High-performance modified chloroprene rubber adhesive

A chloroprene rubber and adhesive technology, applied in the direction of chloroprene adhesives, adhesives, adhesive additives, etc., can solve the problems of low temperature resistance, weather resistance and heat resistance, limited application range, storage Poor stability and other problems, to achieve the effect of improving storage stability, good viscosity increasing effect, and good compatibility

Inactive Publication Date: 2016-01-13
安徽大松树脂有限公司
View PDF4 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, neoprene adhesives have the disadvantages of poor storage stability, unsatisfactory low temperature resistance, weather resistance and heat resistance, which limit its application range.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020]A kind of high-performance modified chloroprene rubber adhesive proposed by the present invention, its raw material comprises the following components by weight: 70 parts of chloroprene rubber, 15 parts of butadiene rubber, 5 parts of styrene-butadiene rubber, alkyl benzoic acid resin 15 parts, 3 parts of p-tert-butylphenolic resin, 5 parts of terpene resin, 1 part of nano-silica, 5 parts of nano-alumina, 2 parts of organic bentonite, 12 parts of white carbon black, 3 parts of activated magnesium oxide, polystyrene 3.5 parts of ethylene, 1 part of ethylene thiourea, 8 parts of zinc oxide, 30 parts of ethyl acetate, 25 parts of cyclohexane, 60 parts of dimethyl carbonate, 30 parts of propylene glycol, 10 parts of methylcyclopentane, 120# 35 parts of mineral spirits, 0.5 parts of resorcinol-formaldehyde resin, 3.5 parts of anti-aging agent, 2 parts of cerium oxide, 2.5 parts of silane coupling agent KH-560, and 3 parts of plasticizer.

Embodiment 2

[0022] A kind of high-performance modified chloroprene rubber adhesive proposed by the present invention, its raw material comprises the following components by weight: 100 parts of chloroprene rubber, 5 parts of butadiene rubber, 20 parts of styrene-butadiene rubber, alkyl benzoic acid resin 5 parts, 10 parts of p-tert-butylphenolic resin, 2 parts of terpene resin, 5 parts of nano-silica, 1 part of nano-alumina, 8 parts of organic bentonite, 5 parts of white carbon black, 10 parts of activated magnesium oxide, polystyrene 1 part of ethylene, 5 parts of ethylene thiourea, 2 parts of zinc oxide, 50 parts of ethyl acetate, 10 parts of cyclohexane, 120 parts of dimethyl carbonate, 10 parts of propylene glycol, 25 parts of methylcyclopentane, 120# 10 parts of solvent oil, 2 parts of resorcinol-formaldehyde resin, 1 part of anti-aging agent RD, 5 parts of cerium oxide, 1 part of silane coupling agent KH-5601, 3 parts of dioctyl sebacate, 2 parts of butyl oleate;

[0023] Wherein, t...

Embodiment 3

[0025] A kind of high-performance modified chloroprene rubber adhesive proposed by the present invention, its raw material comprises the following components by weight: 90 parts of chloroprene rubber, 12 parts of butadiene rubber, 11 parts of styrene-butadiene rubber, alkyl benzoic acid resin 11 parts, 6 parts of p-tert-butylphenolic resin, 3.5 parts of terpene resin, 3.8 parts of nano-silica, 3.9 parts of nano-alumina, 5.2 parts of organic bentonite, 10 parts of white carbon black, 5.8 parts of activated magnesium oxide, polystyrene 2.6 parts of ethylene, 3.2 parts of ethylene thiourea, 6 parts of zinc oxide, 40 parts of ethyl acetate, 20 parts of cyclohexane, 89 parts of dimethyl carbonate, 24 parts of propylene glycol, 19 parts of methylcyclopentane, 120# 25 parts of solvent oil, 1.1 parts of resorcinol-formaldehyde resin, 0.2 parts of anti-aging agent AW, 0.3 parts of anti-aging agent RD, 0.2 parts of anti-aging agent, 0.5 parts of anti-aging agent 4010NA, 1.1 parts of anti...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
The average particle sizeaaaaaaaaaa
The average particle sizeaaaaaaaaaa
The average particle sizeaaaaaaaaaa
Login to View More

Abstract

The present invention discloses a high-performance modified chloroprene rubber adhesive, wherein the raw materials comprise chloroprene rubber, cis-polybutadiene rubber, styrene-butadiene rubber, an alkyl benzoic acid resin, a p-tert-butyl phenol formaldehyde resin, a terpene resin, nanometer silica, nanometer alumina, organic bentonite, white carbon black, active magnesium oxide, polystyrene, ethylene thiourea, zinc oxide, ethyl acetate, cyclohexane, dimethyl carbonate, propylene glycol, methyl cyclopentane, 120# solvent oil, a resorcinol-formaldehyde resin, an anti-aging agent, cerium oxide, a silane coupling agent KH-560 and a plasticizer. According to the present invention, the high-performance modified chloroprene rubber adhesive has characteristics of high bonding strength, good low temperature resistance, good weather resistance, good heat resistance, good aging resistance, and excellent storage stability.

Description

technical field [0001] The invention relates to the technical field of neoprene rubber adhesives, in particular to a high-performance modified neoprene rubber adhesive. Background technique [0002] Neoprene is the main raw material of neoprene adhesive, its molecular structure is regular, and there are polar chlorine atoms on the molecular chain, which makes neoprene have high cohesive strength and flame resistance at room temperature And the aging resistance is good, the adhesive formulated with it can be cold-cured at room temperature, the initial adhesion is very large, the strength is quickly established, and the bonding strength is high. It can be used for bonding rubber, leather, fabric, Artificial leather, plastic, wood, paper, glass, ceramics, etc. However, neoprene adhesives have the disadvantages of poor storage stability, unsatisfactory low temperature resistance, weather resistance and heat resistance, which limit their application range. Contents of the inve...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09J111/00C09J11/08C09J11/06C09J11/04
Inventor 朱立芳
Owner 安徽大松树脂有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com