Solvent-based reticulated pressure-sensitive adhesive for polyethylene protective film and preparation method thereof

A polyethylene protective film, solvent-based technology, applied in the direction of adhesive types, ester copolymer adhesives, film/sheet adhesives, etc. , easy to form bubbles and other problems, to achieve the effect of good peel strength and cohesion, less glue, and fast curing speed

Active Publication Date: 2012-06-20
无锡达美新材料有限公司
View PDF1 Cites 45 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

PE protective film is generally made of plain weave film, which is characterized by high transparency and good adhesion to the surface of the article, but the coating amount of the plain weave film is large, and it is easy to form bubbles when it is attached to the surface of the article. Wrinkles on the surface affect the appearance and use of the item

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Solvent-based reticulated pressure-sensitive adhesive for polyethylene protective film and preparation method thereof
  • Solvent-based reticulated pressure-sensitive adhesive for polyethylene protective film and preparation method thereof
  • Solvent-based reticulated pressure-sensitive adhesive for polyethylene protective film and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] Mix 86.4g isooctyl acrylate, 27g ethyl acrylate, 75.6g butyl acrylate, 54g methyl methacrylate, 10.8g hydroxyethyl acrylate, 1.4g acrylic acid and 0.95g benzoyl peroxide; 240g of ethyl acetate and 60g of toluene were added to the reactor, and 67.5g of the above mixture was added when the temperature rose to 80°C; after 45 minutes of polymerization, the remaining amount of the above mixture was slowly added dropwise under reflux for about 3 hours Dropwise; After the dropwise addition, continue reflux reaction for 60 minutes, add 0.14g benzoyl peroxide (dissolved in 15g ethyl acetate); continue reflux reaction for 60 minutes, add 0.14g benzoyl peroxide ( dissolved in 15 g of ethyl acetate); the reaction was continued for 2 hours, the reaction was stopped, and the acrylate pressure-sensitive adhesive was obtained after cooling.

[0033] Stir 50g of acrylate pressure-sensitive adhesive, 60g of ethyl acetate, 0.5g of toluene diisocyanate and 0.08g of dibutyltin dilaurate at ...

Embodiment 2

[0046]73.7g isooctyl acrylate, 31.6g ethyl acrylate, 67.5g butyl acrylate, 72.9g methyl acrylate, 6.2g hydroxypropyl acrylate, 0.81g glycidyl methacrylate and 0.81g azobisisobutyronitrile Mix evenly; add 200g of ethyl acetate and 100g of toluene into a nitrogen-protected reactor, and add 54g of the above mixture when the temperature rises to 82°C; after 45 minutes of polymerization, slowly add the remaining amount of the above mixture dropwise under reflux , dripped in about 3.5 hours; after the dropwise addition, continue to reflux for 60 minutes, add 0.14g of azobisisobutyronitrile (dissolved in 15g of ethyl acetate); continue to reflux for 60 minutes, add 0.14g Azobisisobutyronitrile (dissolved in 15 g of ethyl acetate); continue to react for 2 hours, stop the reaction, and obtain an acrylate pressure-sensitive adhesive after cooling.

[0047] Stir 45g of acrylate pressure-sensitive adhesive, 30g of ethyl acetate, 30g of toluene, 0.5g of methyl etherified high methylene mel...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a solvent-based reticulated pressure-sensitive adhesive for a polyethylene protective film and a preparation method thereof. The solvent-based reticulated pressure-sensitive adhesive comprises the following components in parts by weight: 42-45 parts of acrylate pressure-sensitive adhesive, 0.3-0.5 part of curing agent, 0.1-0.2 part of catalyst and 54-57% of solvent. The solvent-based reticulated pressure-sensitive adhesive disclosed by the invention has good adhesion to a polyethylene protective film and can realize good balance among Initial adhesion, peel strength and cohesion.

Description

technical field [0001] The invention relates to a solvent-type reticulated pressure-sensitive adhesive and a preparation method thereof, more specifically, the invention relates to a solvent-type reticulated pressure-sensitive adhesive for polyethylene protective film and a preparation method thereof. Background technique [0002] The protective film is a surface protection material used to protect the surface of an article. It is pasted on the surface of metal products, coated metal products, plastic products, automotive products, electronic products, signage products, profile products, and The surface of other products, so that it can protect the surface of the article during manufacturing, transportation, processing, storage and use, prevent the article from being polluted, scratched and slow down the oxidation of the article surface, so that the pasted article can be protected during transportation, processing, storage and use. Avoid contamination, corrosion, scratches, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J133/08C09J133/04C09J7/02C08F220/18C08F220/14C08F220/28C08F220/32
Inventor 许钟武柯跃虎张刚
Owner 无锡达美新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com