OMC/sponge Pb composite structure material lead plaster and preparing method and application thereof

A composite structure, sponge technology, applied in the field of electrochemistry, can solve the problems of short cycle life, uneven dispersion of carbon materials, slow research progress, etc., to achieve the effect of ensuring stability

Inactive Publication Date: 2019-11-05
ZHAOQING LEOCH BATTERY TECH
View PDF6 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, traditional lead-acid batteries have disadvantages such as low specific energy and short cycle life, which cannot meet the needs of long-life and high-capacity batteries in modern society. The electrochemical properties of electrode materials have an important impact on the performance of lead-acid batteries. There are few types of anode materials that have the same status as Pb in practical applications, and the research progress is slow
The traditional method of preparing lead paste for carbon material modified electrodes is to mix carbon material and lead powder, and then add water and sulfuric acid to prepare lead paste. Preparation of the negative electrode of the lead-acid battery is easy to cause the local energy density of the plate to be low

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • OMC/sponge Pb composite structure material lead plaster and preparing method and application thereof
  • OMC/sponge Pb composite structure material lead plaster and preparing method and application thereof
  • OMC/sponge Pb composite structure material lead plaster and preparing method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0049] Add 50g of OMC to 2000ml of 10% H 2 o 2 Solution, accompanied by stirring, reacted for 2h, and the reaction temperature was 60°C. After the reaction, the reactants were cooled to room temperature, the supernatant solution was removed, the obtained suspension was centrifuged 3 times, washed and filtered with deionized water repeatedly until neutral, and dried in a drying oven at 60°C to constant weight; A hydrophilic ordered mesoporous carbon is obtained.

[0050] The characterization methods of OMC are as follows: (1) Burier transform infrared spectroscopy (FT-IR, Nicolet6700) to characterize the functional groups of the sample; (2) laser Raman spectrometer (Raman, Dilor LABRAM-1B microscope) to characterize the structure of the sample (3) X-ray diffractometer (XRD, Philips XPert pro MPD) characterizes the crystal phase composition of the sample; (4) Scanning electron microscope (SEM, JSM-7500F) characterizes the surface morphology of the sample; (5) Transmission elec...

Embodiment 2

[0080] Weigh 50 g of the hydrophilic OMC prepared in Example 1 and add it into 100 kg of deionized water, and stir for 30 min at a room temperature of 25° C. to obtain a uniform OMC dispersion.

[0081] The OMC dispersion is added into a paste mixer and mixed with 1000kg of lead powder to obtain a mixture. In order to realize the uniform mixing of OMC and lead powder, and to ensure the stability of negative OMC / sponge Pb composite lead paste paste, the binding ability of the plate and lead paste, add bonding agent during the mixing and stirring process of OMC dispersion liquid and lead powder Substance short fiber, its addition amount is 0.015% of the overall mass of the mixture.

[0082] In the mixture of mixed OMC and lead powder, add 100kg of sulfuric acid with a density of 1.325g / ml and stir for 20min, the reaction temperature is controlled at 65°C, and the obtained OMC / sponge Pb composite material lead paste has an apparent density of 4.28g / cm 3 .

[0083] The surface...

Embodiment 3

[0104] Negative plate prepared by machine coating: the apparent density prepared in Example 2 is 4.28g / cm 3 The OMC / sponge Pb composite material lead paste is used to prepare the OMC-based composite negative electrode, or in other words, the OMC-based composite negative electrode is the OMC / sponge Pb composite electrode. Among them, the OMC / sponge Pb composite material lead paste is all coated on the negative grid. The size of the negative grid is: 68mm×44mm×1.7mm, and it is made of lead-calcium-tin alloy with a calcium content of 0.09% and a tin content of 0.3%. . Certainly, the lug portion of the negative electrode grid does not need to be coated. The negative electrode grid coated with the sponge Pb composite material lead paste is continuously cured for 24 hours at 60°C and humidity 85-95%; then continuously dried for 24 hours at 60°C and humidity less than 50% to make the negative electrode The plate is the OMC-based composite negative electrode. After the composite el...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
densityaaaaaaaaaa
Login to view more

Abstract

An OMC/sponge Pb composite structure material lead plaster and a preparing method and an application thereof are provided. The preparing method comprises the following steps: performing passivation modification processing on OMC by using hydrogen peroxide, to obtain hydrophilic OMC; configuring the hydrophilic OMC into OMC dispersion liquid by using deionized water, wherein a mass ratio of the hydrophilic OMC to the deionized water is 1:2000 to 1:3500; mixing and stirring the OMC dispersion liquid and lead powder at the mass ratio of 0.1:1 to 0.11:1, to obtain a mixture; and adding sulfuric acid to the mixture, and performing mechanical agitation and mixing to prepare the OMC /sponge Pb composite structure material lead plaster. Therefore, OMC and lead powder can be mixed uniformly, and robustness of negative OMC/sponge Pb composite material pasting and a bonding capability of a polar plate and lead plaster can be ensured.

Description

technical field [0001] The present application relates to the technical field of electrochemistry, in particular to an OMC / sponge Pb composite structural material lead paste and its preparation method and application. Background technique [0002] With the advantages of low cost and mature technology, traditional lead-acid batteries have been successfully used in communications, electric vehicles and other systems. They are an energy storage battery that conforms to my country's industrial layout and manufacturing level. However, traditional lead-acid batteries have disadvantages such as low specific energy and short cycle life, which cannot meet the needs of long-life and high-capacity batteries in modern society. The electrochemical properties of electrode materials have an important impact on the performance of lead-acid batteries. There are very few types of anode materials that have the same status as Pb in practical applications, and the research progress is slow. The...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): H01M4/36H01M4/57H01M4/62H01M10/06
CPCH01M4/362H01M4/57H01M4/625H01M10/06Y02E60/10
Inventor 高士元
Owner ZHAOQING LEOCH BATTERY TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap