Super-hard middle-chrome cast grinding ball and production process thereof

A technology for casting grinding balls and production processes, applied in the direction of manufacturing tools, furnace types, quenching agents, etc., can solve the problems of low wear resistance, low hardness, etc., to improve toughness and wear resistance, grain refinement, reduce The effect of the content of precious metal chromium

Inactive Publication Date: 2013-04-24
NINGGUO ZHONGYI WEAR RESISTANT MATERIALS
View PDF2 Cites 19 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the existing medium-chromium casting grinding ball ZQCr8 has a chromium content of 7-10%, and a surface hardness ≥ HRC48 is qualified. The hardness is too low and the wear resistance is low, which is far from meeting the requirements of domestic and foreign markets.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] To produce 30 mm superhard medium chromium casting grinding balls, the chemical composition of which is as follows:

[0043] Carbon (C): 2.78%, Silicon (Si): 0.61%, Manganese (Mn): 0.46%, Chromium (Cr): 8.15%, Phosphorus (P): 0.052%, Sulfur (S): 0.055%; Copper (CLl): 0.062%, molybdenum (Mo): 0.033%, nickel (Ni): 0.027%, tungsten (W): 0.02%, rare earth yttrium (Y-Re): 0.121%, iron (Fe): 87.43%.

[0044] The manufacturing process of 30mm superhard medium chromium casting grinding ball is as follows:

[0045] First, the steel scrap is melted in an intermediate frequency induction furnace, and the temperature is raised to 1510--1550°C, and then Cr, Cu, Mo, Ni, W alloys are added to achieve the required chemical composition. Then put the rare earth yttrium into the molten iron ladle, melt it with molten iron and let it stand for 7 minutes, so as to degrade and inoculate the molten iron. The treated molten iron uses casting direct-reading spectrometer to measure its chemic...

Embodiment 2

[0047] 40 mm superhard medium chromium casting grinding ball, its chemical composition is as follows:

[0048]Carbon (C): 2.86%, Silicon (Si): 0.78%, Manganese (Mn): 0.46%, Chromium (Cr): 7.5%, Phosphorus (P): 0.052%, Sulfur (S): 0.065%; Copper (CLl): 0.057%, molybdenum (Mo): 0.035%, nickel (Ni): 0.031%, tungsten (W): 0.02%, rare earth yttrium (Y-Re): 0.139%, iron (Fe): 89.53%.

[0049] The manufacturing process of 40mm ultra-high chromium grinding body is as follows:

[0050] First, the steel scrap is melted in an intermediate frequency induction furnace, and the temperature is raised to 1510--1550°C, and then Cr, Cu, Mo, Ni, W alloys are added to achieve the required chemical composition. Then put the rare earth yttrium into the molten iron ladle, melt it with molten iron and let it stand for 7 minutes, so as to degrade and inoculate the molten iron. The treated molten iron uses casting direct-reading spectrometer to measure its chemical element content, and the qualified...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
hardnessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a super-hard middle-chrome cast grinding ball which consists of the following chemical ingredients: 1.8-3.0% of carbon, 0.3-1.5% of silicon, 0.2-1.5% of manganese, 7.0-10.0% of chrome, 0.02-0.1% of phosphorus, 0.02-0.1% of sulfur, 0.02-0.1% of copper, 0.02-0.1% of molybdenum, 0.02-0.1% of nickel, 0.02-0.1% of tungsten, 0.1-0.2% of rare earth yttrium and 80.1-87.2% of iron. The rare earth yttrium is adopted for evolution inoculation treatment, so that a carbide is changed in shape and distribution, furthermore a net is broken, and meanwhile crystal grains are refined, the texture is compact and the flexibility is improved. By adopting an oil medium annealing and tempering thermal treatment process, eutectic carbide with martensite with the broken net is obtained, the hardness of the middle-chrome grinding ball is HRC60-69, and the toughness and the abrasion resistance of a high-chrome grinding ball are remarkably improved. On premise that the abrasion resistance and the crushing resistance of the grinding ball are further improved, the content of the noble metal chrome is reduced, and relatively the manufacturing cost of the grinding ball is lowered, and significant social benefits are achieved.

Description

technical field [0001] The invention relates to a grinding medium, that is, a cast grinding ball and a production process thereof Background technique [0002] As a grinding medium, grinding balls are widely used in powder engineering in industries such as building materials, cement, mining metallurgy, energy thermal power, non-metal processing, coal water slurry and magnetic materials. [0003] High chromium casting grinding balls are a new generation of high-efficiency grinding balls developed from ordinary forged steel balls, low and medium chromium casting grinding balls. The chromium content is greater than 10%. The known heat treatment technology is oil quenching and low temperature tempering. Under this condition, high-hardness martensite is formed, which greatly enhances the continuity and strength of the matrix, so the hardness and toughness of the grinding ball are significantly improved. my country's current standards (GB / T17445-2009, JC / T533-2004 and YB / T0...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C37/10C22C33/08C21D1/58C21D1/18C21D5/00C21D9/36
Inventor 韩文博韩仁青
Owner NINGGUO ZHONGYI WEAR RESISTANT MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com