Production method for environmental-friendly low-temperature-resistant antiflaming compound plasticizer

A flame-retardant compounding and production method technology, which is applied in the production field of environmentally friendly low-temperature resistant flame-retardant composite plasticizers, can solve problems such as low mechanical properties of plasticizer products, achieve improved mechanical properties, be environmentally friendly, and enhance flame-retardant properties Effect

Pending Publication Date: 2017-03-15
JIANGSU SENHE CHEM TECH CO LTD
View PDF3 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] (2) How to improve the technical problem of the low mechanical properties of the plasticizer product of the present invention due to the addition of the low temperature flame retardant system

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] This embodiment is a production method of an environmentally friendly low temperature resistant flame retardant composite plasticizer, comprising the following steps:

[0023] (1) Preparation of plasticizer matrix:

[0024] (1) Esterification: Pour the measured decanol into the reactor according to the ratio. After the temperature of the reactor is lower than 80°C, add sebacic acid according to the ratio, and then add the catalyst according to the ratio. When the temperature of the material rises to 220°C, the negative Pressure reaction, when the acid value <0.1mgKOH / g, carry out flash dealcoholization; the weight ratio of sebacic acid and decanol is: sebacic acid: 1 part, decanol: 1.57 parts; the addition amount of catalyst is decanol 0.2% of the total weight of diacid and decanol;

[0025] (2) Refining: After the flash evaporation, add sodium carbonate according to the ratio for neutralization. The neutralization time is 10 minutes. When the temperature of the reacto...

Embodiment 2

[0033] This embodiment is a production method of an environmentally friendly low temperature resistant flame retardant composite plasticizer, comprising the following steps:

[0034] (1) Preparation of plasticizer matrix:

[0035] (1) Esterification: Pour the measured decanol into the reactor according to the ratio. After the temperature of the reactor is lower than 80°C, add sebacic acid according to the ratio, and then add the catalyst according to the ratio. When the temperature of the material rises to 223°C, start negative reaction. Pressure reaction, when the acid value <0.1mgKOH / g, carry out flash dealcoholization; the weight ratio of sebacic acid and decanol is: sebacic acid: 1 part, decanol: 3 parts; the addition amount of catalyst is decanol 0.6% of the total weight of diacid and decanol;

[0036] (2) Refining: After the flash evaporation, add sodium carbonate according to the ratio for neutralization. The neutralization time is 20 minutes. When the temperature of t...

Embodiment 3

[0044] This embodiment is a production method of an environmentally friendly low temperature resistant flame retardant composite plasticizer, comprising the following steps:

[0045] (1) Preparation of plasticizer matrix:

[0046] ⑴Esterification: Pour the measured decanol into the reactor according to the ratio. After the temperature of the reactor is lower than 80°C, add sebacic acid according to the ratio, and then add the catalyst according to the ratio. When the temperature of the material rises to 225°C, start negative reaction. Pressure reaction, when the acid value <0.1mgKOH / g, carry out flash dealcoholization; the weight ratio of sebacic acid and decyl alcohol is: sebacic acid: 1 part, decyl alcohol: 5 parts; the addition amount of catalyst is decyl alcohol 1% of the total weight of diacid and decanol;

[0047] (2) Refining: After the flash evaporation, add sodium carbonate according to the ratio for neutralization. The neutralization time is 30 minutes. When the tem...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a production method for environmental-friendly low-temperature-resistant antiflaming compound plasticizer. The production method comprises the following steps: (1) preparing a plasticizer matrix: 1) esterification, 2) purification, 3) filter pressing purification, and 4) distillation; (2) preparing a low-temperature-resistant antiflaming system: evenly mixing nanosilicon dioxide, gas phase method silica aerogel, methyl hydrogen silicone oil, hydroxyl polydimethylsiloxane, vinyl trimethoxy silane, ammonium polyphosphate, reactive diluent, compatilizer, coupling reagent, flatting agent and mixed rare earth chloride at a ratio; (3) preparing the environmental-friendly low-temperature-resistant antiflaming compound plasticizer: evenly mixing the plasticizer matrix and the low-temperature-resistant antiflaming system obtained in the steps, wherein the addition of the low-temperature-resistant antiflaming system is 1.7-1.9wt% of the plasticizer matrix. The plasticizer has the advantages of good environmental protection property, high plastification efficiency, low temperature resistance, extremely low volatility and good stability.

Description

technical field [0001] The invention relates to a production method of a plasticizer, in particular to a production method of an environment-friendly low temperature resistant flame retardant composite plasticizer. Background technique [0002] Plasticizer is a kind of polymer material additives. There are many kinds. The most common variety is DEHP (commercial name DOP). DEHP chemical name is bis(2-ethylhexyl) phthalate, which is a colorless , Odorless liquid, widely used in industry. Plasticizer is a polymer material additive widely used in industry. Adding this substance in plastic processing can make it more flexible, easy to process, and can be legally used for industrial purposes. The existing ordinary low-temperature resistant plasticizers are easy to volatilize because of their small molecular weight and low boiling point. After long-term use, the plasticizers will precipitate from the product, which directly affects the low temperature resistance of the product and...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L83/05C08L83/06C08L51/06C08K13/06C08K3/36C08K5/5425C08K3/32C08K3/08
CPCC08L83/04C08K2201/003C08K2201/011C08K2201/014C08L2201/02C08L2201/04C08L2205/03C08L2205/035C08L83/06C08L51/06C08K13/06C08K3/36C08K5/5425C08K2003/323C08K3/08
Inventor 吴胜刚丁磊
Owner JIANGSU SENHE CHEM TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com