Aluminum alloy nickel plating pretreatment method

An aluminum alloy and pretreatment technology, applied in liquid chemical plating, metal material coating process, coating and other directions, can solve the problems of difficult chemical sedimentation of heavy metal zinc ions, and the difficulty of discharging wastewater to meet the standards, and achieve increased quality stability and efficiency. Cost-effective, easy chemical settling, improved adhesion and service life

Active Publication Date: 2020-04-03
HANGZHOU WIN WIN TECH CO LTD
View PDF8 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] In particular, the strong complexing agent contained in the zinc immersion solution will cause difficulties in the chemical precipitation of heavy metal zinc ions in the wastewater, and it is difficult to use neutralization chemical sedimentation to treat the discharged wastewater to meet the standard (Table 3 in GB 21900-2008 The special discharge limit of water pollutants total zinc The requirement is less than 1mg / l), which makes the manufacturer very troubled

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Aluminum alloy nickel plating pretreatment method
  • Aluminum alloy nickel plating pretreatment method
  • Aluminum alloy nickel plating pretreatment method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0034] Below in conjunction with embodiment the present invention is further explained. The following examples are only used to illustrate the present invention, but are not intended to limit the scope of the present invention.

[0035] A kind of aluminum alloy nickel plating pretreatment method, comprises the steps:

[0036] 1) Cleaning: Put the aluminum alloy workpiece into the cleaning agent for cleaning. The cleaning agent is the phosphorus-free degreasing agent ODM ACLEAN 50 produced by Hangzhou Heyun Technology Co., Ltd., the concentration is 20-50g / l, and the operating temperature is 40-70°C , the soaking time is 2-10min; after that, wash it with water.

[0037] The invention uses a non-phosphorus degreasing agent for cleaning, reduces the use of phosphate, and is more environmentally friendly.

[0038] 2) Alkaline micro-etching: Put the cleaned and water-washed aluminum alloy workpiece into the alkaline etching solution for micro-etching. The alkaline etching solutio...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an aluminum alloy nickel plating pretreatment method, which comprises cleaning, alkaline micro-etching and acidic neutralization: an acidic neutralization solution is a mixed solution of sulfuric acid and hydrogen peroxide; first zinc immersion: a zinc immersion solution is a mixed solution composed of zinc oxide, sodium hydroxide, lactic acid or / and malic acid and water; stripping: a stripping solution is a low-concentration HNO3 solution; second zinc immersion: the zinc immersion solution is the same as the zinc dipping solution used in the first time; and zinc reduction: a zinc reduction solution comprises glacial acetic acid, succinic acid, lactic acid and malic acid. According to the method, the pollution of zinc ions to a chemical nickel plating solution or anickel electroplating solution is greatly reduced, the service life of the chemical nickel plating solution or the nickel electroplating solution is prolonged, tank replacement of the chemical nickelplating solution or the nickel electroplating solution is reduced, and the binding force of the plating layer is kept at a high level. According to the method, the dosage of chemicals such as phosphate, zinc oxide and nitric acid can be greatly reduced, the waste liquid generated by the method is easier to treat, and the contained heavy metal zinc ions are easy to chemically settle and are separated from the waste liquid.

Description

technical field [0001] The invention relates to the technical field of aluminum alloy surface treatment, in particular to a pretreatment method before electroless nickel plating or nickel electroplating on aluminum alloys. Background technique [0002] Due to the self-passivation of the aluminum alloy, if the aluminum alloy is directly electroless nickel-plated or electro-nickel-plated, a coating with excellent adhesion cannot be obtained, and a special step of zinc-dipping treatment (zinc replacement) or nickel-immersion treatment is usually required. [0003] In the surface treatment industry, the pretreatment methods of electroless nickel plating or nickel plating on aluminum alloys are widely used as cleaning-alkali etching-neutralization-first zinc dip-nitric acid stripping-second zinc dip-electroless nickel plating or other electroplating. The cleaning agent used in the process usually contains phosphate, borate, sulfate, silicate and other inorganic salts and surfacta...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C25D5/44C23C18/32C23C18/18
CPCC23C18/1844C23C18/32C25D5/44
Inventor 金波愔
Owner HANGZHOU WIN WIN TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products