Vinyl ester resin building steel-bar-planting glue and preparation method thereof

A technology of vinyl ester resin and planting glue, applied in the direction of adhesives, etc., can solve the problems of flowing storage period, low viscosity of glue, large volatile content, etc., and achieve long storage and service life, high curing strength, and strong bonding. Effect

Active Publication Date: 2005-03-16
江苏大力士云石护理材料有限公司
View PDF0 Cites 23 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Use hot-melt glue or polystyrene glue, which contains more than 40% low-molecular solvents, which is not conducive to the health of decoration construction workers; in China, epoxy resin is mainly used to make glue on site, which is inconvenient for construction; epoxy resin is also used. Or acrylic acid to prepare two-component adhesives, but there are disadvantages such as high brittleness, large volatile content, air pollution, low viscosity of glue, flowing phenomenon and short shelf life.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] 35% of MFE-3 vinyl polyester resin (produced by Huachang Polymer Co., Ltd.), 5% of crystalline unsaturated polyester resin Crystic Impreg (ScottBacler company), 0.3% of N.N-diethylaniline %, BYKA-555 (produced by German BYK chemical company) 0.2%, KH-560 (γ-(2,3 glycidoxy) propyltriethoxysilane) 0.1%, tert-butylcatechol 0.1% , benzoquinone 0.2%, and liquid polysulfide rubber 6% are poured into the stirring tank in turn, and poured while stirring; after stirring evenly, 50% of quartz powder (150 mesh), aluminum powder: 3% (325 mesh) ) into the stirring tank, pour it in while stirring, mix well, then raise the temperature of the stirring tank to 70°C, vacuumize, and stir for 2 hours to obtain component A;

[0027] Mix 50% of benzoyl peroxide and 20% of dibutyl phthalate in component B and mix well, then add 28% of quartz powder (150 mesh) and 2% of carbon black into the mixture, stirring while adding While adding, mix well to obtain component B.

[0028] When in use, mi...

Embodiment 2

[0030] 36% of MFE-3 vinyl polyester resin (produced by Huachang Polymer Co., Ltd.), 5% of crystalline unsaturated polyester resin Crystic Impreg, 0.3% of cobalt naphthenate, N.N-diethyl Pour aniline 0.05%, BYKA-555 (Germany BYK chemical company) 0.2%, KH-560 0.05%, tert-butyl catechol 0.1%, naphthoquinone 0.2%, liquid polysulfide rubber 5% into the stirring tank in turn , pour in while stirring; after stirring evenly, add 50% of quartz powder (150 mesh) and 3% of aluminum powder (325 mesh) into the stirring tank, pour in while stirring, mix well, and then put the stirring tank Raise the temperature to 70°C, vacuumize, and stir for 2 hours to obtain component A;

[0031] Mix 50% of cyclohexanone peroxide and 20% of dibutyl phthalate in component B and mix well, then add 28% of quartz powder (150 mesh) and 2% of iron oxide red into the mixture, and when adding Add while stirring, and mix well to obtain component B.

[0032] When in use, mix the ratio of component A: component ...

Embodiment 3

[0034] 38% of MFE-3 vinyl polyester resin (produced by Huachang Polymer Co., Ltd.), organic bentonite 2%, fumed silica 2%, N.N-diethylaniline 0.3%, methyl 0.2% of silicone oil, 0.1% of KH-550 (γ-aminopropyltriethoxysilane), 0.1% of tert-butylcatechol, 0.2% of hydroquinone, and 6% of liquid nitrile rubber are poured into the stirring tank in sequence, Pour in while stirring; after stirring evenly, add 48% of quartz powder (150 mesh) and 3% of iron powder into the stirring tank, pour in while stirring, mix well, then heat the stirring tank to 70°C, Vacuumize and stir for 2 hours to obtain component A;

[0035] Mix 50% of benzoyl peroxide and 20% of dibutyl phthalate in component B and mix well, then add 25% of quartz powder (150 mesh) and 2% of iron oxide green into the mixture, and when adding Add while stirring, and mix well to obtain component B.

[0036] When in use, mix the ratio of component A: component B = 100: 1.5 and mix evenly to obtain vinyl ester resin building re...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a vinyl ester resin building steel-bar-planting glue and preparation method thereof, wherein the glue comprises component A and component B by the weight ratio of 100 : 1-3, the component A comprises vinyl ester resin 30-45%, thickening agent 4-10%, filling material 40-55%, toughening agent 5-10%, defoaming agent 0.05-0.5%, coupling agent 0.05-0.5%, polymerization inhibitor 0.05-0.3%, accelerating agent 0.05-0.5%, and the component B comprises curing agent 50-70%, thinning agent 10-30%, filling material 10-30%, pigment 1-2%.

Description

technical field [0001] The invention relates to the field of chemical raw materials, in particular to vinyl ester resin building reinforcement glue and a preparation method thereof. Background technique [0002] With the vigorous development of the construction industry and the widespread application of building structure rubber-to-reinforcement technology, the amount of adhesives is increasing. The original bonding process and adhesives have many deficiencies. Use hot-melt glue or polystyrene glue, which contains more than 40% of low-molecular solvents, which is not conducive to the health of decoration construction workers; in China, epoxy resin is mainly used to make glue on site, which is inconvenient for construction; epoxy resin is also used. Or acrylic acid to prepare two-component adhesives, but there are disadvantages such as high brittleness, large volatile content, air pollution, low viscosity of glue, flowing phenomenon and short shelf life. Contents of the in...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J131/00
Inventor 黄志雄于浩谢文峰梅启林秦岩李俊菊李健
Owner 江苏大力士云石护理材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com