Anti-corrosion and fireproof antibacterial epoxy paint

An antibacterial coating, epoxy technology, applied in the direction of anti-corrosion coatings, fire-proof coatings, epoxy resin coatings, etc., to achieve good anti-static effect, water resistance, and improved anti-bacterial effect

Inactive Publication Date: 2017-05-31
合肥英索莱特新材料科技有限公司
View PDF6 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Commonly used anti-corrosion coatings can no longer meet these needs

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0010] Embodiment 1: a kind of epoxy anticorrosion fireproof antibacterial coating, the raw material according to weight percentage comprises: epoxy resin 23%, phenalkamine 5%, nano-titanium dioxide 6%, nano-silica 5%, nano-zinc oxide 4%, remove Ionized water 8%, methylisothiazolinone 4%, polyhedral silsesquioxane 3%, butylated amino resin 5%, flake graphite 4%, glass flake 3%, sericite powder 2%, trimer Aluminum phosphate 2%, zinc phosphate 2%, aluminum oxide 3%, tertiary amine curing accelerator 1%, silane coupling agent 2%, ethanol ethyl ether acetate 7%, diluent 1%, cellulose acetate 3%, Melamine fiber 3%, aqueous magnesium hydroxide 4%.

[0011] Further, the nano titanium dioxide is anatase titanium dioxide.

[0012] The technical effects of the present invention are: the epoxy anti-corrosion, fire-proof and anti-bacterial coating obtained according to the above formula has the characteristics of fire-proof and flame-retardant, anti-bacterial, tough coating film, wear-re...

Embodiment 2

[0013] Embodiment 2: a kind of epoxy anticorrosion fireproof antibacterial coating, the raw material according to weight percentage comprises: epoxy resin 28%, phenalkamine 6%, nano-titanium dioxide 5%, nano-silica 5%, nano-zinc oxide 5%, remove Ionized water 8%, methylisothiazolinone 4%, polyhedral silsesquioxane 3%, butylated amino resin 5%, flake graphite 3%, glass flake 3%, sericite powder 1%, trimer Aluminum phosphate 1%, zinc phosphate 1%, aluminum oxide 1%, tertiary amine curing accelerator 1%, silane coupling agent 1%, ethanol ethyl ether acetate 6%, diluent 1%, cellulose acetate 2%, Melamine fiber 4%, aqueous magnesium hydroxide 6%.

[0014] Further, the nano titanium dioxide is anatase titanium dioxide.

[0015] The technical effect of the present invention is that: the epoxy anti-corrosion, fire-proof and anti-bacterial coating obtained according to the above formula has the characteristics of fire-proof and flame-retardant, anti-bacterial, tough coating film, wear-r...

Embodiment 3

[0016] Embodiment 3: a kind of epoxy anticorrosion fireproof antibacterial coating, the raw material according to weight percentage comprises: epoxy resin 22%, phenalkamine 6%, nano-titanium dioxide 7%, nano-silica 7%, nano-zinc oxide 6%, go Ionized water 9%, methylisothiazolinone 5%, polyhedral silsesquioxane 3%, butylated amino resin 5%, flake graphite 4%, glass flake 2%, sericite powder 2%, trimer 1% aluminum phosphate, 1% zinc phosphate, 2% aluminum oxide, 1% tertiary amine curing accelerator, 1% silane coupling agent, 6% ethanol ether acetate, 1% diluent, 3% cellulose acetate, Melamine fiber 3%, aqueous magnesium hydroxide 3%.

[0017] Further, the nano titanium dioxide is anatase titanium dioxide.

[0018] The technical effect of the present invention is that: the epoxy anti-corrosion, fire-proof and anti-bacterial coating obtained according to the above formula has the characteristics of fire-proof and flame-retardant, anti-bacterial, tough coating film, wear-resistant...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to an anti-corrosion and fireproof antibacterial epoxy paint. The anti-corrosion and fireproof antibacterial epoxy paint contains the following raw materials in percentage by weight: 20-30% of epoxy resin, 3-8% of phenolic aldehyde amine, 3-8% of nanometer titania, 3-8% of nanosilicon dioxide, 3-8% of nano-zinc oxide, 5-10% of deionized water, 3-8% of methylisothiazolinone, 2-5% of polyhedral oligomeric silsesquioxane, 4-8% of butylated amino resin, 3-6% of flaky graphite, 2-4% of glass flake, 1-3% of sericite powder, 1-3% of aluminium triphosphate, 1-3% of zinc phosphate, 1-4% of aluminium oxide, 1-2% of a tertiary amine curing accelerator, 1-3% of a silane coupling agent, 5-10% of ethoxyethyl acetate, 1-2% of a diluent, 2-4% of cellulose acetate, 2-5% of melamine fiber and 2-6% of waterborne magnesium hydroxide. The anti-corrosion and fireproof antibacterial epoxy paint obtained according to the formula has the advantages of fireproof and flame-retardant property, antibacterial property, tough paint film, wear resistance, good adhesion force, chemical corrosion resistance, water resistance and so on.

Description

technical field [0001] The invention relates to an anti-corrosion coating, in particular to an epoxy anti-corrosion, fire-proof and anti-bacterial coating. Background technique [0002] With the development of modern industry, the emergence of a number of emerging industrial fields and the construction of many modern projects have put forward higher requirements for the ability and service life of anti-corrosion coatings to withstand the environment. Commonly used anti-corrosion coatings can no longer meet these needs. The concept of "Heavy Duty Coating" proposed by people generally refers to the use in harsh corrosive environments, including supporting coatings for primers and topcoats. To put it simply: heavy-duty anti-corrosion coatings are coatings that have a longer service life and can adapt to more harsh environments. In chemical atmosphere and marine environment, heavy-duty anti-corrosion coatings can generally be used for more than 10 years or 15 years. In acid, a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D163/00C09D5/08C09D5/18C09D5/14C09D7/12
CPCC09D163/00C08K2201/011C08L2201/02C08L2201/08C08L2205/035C09D5/08C09D5/14C09D5/18C09D7/61C09D7/63C09D7/65C09D7/70C08L1/12C08L83/04C08K13/04C08K3/36C08K2003/2241C08K5/47C08K2003/2296C08K2003/2224
Inventor 倪世宏王华林
Owner 合肥英索莱特新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com