown ether in the prepared oil is 85.58wt%. The oil has excellent high temperature resistance. After heat treatment at 200°C for 2 hours, the thermal weight loss is 9wt%. The viscosity of the oil is low. When the kinematic viscosity is 29.5mm 2 / s, the kinematic viscosity after the concentration of 10wt% emulsion is configured with water is 0.93mm 2 / s, t...

Embodiment 2

[0069] A moisture-absorbing and sweat-wicking fiber, the preparation method of which is as follows:

[0070] (1) Preparation of oil preparation for oiling; 15-crown ether-5 and isomeric tridecyl alcohol polyoxyethylene ether phosphate potassium salt, trimethylolpropane laurate and sodium dodecylsulfonate at normal temperature After mixing evenly at low temperature, add it to 13# mineral oil and stir evenly at 52°C for 2 hours to obtain an oil agent; in parts by weight, the addition amount of each component is as follows: 10 parts of 13# mineral oil; trimethylolpropane lauric acid 5 parts of ester; 70 parts of 15-crown ether-5; 8 parts of isomeric tridecyl polyoxyethylene ether phosphate potassium salt; 6 parts of sodium dodecylsulfonate. The content of the crown ether in the prepared oil is 70.70wt%. The high temperature resistance of the oil is excellent. After heat treatment at 200°C for 2 hours, the thermal weight loss is 13.5wt%. The viscosity of the oil is low, at (50 ± 0...

Embodiment 3

[0075] A moisture-absorbing and sweat-wicking fiber, the preparation method of which is as follows:

[0076] (1) Oil preparation for oiling; 2-hydroxymethyl-15-crown-5 and potassium salt of tetradecyl phosphate, trimethylolpropane laurate and sodium pentadecylsulfonate After mixing evenly at room temperature, add it to 11# mineral oil and stir evenly at 48°C for 3 hours to obtain an oil agent; in parts by weight, the addition amount of each component is as follows: 8 parts of 11# mineral oil; trimethylolpropane lauryl 10 parts of acid ester;

[0077] 2-Hydroxymethyl-15-crown-585 parts; Tetradecyl phosphate potassium salt 11 parts; Sodium pentadecylsulfonate 5 parts. The content of crown ether in the prepared oil is 70.83wt%. The oil has excellent high temperature resistance. After heat treatment at 200°C for 2 hours, the thermal weight loss is 11wt%. The viscosity of the oil is low. When the kinematic viscosity is 30.1mm 2 / s, the kinematic viscosity after the concentration...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Finenessaaaaaaaaaa
Finenessaaaaaaaaaa
Finenessaaaaaaaaaa
Login to View More

Abstract

The invention relates to a moisture absorption and perspiration fiber and a preparation method thereof. The moisture absorption and perspiration fiber is prepared by measuring polyester melt, extruding by a compositing spinneret plate, cooling, oiling, stretching, thermally shaping and coiling, wherein the composite spinneret plate is provided with a cross spinneret hole and a spinneret hole shaped like the Chinese character Wang, a length ratio of micropores of the cross spinneret hole and the spinneret hole shaped like the Chinese character Wang is equal to a product of an equivalent diameter ratio of the cross spinneret hole and the spinneret hole shaped like the Chinese character Wang and a coefficient K, the equivalent diameter is a ratio of an area and perimeter of a cross section ofthe spinneret hole, the valuing range of the coefficient K is 0.97 to 1.03, an oiling agent comprises crown ether, the content of the crown ether is 67.30 to 85.58 percent, and a capillary parameterof the prepared moisture absorption and perspiration fiber is greater than or equal to 0.16. The preparation method is simple and reasonable in method, and the prepared fiber has excellent moisture absorption and perspiration performance and has good popularization value.

Description

technical field [0001] The invention belongs to the field of fiber preparation, and relates to a moisture-absorbing and sweat-wicking fiber and a preparation method thereof. Background technique [0002] Since the appearance of polyethylene terephthalate (PET) fiber, it has developed rapidly because of its excellent performance, and its output has become the crown of synthetic fiber in the world. PET fiber has a series of excellent properties such as high breaking strength, high elastic modulus, moderate resilience, excellent heat setting performance, good heat resistance and light resistance, acid resistance, alkali resistance and corrosion resistance, and the fabric prepared by it has anti-wrinkle and With good stiffness and other advantages, it is widely used in the fields of fiber, bottle packaging, film and sheet, etc. The output is increasing year by year, and the industry status has been significantly improved. However, due to the high crystallinity, compact structur...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D01F6/62D01F11/08D01D5/08D01D5/088D01D5/16D01D5/253D01D10/02
CPCD01D5/08D01D5/088D01D5/16D01D5/253D01D10/02D01F6/62D01F11/08
Inventor 汤方明张群晏金龙王雪王永锋
Owner JIANGSU HENGLI CHEM FIBER
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com