Multifunctional protection coating of teaching aid

A protective coating and multi-functional technology, applied in the field of teaching appliances, to achieve the effect of improving product performance and superior flame retardancy

Inactive Publication Date: 2016-11-16
XIAOGAN QISIMIAOXIANG CULTURAL MEDIA
View PDF0 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

It is necessary to protect these teaching instruments with suitable coatings in order to improve their use effect. The coating of general teaching instruments cannot achieve more functions, so it is necessary to improve them.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Multifunctional protection coating of teaching aid

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] The multifunctional protective coating for teaching utensils in this embodiment consists of the following components in parts by mass: 22 parts of chlorohydrin rubber, 20 parts of chlorosulfonated polyethylene resin, 20 parts of bisphenol A epoxy resin, 20 parts of hexabromo 18 parts of cyclododecane, 20 parts of triethylene glycol diisocaprylate, 20 parts of zinc borate hydrate, 18 parts of sodium antimonate, 20 parts of methyl p-hydroxybenzoate, 20 parts of oxazolidinone, tetrasulfide 18 parts of methyl thiuram, 18 parts of dibromomethane, 18 parts of fluoroquinolone, 20 parts of nano-aluminum powder, 18 parts of nano-silicon carbide, 16 parts of nano-alumina powder, 20 parts of albite powder, 18 parts of zirconium boride powder , 16 parts of bentonite, 18 parts of sodium metasilicate, 16 parts of polyglycerol ricinoleate, 16 parts of polyether silicone oil, 18 parts of polyvinyl acetate emulsion, 18 parts of sunflower oil, 18 parts of polyethylene glycol stearate 18 ...

Embodiment 2

[0022] The multifunctional protective coating for teaching utensils in this embodiment consists of the following components in parts by mass: 24 parts of chlorohydrin rubber, 22 parts of chlorosulfonated polyethylene resin, 22 parts of bisphenol A type epoxy resin, 22 parts of hexabromo 20 parts of cyclododecane, 22 parts of triethylene glycol diisocaprylate, 22 parts of zinc borate hydrate, 20 parts of sodium antimonate, 22 parts of methyl p-hydroxybenzoate, 22 parts of oxazolidinone, tetrasulfide 20 parts of methyl thiuram, 20 parts of dibromomethane, 20 parts of fluoroquinolone, 22 parts of nano-aluminum powder, 20 parts of nano-silicon carbide, 18 parts of nano-alumina powder, 22 parts of albite powder, 20 parts of zirconium boride powder , 18 parts of bentonite, 20 parts of sodium metasilicate, 18 parts of polyglycerol ricinoleate, 18 parts of polyether silicone oil, 20 parts of polyvinyl acetate emulsion, 20 parts of sunflower oil, 20 parts of polyethylene glycol stearate...

Embodiment 3

[0028] The multifunctional protective coating for teaching utensils in this embodiment is composed of the following components in parts by mass: 26 parts of chlorohydrin rubber, 24 parts of chlorosulfonated polyethylene resin, 24 parts of bisphenol A type epoxy resin, 24 parts of hexabromo 22 parts of cyclododecane, 24 parts of triethylene glycol diisocaprylate, 24 parts of zinc borate hydrate, 22 parts of sodium antimonate, 24 parts of methyl p-hydroxybenzoate, 24 parts of oxazolidinone, tetrasulfide 22 parts of methyl thiuram, 22 parts of dibromomethane, 22 parts of fluoroquinolone, 24 parts of nano-aluminum powder, 22 parts of nano-silicon carbide, 20 parts of nano-alumina powder, 24 parts of albite powder, 22 parts of zirconium boride powder , 20 parts of bentonite, 22 parts of sodium metasilicate, 20 parts of polyglycerol ricinoleate, 20 parts of polyether silicone oil, 22 parts of polyvinyl acetate emulsion, 22 parts of sunflower oil, 22 parts of polyethylene glycol stear...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a multifunctional protective coating for teaching equipment, which is composed of the following components: chlorohydrin rubber, chlorosulfonated polyethylene resin, bisphenol A epoxy resin, hexabromocyclododecane, triethylene glycol di Isooctanoate, zinc borate hydrate, sodium antimonate, methyl p-hydroxybenzoate, oxazolidinone, tetramethylthiuram disulfide, dibromomethane, fluoroquinolone, nano aluminum powder, nano silicon carbide, nano oxide Aluminum powder, albite powder, zirconium boride powder, bentonite, sodium metasilicate, polyglycerol ricinoleate, polyether silicone oil, polyvinyl acetate emulsion, sunflower oil, polyethylene glycol stearate, Furfurylamine, Diphenyl Ether, Diisononyl Phthalate, Tributyl Phosphate, Thiourea, Chlorinated Paraffin. The product of the invention has relatively superior flame retardancy, acid and alkali resistance, anti-mildew and antibacterial properties, and improves product performance.

Description

technical field [0001] The invention relates to a multifunctional protective coating for teaching appliances, which belongs to the technical field of teaching appliances. Background technique [0002] Teaching equipment is a general term for all kinds of equipment used to enable students to intuitively and visually understand the teaching content and the equipment used by teachers in teaching. Teaching aids for short. Teaching aids can improve students' interest in learning, enrich perceptual knowledge, help form clear concepts, and develop students' observation and thinking skills. It is generally divided into three categories: ordinary teaching aids, special teaching aids, and children's teaching aids. It is necessary to protect these teaching instruments with suitable coatings in order to improve their use effect. The coatings of general teaching instruments cannot achieve more functions, so it is necessary to improve them. Contents of the invention [0003] The purp...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D171/03C09D123/34C09D163/00C09D131/04C09D191/00C09D171/02C09D5/18C09D5/10C09D5/14C09D7/12
CPCC09D171/03C08K2201/011C08K2201/014C08L2201/02C08L2205/02C08L2205/035C09D5/103C09D5/14C09D5/18C09D7/61C09D7/63C09D7/65
Inventor 魏正如
Owner XIAOGAN QISIMIAOXIANG CULTURAL MEDIA
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com