Method for preparing high-temperature wear resistant lining plate by plasma arc cladding

A plasma arc and high temperature resistant technology, applied in the coating process and coating of metal materials, etc., can solve the problems of low high temperature wear resistance and high temperature impact resistance, affecting the continuous production of enterprises, increasing production costs, etc., to achieve good high temperature resistance. Impact capability, ideal resistance to high temperature abrasive wear, and the effect of improving performance and life

Inactive Publication Date: 2013-02-06
QINHUANGDAO GERUIDE ENERGY SAVING TECH SERVICE
View PDF5 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, these materials have high cost, poor high-temperature oxidation resistance, especially low high-temperature wear resistance and high-temperature impact resistance, resulting in low service life of high-temperature liners, affecting continuous production of enterprises, and increasing production costs.
[0003] In recent years, a lot of research work has been carried out at home and abroad to address the problems of low life and high cost of high-temperature linings, but they mainly focus on the research of a single material
Since the performance of a single material in terms of strength, toughness, hardness, high temperature resistance, wear resistance and oxidation resistance cannot be taken into account, the developed single material high temperature liner is not due to the shock of cooling and heat under the actual complex high temperature conditions on site. Cracking is due to high temperature oxidation failure, low high temperature wear resistance, high cost and low reliability, which cannot meet the needs of modern enterprises

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] Firstly, sandblasting is used to remove the rust, oil stain, scale, etc. on the surface of the hot-rolled steel plate 1Cr13 metal substrate; according to the characteristics of the metal substrate and the requirements of working conditions, the metal-based ceramic particle-reinforced alloy powder is prepared, and the powder of each alloy powder composition The mass percentage is: C 0.1%, Cr 10%, Ni 5%, the balance is Al, the particle size is 180 mesh, and is mixed with a mechanical powder mixer for 2 hours, and the mixed alloy powder is mixed with milky white glue, and then mixed Good alloy powder is evenly brushed on the surface of the metal substrate, the thickness of the pre-coating is 0.8mm, and it is dried naturally, and the metal substrate with the pre-coating is fixed on the processing machine of the plasma arc cladding equipment, and the plasma arc is The pre-coating on the surface of the substrate is scanned in a single pass. The process parameters of plasma arc...

Embodiment 2

[0018] Firstly, sandblasting is used to remove the rust, oil stain and scale on the surface of the hot-rolled steel plate 2Cr13 metal substrate. According to the characteristics of the metal substrate and the requirements of working conditions, the metal-based ceramic particle-reinforced alloy powder is prepared. The mass percentage of each alloy powder component It is: C 0.35%, Cr 15%, Ni 8%, the balance is Al, the particle size is 180 mesh, use a mechanical powder mixer to mix for 2 hours, mix the mixed alloy powder with milky white glue, and then mix the mixed The alloy powder is evenly brushed on the surface of the metal substrate, the thickness of the pre-coating is 1mm, and it is dried naturally. The coating is scanned in a single pass, and the process parameters of plasma arc cladding are: working current: 180A, working voltage: 18V, scanning width: 4mm, scanning speed: 290mm / min, overlap rate: 5%, nozzle distance The workpiece is 3mm, using argon as the protective and ...

Embodiment 3

[0020] Firstly, sandblasting is used to remove the rust, oil stain and scale on the surface of the hot-rolled steel plate 2Cr13 metal substrate. According to the characteristics of the metal substrate and the requirements of working conditions, the metal-based ceramic particle-reinforced alloy powder is prepared. The mass percentage of each alloy powder component It is: C 0.4%, Cr 25%, Ni 10%, the balance is Al, the particle size is 230 mesh, use a mechanical powder mixer to mix for 2 hours, mix the mixed alloy powder with milky white glue, and then put the mixed The alloy powder is evenly brushed on the surface of the metal substrate, the thickness of the pre-coating is 1.5mm, and it is dried naturally. The metal substrate with the pre-coating is fixed on the processing machine tool of the plasma arc cladding equipment. The coating is scanned in a single pass, and the process parameters of plasma arc cladding are: working current: 190A, working voltage: 19V, scanning width: 4m...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a method for preparing a high-temperature wear resistant lining plate by plasma arc cladding. The method comprises the steps as follows: removing rust, greasy dirt and oxide skin on the surface of a metal base; preparing metal-based ceramic particle reinforced alloy powder according to the metal base and the work requirement; mixing mixed alloy powder with white emulsion; uniformly coating the mixed alloy powder onto the surface of the metal base; controlling the thickness of a precoating layer to be 0.8-2 mm; naturally drying; fixing the metal base with the precoating layer to a machine tool of plasma arc cladding equipment; conducting single-pass scan on the precoating layer on the surface of the metal base by plasma arc; and uniformly cladding the surface of the metal base along with the movement of the plasma arc so as to obtain a cladding layer with the cladding thickness of 0.3-1.5 mm. The high temperature resistant compound lining plate prepared by the method is low in cost and stable in quality, is suitable for large-scale production, can meet the requirements of field high-temperature wear condition and can be effectively prolonged in service life.

Description

technical field [0001] The invention belongs to the field of mechanical processing technology, and in particular relates to a method for preparing a high-temperature wear-resistant liner by plasma arc cladding. Background technique [0002] With the development of industrial modernization, there are more and more high-temperature production environments, such as blast furnaces, coke ovens, continuous casting production systems in the metallurgical field, refining and synthesis systems in the petrochemical field, etc. Generally, the operating temperature of these high-temperature occasions can reach Above 800°, this working condition puts forward higher requirements for the high-temperature liner in work: it is required to meet high temperature resistance, oxidation resistance, wear resistance, high temperature impact resistance and other properties. The selection of high-temperature liners directly affects the safe production and continuous production of enterprises, and al...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C23C24/10
Inventor 赵明鹰
Owner QINHUANGDAO GERUIDE ENERGY SAVING TECH SERVICE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products