A heat-resistant and cold-resistant outdoor pressure-sensitive adhesive and preparation method thereof

A pressure-sensitive adhesive, outdoor technology, applied in the field of pressure-sensitive adhesives, can solve the problems of shedding, insufficient viscosity, insufficient cold and heat resistance, etc., to reduce interaction force, improve heat and cold resistance, improve adhesion and coating. The effect of cloth craftsmanship

Active Publication Date: 2021-02-02
新田县德润新材料产业园有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In some outdoor environments, the environment is relatively harsh, and the performance requirements for pressure-sensitive adhesives are relatively high. Some traditional pressure-sensitive adhesives have insufficient cold and heat resistance, and are prone to fall off due to insufficient viscosity during use.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A heat-resistant and cold-resistant outdoor pressure-sensitive adhesive and preparation method thereof
  • A heat-resistant and cold-resistant outdoor pressure-sensitive adhesive and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] A heat-resistant and cold-resistant pressure-sensitive adhesive for outdoor use, comprising the following components and parts by weight: natural rubber, tackifying resin, plasticizer, vulcanizing agent, anti-aging agent, softener, mixed filler and titanium dioxide;

[0027] And specifically in the present embodiment, it is specifically: 125 parts of natural rubber, 125 parts of tackifying resin, 40 parts of plasticizer, 7 parts of vulcanizing agent, 7 parts of antioxidant, 7 parts of softening agent, 15 parts of mixed filler and titanium dioxide 3 copies;

[0028] Further, in the above-mentioned ingredients, the tackifying resin is specifically a mixture of rosin resin, terpene resin, maleic acid resin and water-white resin, and the rosin resin, terpene resin, maleic acid resin and water-white resin The mixing ratio is 1:3:1:1;

[0029] The viscosity of the tackifying resin is 280000mPa·s, and the softener is specifically a mixture of lanolin, lecithin, dibutyl phthal...

Embodiment 2

[0037] A heat-resistant and cold-resistant pressure-sensitive adhesive for outdoor use, comprising the following components and parts by weight: natural rubber, tackifying resin, plasticizer, vulcanizing agent, anti-aging agent, softener, mixed filler and titanium dioxide;

[0038] And specifically in the present embodiment, it is specifically: 125 parts of natural rubber, 125 parts of tackifying resin, 40 parts of plasticizer, 7 parts of vulcanizing agent, 7 parts of antioxidant, 7 parts of softening agent, 15 parts of mixed filler and titanium dioxide 3 copies;

[0039] Further, in the above-mentioned ingredients, the tackifying resin is specifically a mixture of rosin resin, terpene resin, maleic acid resin and water-white resin, and the rosin resin, terpene resin, maleic acid resin and water-white resin The mixing ratio is 1:3:1:1;

[0040] The viscosity of the tackifying resin is 250000mPa·s, and the softener is specifically a mixture of lanolin, lecithin, dibutyl phthalat...

Embodiment 3

[0048] A heat-resistant and cold-resistant pressure-sensitive adhesive for outdoor use, comprising the following components and parts by weight: natural rubber, tackifying resin, plasticizer, vulcanizing agent, anti-aging agent, softener, mixed filler and titanium dioxide;

[0049] And specifically in the present embodiment, it is specifically: 125 parts of natural rubber, 125 parts of tackifying resin, 40 parts of plasticizer, 7 parts of vulcanizing agent, 7 parts of antioxidant, 7 parts of softening agent, 15 parts of mixed filler and titanium dioxide 3 copies;

[0050] Further, in the above-mentioned ingredients, the tackifying resin is specifically a mixture of rosin resin, terpene resin, maleic acid resin and water-white resin, and the rosin resin, terpene resin, maleic acid resin and water-white resin The mixing ratio is 1:3:1:1;

[0051] The viscosity of the tackifying resin is 300000mPa·s, and the softener is specifically a mixture of lanolin, lecithin, dibutyl phthal...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
viscosityaaaaaaaaaa
viscosityaaaaaaaaaa
viscosityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a heat-resistant and cold-resistant outdoor pressure-sensitive adhesive and a preparation method thereof, specifically relates to the technical field of pressure-sensitive adhesives, comprising the following components and parts by weight: 100-150 parts of natural rubber, 100-150 parts of tackifying resin part, 30-50 parts of plasticizer, 5-10 parts of vulcanizing agent, 5-10 parts of anti-aging agent, 10-20 parts of softener, 10-20 parts of mixed filler and 1-5 parts of titanium dioxide; the tackifying resin Specifically, it is a mixture of rosin resin, terpene resin, maleic acid resin and water-whitening resin, and the softening agent is specifically a mixture of lanolin, lecithin, dibutyl phthalate and glycerin. The invention can reduce the bulk viscosity of the pressure-sensitive adhesive, improve its adhesion to the base material and the coating process, improve the initial viscosity at low temperature, and improve the cold and heat resistance of the pressure-sensitive adhesive. It should not fall off when used in the environment.

Description

technical field [0001] The invention relates to the technical field of pressure-sensitive adhesives, more specifically, the invention relates to a heat-resistant and cold-resistant outdoor pressure-sensitive adhesive and a preparation method thereof. Background technique [0002] Adhesive bonding (bonding, bonding, cementation, gluing) refers to the technology of connecting the surfaces of homogeneous or heterogeneous objects with adhesives. It has the characteristics of continuous stress distribution, light weight, or sealing, and low temperature in most processes. Gluing is especially suitable for the connection of different materials, different thicknesses, ultra-thin specifications and complex components. Glue is the fastest growing in modern times, with a wide range of applications, and has a major impact on the progress of high-tech science and technology and the improvement of people's daily life. Therefore, it is very important to research, develop and produce vario...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09J107/00C09J145/00C09J11/04C09J11/06C09J11/08
CPCC08K2003/3045C08L2201/08C08L2205/025C08L2205/035C09J11/04C09J11/06C09J11/08C09J107/00C08L45/00C08L93/04C08L91/00C08K13/02C08K5/12C08K5/053C08K3/34C08K3/30C08K5/39
Inventor 廖平湘
Owner 新田县德润新材料产业园有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com