Outdoor feedwater anti-ageing PE tubular product and preparation method thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A kind of anti-aging and pipe material technology, which is applied in the direction of pipes, rigid pipes, mechanical equipment, etc., can solve the problems of reducing the service life of PE pipes, poor aging resistance, and limiting the application range, etc., to achieve long service life, good aging resistance, The effect of excellent heat resistance
Inactive Publication Date: 2014-10-15
ANHUI DINGYUAN ZHENYUN PLASTIC
View PDF5 Cites 3 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
In recent years, with the rapid development of science and technology and the continuous improvement of people's living standards, the performance requirements of PE water supply pipes are getting higher and higher. At present, the PE water supply pipes on the market have poor aging resistance and are prone to cracking when exposed outdoors. , which greatly reduces the service life of PE pipes and limits its application range
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0013] An aging-resistant PE pipe for outdoor water supply, made of the following raw materials (kg): high-density polyethylene 60, polydiallyl terephthalate 30, bisphenol A polyarylate 16, montan wax 5 , Ethylene bis stearamide 4, methyl fluorosilicone oil 7, pentaerythritol monooleate 3.5, titanium dioxide 12, organic montmorillonite 13, dibutyltin dilaurate 1.5, basic lead carbonate 3, ethyl-3- Aminobutylate 2, diphenylthiourea 2.5, bis(dioctyl pyrophosphate acyloxy)ethylene titanate 1.5, bis(2-ethylhexyl) phosphate 6, filler masterbatch 22, bis (2,4-di-tert-butylphenyl) pentaerythritol diphosphite 2.5, 2,4-di-tert-butylphenol 1.5, resorcinol monobenzoate 1;
[0014] The preparation method of the filler masterbatch is as follows: a. Weigh the raw materials of the following weight (kg): serpentine 40, diatomite 30, pyrophyllite 18, olivine 12, behenyloxypolydimethylsiloxane 2. Distearyloxy isopropyl aluminate 2.5, di-n-octyl phthalate 10, diisodecyl adipate 15, decyl te...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Property
Measurement
Unit
yield strength
aaaaa
aaaaa
Vicat softening point
aaaaa
aaaaa
Login to view more
Abstract
The invention discloses an outdoor feedwater anti-ageing PE tubular product and a preparation method thereof. The outdoor feedwater anti-ageing PE tubular product is prepared from the following raw materials in parts by weight: 55-65 parts of high density polyethylene, 25-35 parts of poly diallyl terephthalate, 15-20 parts of bisphenol A type polyarylate, 4-7 parts of lignite wax, 3-5 parts of ethylene bis stearamide, 6-9 parts of methyl fluoride silicone oil, 2.5-4.5 parts of pentaerythritol monooleate, 10-15 parts of titanium white powder, 10-15 parts of organic montmorillonite, 1-2 parts of dibutyltin dilaurate, 2-4 parts of basic lead carbonate, 1.5-2.5 parts of ethyl-3-amino crotonate, 2-3 parts of diphenylthiourea, 1-2 parts of di(dioctylpyrophosphato) ethylene titanate, 4-8 parts of bis(2-ethylhexyl)phosphate, 18-24 parts of filling master batch, 2-3 parts of bis(2,4-di-tert-butylphenyl)pentaerythritol diphosphite, 1-2 parts of 2,4-di tertbutyl phenol, and 1-2 parts of resorcinol monobenzoate. The PE tubular product, provided by the invention, is good in age resistance and prominent in environmental stress crack resistance and anti-ultraviolet performance, has good heat resistance, flexibility, wear resistance and chemical corrosion resistance, and is long in service life.
Description
technical field [0001] The invention relates to a PE pipe and a preparation method thereof, in particular to an aging-resistant PE pipe for outdoor water supply and a preparation method thereof. Background technique [0002] PE pipes are widely used in the field of water supply manufacturing because of their high strength, high temperature resistance, corrosion resistance, non-toxicity, and wear resistance. They are replacement products for traditional steel pipes and PVC drinking water pipes. In recent years, with the rapid development of science and technology and the continuous improvement of people's living standards, the performance requirements of PE water supply pipes are getting higher and higher. At present, the PE water supply pipes on the market have poor aging resistance and are prone to cracking when exposed outdoors. , which greatly reduces the service life of the PE pipe and limits its application range. Therefore, there is an urgent need to develop an aging-...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.