Adsorbing agent for removing trace amount of nitric oxide in carbon dioxide and preparation

A carbon dioxide and nitric oxide technology, applied in the field of environmental resources, can solve the problems of adsorption capacity, limited adsorption capacity, low metal utilization rate, etc., and achieve high purification capacity, high thermal stability and thermal regeneration, and good adsorption capacity. Effect

Inactive Publication Date: 2008-11-05
DALIAN UNIV OF TECH
View PDF2 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the adsorption of NO under anaerobic conditions is very limited, and only the conversion of NO into NO 2 , in order to better absorb and store
[0005] In the literature (Langmuir 17 (2001) 4997-5003), Helen Y.Huang et al prepared Fe-Mn-Ti mixed metal oxides for the adsorption of NO under aerobic conditions, CO 2 It has a greater impact on the adsorption capacity, and the metal utilization rate is relatively low

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] Accurately weigh 80g of HZSM-5 (25) raw powder and 20g of pseudo-boehmite (both on a dry basis); use a 100-200 mesh sieve to thoroughly mix the two, add 5% nitric acid, and stir into sand After that, the squeezing bar machine squeezed into a bar with a diameter of 2.5mm; dried at room temperature and transferred to an oven, dried at 120°C for 12 hours, placed in a muffle furnace, and heated at a rate of 10°C / min at room temperature It is calcined at a constant temperature of 550°C for 5 hours to prepare a hard white alumina-HZSM-5 composite carrier.

[0028] Accurately weigh 309mg Ce(NO 3 ) 4 ·6H 2 O, add 95ml of deionized water to dissolve, and this solution impregnates 99.7g of the above composite carrier. After immersion, it is placed at room temperature for 4 hours, transferred to an oven, dried at 105°C for 12 hours, then placed in a muffle furnace, heated to 500°C at room temperature at 10°C / min, and roasted at a constant temperature for 3 hours to prepare the adsorpt...

Embodiment 2

[0030] Accurately weigh 7.902g Co(NO 3 ) 2 ·6H 2 O, add 36ml of deionized water to dissolve, soak 40g of adsorbent precursor P with this solution, put it at room temperature for 4 hours after dipping, transfer to an oven, dry at 105°C for 12 hours, then put it in a muffle furnace at room temperature Next, the temperature was increased to 500°C by a program of 10°C / min, and the temperature was roasted for 5 hours to prepare the NO adsorbent (YC-1).

Embodiment 3

[0032] Accurately weigh 7.925g Ni(NO 3 ) 2 ·6H 2 O, add 36 ml of deionized water to dissolve, and impregnate 40 g of the adsorbent precursor P with this solution, and prepare the NO adsorbent (YC-2) according to the operation method of Example 2.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to an adsorbent for removing trace amount of nitric oxide in carbon dioxide and a preparation method thereof, and pertains to the technical field of environment resources and is characterized by providing the adsorbent prepared by taking alumina-HZSM-5 as a carrier and the preparation method, which is used for removing the trace amount of nitric oxide in carbon dioxide; the carrier of the adsorbent loads an activation auxiliary agent Ce salt and one of active components of Co, Ni and Mn, or two metal salts of Mn and Ni or Mn and Co by an equal volume impregnation-high temperature roasting method. The invention have the effects and benefits that the adsorbent has high purification degree and good thermal stability, can be able to remove the nitric oxide in the carbon dioxide to lower than 0.1ppmv under an oxygen free condition and an aerobic condition, and can be reproduced by being heated and scavenged with dry air, nitrogen and carbon dioxide after adsorption saturation; the invention provides a key technology for the preparation of food-grade carbon dioxide and has wide application prospect.

Description

Technical field [0001] The invention belongs to the technical field of environmental resources, and relates to an adsorbent for removing trace amounts of nitric oxide in carbon dioxide and a preparation method thereof. Background technique [0002] Food grade CO 2 Not only an important additive in the food industry, but also in CO 2 The applications in the polyester industry and the medical field are becoming more and more extensive. Recovery of CO in flue gas 2 Often accompanied by trace nitrogen oxides (NO and NO 2 ), where the content of NO accounts for NO x It is more than 90%, and it is difficult to remove. CO 2 Other light components in the impurities can be separated by low-temperature rectification, but because the concentration of NO is very low (<200ppmv), and after a period of time, it is easy to oxidize to NO 2 , Can not be removed by distillation, so that CO 2 Meet food grade requirements. At present, the main application methods for NO removal are catalytic reduc...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B01J20/18B01J20/30B01D53/04
CPCY02C10/08Y02C20/40
Inventor 陈绍云张永春郭新闻
Owner DALIAN UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com