Anticorrosion coating composition, anticorrosion coating film, substrate with anticorrosion coating film, and method of manufacturing same

A technology for anti-corrosion coatings and compositions, applied in the direction of anti-corrosion coatings, epoxy resin coatings, chemical instruments and methods, etc., which can solve the problems of poor weather resistance, easy decline in the suitability of top coatings, primer coatings and top coatings Insufficient adhesion between film layers and other problems, to achieve the effect of excellent adhesion, excellent interlayer adhesion, and not easy to reduce the suitability of surface coating

Active Publication Date: 2018-10-23
CHUGOKU MARINE PAINTS
View PDF14 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In general, the weather resistance of the primer coating film formed from the epoxy resin coating composition is poor, so the interlayer adhesion with the top coating film and the physical properties exhibited by the laminate with the top coating film, etc. Topcoat coating suitability is easy to decline
In particular, when the time from primer coating to top coat coating of the epoxy resin coating composition is prolonged, there is a problem that the interlayer adhesion between the formed primer coating film and the top coating film is insufficient.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Anticorrosion coating composition, anticorrosion coating film, substrate with anticorrosion coating film, and method of manufacturing same
  • Anticorrosion coating composition, anticorrosion coating film, substrate with anticorrosion coating film, and method of manufacturing same
  • Anticorrosion coating composition, anticorrosion coating film, substrate with anticorrosion coating film, and method of manufacturing same

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0145] As shown in the following table 1-1, add 33 parts by weight of epoxy resin "E834-85X(T)", 1 part by weight of polyvinyl alkyl ether 1 "Lutonal A-25", and talc "F-2talc" to the container "20 parts by weight, potassium feldspar "potassium feldspar KM 325" 21.48 parts by weight, barium sulfate "Barico300W" 5 parts by weight, titanium dioxide "titanium white R-930" 4 parts by weight, carbon black "MA-100" 0.02 parts by weight Parts, 0.3 parts by weight of acrylate monomer "M-CURE 400", 0.6 parts by weight of silane coupling agent "KBM-403", 0.2 parts by weight of defoamer "BYK-1790", and anti-sagging agent "ASA T-250F "0.9 parts by weight, 10 parts by weight of xylene, 1.5 parts by weight of n-butanol, and 2 parts by weight of propylene glycol monomethyl ether acetate, glass beads are added thereto, and these ingredients are mixed with a paint mixer. Next, the glass beads were removed, and the mixture was dispersed uniformly at room temperature (23°C) using a high-speed disp...

Embodiment 2～18 and comparative example 1～3

[0149] Except that the main agent component and curing agent component of Example 1 contained the ingredients and the mixing amount and the mixing ratio of the main agent component and the curing agent component as shown in the following Tables 1-1, 1-2, the implementation In Example 1, the same operation was performed to prepare each anti-corrosion coating composition.

[0150] [Table 1-1]

[0151]

[0152] [Table 1-2]

[0153]

[0154]

[0155] ·Epoxy resin

[0156] "E834-85X(T)" (manufactured by Otake Akashin Chemical Co., Ltd., bisphenol A epoxy resin (semi-solid at room temperature), epoxy equivalent 290-310g / eq, non-volatile content 85%)

[0157] ·Reactive diluent

[0158] "Cardo Lite Lite 2513HP" (manufactured by Cardolite, alkylphenol glycidyl ether, epoxy equivalent 375~450g / eq)

[0159] ·Polyvinyl alkyl ether 1

[0160] "Lutonal A-25" (manufactured by BASF, polyvinyl ethyl ether)

[0161] ·Polyvinyl alkyl ether 2

[0162] "Lutonal M-40" (manufactured by BASF, polyvinyl methyl ethe...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
epoxy equivalentaaaaaaaaaa
epoxy equivalentaaaaaaaaaa
epoxy equivalentaaaaaaaaaa
Login to View More

Abstract

The present invention relates to an anticorrosion coating composition, an anticorrosion coating film, a substrate with an anticorrosion coating film, and a method of manufacturing a substrate with ananticorrosion coating film. The anticorrosion coating composition contains (a) an epoxy resin, (b) a polyvinyl alkyl ether (co)polymer, and (c) an amine-based curing agent.

Description

Technical field [0001] The invention relates to an anti-corrosion coating composition, an anti-corrosion coating film, a substrate with an anti-corrosion coating film, and a method for manufacturing a substrate with an anti-corrosion coating film. Background technique [0002] In the prior art, (large) steel structures such as ships, bridges, storage tanks, complete sets of equipment, offshore buoys, and offshore oil pipelines are coated with a coating film obtained from an epoxy resin-based anticorrosive coating composition in order to prevent corrosion . According to the use and purpose of the above-mentioned steel structure, in order to impart aesthetics, weather resistance, corrosion resistance, and antifouling properties, various resin-based top coating compositions are coated on such a coating film to form a top coating Coating film. For example, the bottom of a ship is coated with an antifouling coating composition that prevents the adhesion of aquatic organisms such as ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D163/00B05D7/14B32B15/092B32B27/38C09D5/08C09D7/61C09D7/63C09D129/10C09D157/00
CPCB05D7/14B32B15/092B32B27/38C09D5/08C09D129/10C09D157/00C09D163/00C09D7/40C08G59/50C08L29/10C08L35/08C09D7/20B05D2202/10B05D2504/00C08G59/5033C08K5/1515C08L2203/16
Inventor 儿玉真尚
Owner CHUGOKU MARINE PAINTS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com