High-elasticity external wall coating with enhanced anti-corrosive performance of composite epoxy resin emulsion

A technology of epoxy resin emulsion and exterior wall coating, which is applied in the field of coatings to achieve the effect of smooth and beautiful coating film, excellent weather resistance and high elongation

Inactive Publication Date: 2017-05-10
岳承华
View PDF2 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Conventional coatings cannot not only have excellent weather resistance, water resistance and stain resistance, but also have good elasticity, flexibility and crack resistance, so the development of a new type of high-performance elastic waterproof coating has become a research topic for exterior walls. An important subject of the thermal insulation system project

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0013] A high-elastic exterior wall coating with enhanced anticorrosion performance of composite epoxy resin emulsion, made of the following raw materials in parts by weight (kg): methyl methacrylate 20, butyl acrylate 29, hexafluorobutyl acrylate 8.5, vinyl Triethoxysilane 4, ammonium persulfate 0.1, OP-10 2, deionized water amount, ammonia water amount, dodecyl alcohol ester 1.5, superfine kaolin 8, polyether polyol 3, epoxy resin 2, epoxy Resin emulsion 7, boron trifluoride ether 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
elongation at breakaaaaaaaaaa
Login to View More

Abstract

The invention discloses a high-elasticity external wall coating with enhanced anti-corrosive performance of composite epoxy resin emulsion. The high-elasticity external wall coating is prepared from, by weight, 20-22 parts of methyl methacrylate, 29-31 parts of butyl acrylate, 8.5-9.5 parts of hexafluorobutyl acrylate, 4-5 parts of vinyl triethoxy silane, 0.1-0.12 part of ammonium persulfate, 2-3 parts of OP-1, proper amount of deionized water, proper amount of amino water, 1.5-2 parts of n-dodecanol ester, 8-10 parts of superfine kaoline, 3-4 parts of polyether polyol, 2-3 parts of epoxy resin, 7-8 parts of epoxy resin emulsion, and 1-2 parts of boron trifluoride diethyl etherate. The high-elasticity coating has water-based formula and is free from toxic and pollution, high in ductility, excellent in weather fastness, convenient to construct; the coating is especially suitable for the waterproof use of the external wall of the building engineering; the coating film is smooth and beautiful.

Description

technical field [0001] The invention relates to the technical field of coatings, in particular to a high-elastic exterior wall coating with enhanced anticorrosion performance of a composite epoxy resin emulsion. Background technique [0002] At present, an important development direction of building exterior wall coatings is energy-saving and thermal insulation. The performance of the emulsion used for the facing layer has a direct impact on the water resistance, stain resistance, durability and temperature resistance of the external wall thermal insulation system, and the wall Body cracks will cause rainwater and carbon dioxide gas intrusion, cause steel bar corrosion, and accelerate wall carbonization speed. Building wall cracks have become one of the common problems that affect the quality of construction projects. Due to the good extensibility of the coating, elastic architectural coatings can resist and cover the cracks in the base layer to a certain extent, and are fav...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/08C09D163/00C09D187/00C09D5/08C09D7/12C08F220/18C08F220/14C08F220/22C08F230/08
CPCC08F220/18C08F220/1804C08L2205/025C08L2205/035C09D5/08C09D7/61C09D7/63C09D143/04C08L63/00C08L87/00C08K5/103C08K3/346C08K5/55C08F220/14C08F220/22C08F230/08
Inventor 岳承华
Owner 岳承华
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products