High-quality graphene/two-dimensional metal carbide crystal vertical heterostructure material and preparation method thereof

A metal carbide, heterostructure technology, applied in the direction of graphene, carbide, carbon compounds, etc., can solve the problems of weak interface interaction, interface pollution, poor quality of graphene, etc., to achieve strong interface interaction, clean interface , easy to control effect

Active Publication Date: 2018-12-18
INST OF METAL RESEARCH - CHINESE ACAD OF SCI
View PDF4 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to provide a high-quality graphene / two-dimensional metal carbide crystal vertical heterostructure material with clean interface, consistent crystal orientation and strong coupling effect and its preparation method, to solve the vertical heterostructure obtained in the current research. Poor quality of graphene in the structure, interface contamination, weak interface interaction, etc., lay the foundation for studying the intrinsic properties of graphene / two-dimensional metal carbide crystal vertical heterostructure and exploring its application

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-quality graphene/two-dimensional metal carbide crystal vertical heterostructure material and preparation method thereof
  • High-quality graphene/two-dimensional metal carbide crystal vertical heterostructure material and preparation method thereof
  • High-quality graphene/two-dimensional metal carbide crystal vertical heterostructure material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0043] In a specific embodiment, the preparation method of the high-quality graphene / two-dimensional metal carbide crystal vertical heterostructure material of the present invention adopts a double metal laminate composed of copper foil (upper layer) / metal foil (bottom layer) as the growth substrate , at high temperature, graphene is grown by catalytic cracking of carbon source by chemical vapor deposition technology, and then two-dimensional transition metal carbide crystals are grown between liquid copper and graphene, and then the copper substrate is etched away to obtain graphene / two-dimensional metal carbide The specific steps are as follows:

[0044] (1) CVD growth of graphene / two-dimensional metal carbide crystal vertical heterostructure materials: the bimetallic laminate composed of the upper layer copper foil / bottom metal foil is used as the growth substrate, and it is the first in the high temperature chemical vapor deposition process. Graphene grows on the surface o...

Embodiment 1

[0054] In this embodiment, the high-quality graphene / two-dimensional metal carbide crystal vertical heterostructure material and its preparation method are as follows:

[0055] First, if figure 1 As shown, the present invention adopts a horizontal reaction furnace to grow graphene / two-dimensional metal carbide crystal vertical heterostructure, and the two ends of the horizontal reaction furnace are respectively provided with a gas inlet 1 and a gas outlet 3, and the copper foil / molybdenum sheet is placed in a horizontal In the high-temperature zone of the type reaction furnace, the copper foil / molybdenum sheet (copper foil 20 mm × 20 mm × 25 microns, the purity is 99.999wt%, the molybdenum sheet 20 mm × 20 mm × 100 microns, the purity is 99.95 wt%) is placed on a horizontal Type reaction furnace (diameter of furnace tube 22 mm, length of reaction zone 20 mm) in the central area; heated to 1070 ° C in hydrogen and argon atmosphere (hydrogen flow rate is 200 ml / min, argon flow r...

Embodiment 2

[0059] In this embodiment, the high-quality graphene / two-dimensional metal carbide crystal vertical heterostructure material and its preparation method are as follows:

[0060] First, if figure 1 As shown, the present invention adopts a horizontal reaction furnace to grow graphene / two-dimensional metal carbide crystal vertical heterostructure, and the two ends of the horizontal reaction furnace are respectively provided with a gas inlet 1 and a gas outlet 3, and the copper foil / molybdenum sheet is placed in a horizontal In the high temperature zone of the type reaction furnace, the copper foil / molybdenum sheet (copper foil 20 mm × 20 mm × 12.5 microns, purity 99.5wt%, molybdenum sheet 20 mm × 20 mm × 100 microns, purity 99.95 wt%) is placed on a horizontal Type reaction furnace (diameter of furnace tube 22 mm, length of reaction zone 20 mm) in the central area; heated to 1070 ° C in hydrogen and argon atmosphere (hydrogen flow rate is 200 ml / min, argon flow rate is 500 ml / min ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
sizeaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to the field of new materials, particularly to a high-quality graphene / two-dimensional metal carbide crystal vertical heterostructure material and a preparation method thereof. According to the preparation method, a bimetal laminate formed by a copper foil / metal foil sheet is used as a growth substrate, graphene grows at a high temperature through catalytic cracking of a carbon source by using a CVD technology, and a two-dimensional transition metal carbide crystal grows under the graphene by increasing the temperature, or graphene and a two-dimensional transition metal carbide directly grow at a temperature of higher than the melting point of copper so as to prepare a graphene / two-dimensional metal carbide vertical heterostructure; and subsequently the copper substrate is etched off to obtain the graphene / two-dimensional metal carbide vertical heterostructure. According to the present invention, the foundation is established for the research and applications of high-quality graphene / two-dimensional metal carbide vertical heterostructure in the fields of catalysis, laser detection, transparent electric-conduction films, thermal management, two-dimensional superconductivity, high transparent Josephson junctions.

Description

Technical field: [0001] The invention relates to the field of graphene / two-dimensional metal carbide crystal vertical heterostructure new material and its chemical vapor deposition (CVD) preparation field, specifically a high-quality graphene / metal carbide with clean interface, consistent crystal orientation and strong coupling effect The two-dimensional metal carbide crystal vertical heterostructure material and its preparation method are suitable for the preparation of large-area, high-quality graphene / two-dimensional metal carbide crystal vertical heterostructure materials. Background technique: [0002] Graphene and other two-dimensional crystals not only exhibit many new physical properties, super properties and promising applications different from their corresponding bulk materials, but also create unusual properties, new physical properties and for Two-dimensional vertical heterostructures with unprecedented possibilities in the field of technological applications pr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C01B32/186C01B32/949C01B32/194B82Y30/00B82Y40/00
CPCB82Y30/00B82Y40/00C01P2002/01C01P2002/72C01P2002/80C01P2002/82C01P2004/03C01P2004/64C01P2006/40
Inventor 任文才徐川陈龙成会明
Owner INST OF METAL RESEARCH - CHINESE ACAD OF SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com