A kind of high elastic polyester yarn and preparation method thereof

A polyester yarn and high-elasticity technology, which is applied in yarn, melt spinning, rayon manufacturing, etc., can solve the problems of insufficient elastic fabric, tightness and discomfort, poor elasticity of polyester, etc., and achieve increased adhesion and softness Excellent, improved elasticity and wear resistance effect

Active Publication Date: 2021-03-02
浙江正堂实业股份有限公司
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In the above technology, although this kind of high-elastic flame-retardant polyester has overcome the disadvantages of poor air permeability and poor absorption of polyester, the elasticity of polyester is poor due to the addition of phosphate starch and diatom mud as flame retardants, making the obtained The fabric is not elastic enough. If this polyester is used in tight-fitting sportswear, the athlete will feel tight and uncomfortable when wearing it.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of high elastic polyester yarn and preparation method thereof
  • A kind of high elastic polyester yarn and preparation method thereof
  • A kind of high elastic polyester yarn and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0051] A high-elastic polyester yarn, its components and parts by mass are shown in Table 1.

[0052] Wherein, the compatibilizer is formed by mixing maleic anhydride grafted EVA and maleic anhydride grafted HDPE according to a mass ratio of 1:0.8.

[0053] Wherein, the tree ashes are modified tree ashes, and the preparation method of the modified tree ashes is as follows:

[0054] Boil tree ashes with 15-20% hydrogen peroxide for 15 minutes, then wash them with distilled water, dry them in an oven at 110°C, add 5 parts by mass of sodium lignosulfonate, 2 parts of polyisobutylene, and 5 parts of The talcum powder was stirred at a high speed in a water bath at 80°C for 2 hours, dried, crushed and ground into superfine powder, and the modified tree ash could be obtained. The mesh number of the modified tree ash was 600 mesh.

[0055] Among them, the talcum powder used to prepare the modified tree ash is modified talcum powder, and the modified talcum powder is prepared by the f...

Embodiment 2

[0066] The difference with embodiment 1 is:

[0067] A high-elastic polyester yarn, its components and parts by mass are shown in Table 1.

[0068] Wherein, the compatibilizer is formed by mixing maleic anhydride grafted EVA and maleic anhydride grafted HDPE according to a mass ratio of 1.5:0.6.

[0069] Wherein, the tree ashes are modified tree ashes, and the preparation method of the modified tree ashes is as follows:

[0070] Boil tree ashes with 15-20% hydrogen peroxide for 18 minutes, then wash them with distilled water, dry them in an oven at 115°C, add 6.5 parts of sodium lignosulfonate, 2.5 parts of polyisobutylene, 6 parts of The talc powder was stirred in a water bath at 85°C for 2.5 hours at high speed, dried, crushed and ground into superfine powder, and the modified tree ash could be obtained. The mesh number of the modified tree ash was 800 mesh.

[0071] Among them, the talcum powder used to prepare modified tree ash is modified talcum powder, and the modified...

Embodiment 3

[0082] The difference with embodiment 1 is:

[0083] A high-elastic polyester yarn, its components and parts by mass are shown in Table 1.

[0084] Wherein, the compatibilizer is formed by mixing maleic anhydride grafted EVA and maleic anhydride grafted HDPE according to a mass ratio of 2:1.2.

[0085] Wherein, the tree ashes are modified tree ashes, and the preparation method of the modified tree ashes is as follows:

[0086] Boil tree ashes with 20% hydrogen peroxide for 20 minutes, then wash them with distilled water, dry them in an oven at 120°C, add 8 parts by mass of sodium lignosulfonate, 3 parts of polyisobutylene, and 7 parts of talcum powder , stirred at high speed in a water bath at 90°C for 3 hours, dried, crushed and ground into superfine powder to obtain the modified tree ash, and the mesh number of the modified tree ash is 1000 mesh.

[0087] Among them, the talcum powder used to prepare the modified tree ash is modified talcum powder, and the modified talcum ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the field of polyester yarn preparation, in particular to a high-elasticity polyester yarn and a preparation method thereof. The high-elasticity polyester yarn is prepared from, by mass, 60-80 parts of polyester masterbatch, 25-30 parts of polylactic acid fiber powder, 5-10 parts of thermoplastic polyurethane elastomer, 2-5 parts of a compatilizer, 12-18 parts of tree ashand 2-3 parts of an antioxidant. The preparation method includes steps: pretreating the materials according to the parts by mass; mixing the materials to obtain a mixture A; melting and extruding themixture A to obtain a melt B; cooling the melt B to obtain polyester filaments C; subjecting the polyester filaments C to stretching and setting to obtain polyester filaments E; coating the polyesterfilaments E with oil liquid, and subjecting the polyester filaments E to stretching and setting; finally twisting the polyester filaments E to obtain the yarn, and rolling up. The high-elasticity polyester yarn and the preparation method thereof have the advantage that the polyester yarn prepared according to the method is high in elasticity and can be applied to preparation of tight-fitting sportswear.

Description

technical field [0001] The invention relates to the technical field of polyester yarn preparation, more specifically, it relates to a high-elastic polyester yarn and a preparation method thereof. Background technique [0002] Polyester yarn is a yarn spun from polyester. Polyester is one of the important varieties of synthetic fibers. It uses purified terephthalic acid or terephthalate and ethylene glycol as raw materials through esterification or transesterification. Polyethylene terephthalate (PET) obtained by polycondensation reaction, fiber obtained by spinning and post-processing. [0003] In the prior art, the Chinese invention patent application document with the application number 201610568722.6 discloses a high-elastic flame-retardant polyester, which is made according to the following proportions by weight: 5-15 parts of polyethylene glycol, 10-30 parts of purified p-phenylene Diformic acid, 10-25 parts of plant fiber, 5-15 parts of phosphate ester starch, 5-15 pa...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): D02G3/02D02G3/32D02G3/44D01F8/14D01F8/16D01F1/10D06M13/224D06M16/00D01D5/08D01D10/02D02J1/22D06B1/14
CPCD01D5/08D01D10/02D01F1/10D01F8/14D01F8/16D02G3/02D02G3/328D02G3/441D02G3/442D02G3/449D02J1/224D02J1/227D06B1/14D06M13/224D06M16/00D06M2101/32D06M2101/38D06M2200/40D10B2331/04D10B2401/061D10B2401/062D10B2401/13D10B2401/16
Inventor 朱靓韬朱忠华戴掌华倪金虎童赛平
Owner 浙江正堂实业股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka