High temperature resistant and corrosion resistant bearing material and preparation method thereof

A bearing material, corrosion-resistant technology, applied in the field of bearings, can solve the problems of poor heat resistance, expansion deformation, short life, etc., to achieve the effect of high bearing capacity, prolong life, and improve product hardness

Inactive Publication Date: 2017-04-19
ANHUI RZN BEARING
View PDF7 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The steel used in traditional bearing materials has poor heat resistance. When the bearing is in a high tempe...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] A high temperature and corrosion resistant bearing material, made of the following raw materials in parts by weight: 5 parts of titanium carbide, 5 parts of chromium carbide, 4 parts of aluminum oxide, 3 parts of modified montmorillonite powder, 5 parts of actinolite powder, sulfuric acid 8 parts of zinc, 1 part of microcrystalline wax, 4 parts of methyl cellulose, 6 parts of graphite, 8 parts of oleic acid, 2 parts of sodium tripolyphosphate, 60 parts of aluminum, 10 parts of zinc, 3 parts of nickel, 6 parts of iron powder, 1 part of ditungsten boride, 1.2 parts of molybdenum dioxide.

[0019] The preparation method of the modified montmorillonite powder is as follows: calcining the montmorillonite at 800°C for 6 hours, grinding it into powder, soaking it in 10% hydrogen peroxide for 3 hours, washing it with deionized water, drying it, and adding Add 1% methylcellulose by weight, 3% ethyl cyanoacrylate, and 1% crosslinking agent TAC, stir at a high speed of 4500 rpm fo...

Embodiment 2

[0029] A high temperature and corrosion resistant bearing material, made of the following raw materials in parts by weight: 6 parts of titanium carbide, 4 parts of chromium carbide, 5 parts of aluminum oxide, 4 parts of modified montmorillonite powder, 4 parts of actinolite powder, sulfuric acid 9 parts of zinc, 2 parts of microcrystalline wax, 3 parts of methyl cellulose, 6 parts of graphite, 9 parts of oleic acid, 3 parts of sodium tripolyphosphate, 65 parts of aluminum, 11 parts of zinc, 4 parts of nickel, 5 parts of iron powder, 2 parts of ditungsten boride, 1.3 parts of molybdenum dioxide.

[0030] The preparation method of the modified montmorillonite powder is as follows: calcining the montmorillonite at 850°C for 6 hours, grinding it into powder, soaking it in 12% hydrogen peroxide for 3 hours, washing it with deionized water, drying it, and adding Add 2% methyl cellulose, 2% ethyl cyanoacrylate, and 2% crosslinking agent TAC, stir at a high speed of 4600 rpm for 35 mi...

Embodiment 3

[0040] A high temperature and corrosion resistant bearing material, made of the following raw materials in parts by weight: 8 parts of titanium carbide, 5 parts of chromium carbide, 6 parts of aluminum oxide, 5 parts of modified montmorillonite powder, 3 parts of actinolite powder, sulfuric acid 10 parts of zinc, 3 parts of microcrystalline wax, 2 parts of methyl cellulose, 7 parts of graphite, 8 parts of oleic acid, 3 parts of sodium tripolyphosphate, 70 parts of aluminum, 12 parts of zinc, 5 parts of nickel, 6 parts of iron powder, 3 parts of ditungsten boride, 1.5 parts of molybdenum dioxide.

[0041]The preparation method of the modified montmorillonite powder is as follows: calcining the montmorillonite at 900°C for 5 hours, grinding it into powder, soaking it in 15% hydrogen peroxide for 2 hours, washing it with deionized water, drying it, and adding Add 2% methylcellulose by weight, 3% ethyl cyanoacrylate, and 2% crosslinking agent TAC, stir at a high speed of 4800 rpm ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Tensile strengthaaaaaaaaaa
Tensile strengthaaaaaaaaaa
Tensile strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a high temperature resistant and corrosion resistant bearing material and a preparation method thereof. The high temperature resistant and corrosion resistant bearing material is prepared from, by weight, 5-8 parts of titanium carbide, 3-5 parts of chromium carbide, 4-6 parts of aluminium sesquioxide, 3-5 parts of modified montmorillonite powder, 3-5 parts of tremolite, 8-10 parts of zinc sulfate, 1-3 parts of microcrystalline wax, 2-4 parts of methylcellulose, 6-7 parts of graphene, 8-10 parts of oleic acid, 2-3 parts of sodium triphosphate, 60-70 parts of aluminum, 10-12 parts of zinc, 3-5 parts of nickel, 4-6 parts of iron powder, 1-3 parts of tungsten boride and 1.2-1.5 parts of molybdenum dioxide. The high temperature resistant and corrosion resistant bearing material has the beneficial effects of being resistant to high temperature, high in corrosion resistance, not prone to deformation and the like, is long in service life and applicable to the high temperature corrosion environment and can be used for a long time under the condition of the temperature being 300 DEG C or above.

Description

technical field [0001] The invention relates to the technical field of bearings, in particular to a high-temperature-resistant and corrosion-resistant bearing material and a preparation method thereof. Background technique [0002] Bearing is a fixed part in machinery. When other parts move relative to each other on the shaft, it is used to maintain the center position of the shaft and control the movement. It is widely used in aviation, aerospace, national defense, large mechanical equipment, etc. field. Bearing life is a key indicator for judging the quality of bearings, and precision and materials are key indicators that affect bearing life. With the development of modern equipment manufacturing, bearings are gradually shifting from precision research to material research. Therefore, today's high-end bearing research is basically Research on bearing materials. The steel used in traditional bearing materials has poor heat resistance. When the bearing is in a high tempera...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B22F1/00B22F5/00
CPCB22F5/00B22F2998/10B22F2999/00B22F1/10B22F3/1007B22F2201/20B22F2003/247B22F3/02
Inventor 华黎明王凯贤陈群
Owner ANHUI RZN BEARING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap