Water-borne polyurethane synthetic leather size and preparation method and application thereof

A technology of synthetic leather slurry and water-based polyurethane, applied in the preparation of water-based polyurethane synthetic leather slurry, water-based polyurethane synthetic leather slurry is used in the field of synthetic polyurethane synthetic leather preparation, to achieve low irritation, delay thermal oxidation, and peel strength Good results

Inactive Publication Date: 2014-03-05
ZHANGZHOU INST OF TECH
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The object of the present invention is to propose a method for preparing an environmentally friendly, safe, non-organic solvent-free, highly air-permeable water-based polyurethane synthetic leather slurry to solve the technical problem of compatibility between the water-based polyurethane slurry system and non-woven fabrics On the other hand, it is to reduce the purchase cost of organic solvents, reduce the production cost of enterprises, and produce films that are easy to wet on non-woven fabrics and form films on non-woven fabrics. At the same time, they have strong mechanical properties, good air permeability, Non-polluting water polyurethane synthetic leather with good hand feeling

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0056] The preparation method of described aqueous polyurethane synthetic leather slurry, described preparation method comprises the following steps:

[0057] 1) Under a nitrogen atmosphere, react diisocyanate, polyglycol and phosphoric acid in a reactor at 70-90°C under the action of a catalyst until the content of NCO isocyanate groups drops to 2%;

[0058] 2) Continue to add a hydrophilic chain extender to the reactor to extend the chain, keep warm and continue to react for 1 hour;

[0059] 3) Step 2) After the reaction is over, lower the temperature to 40~50°C and continue to add a neutralizing agent to the reaction kettle to neutralize the reaction solution. After neutralization, continue to add a small molecule chain extender or crosslinking agent, surface Active agent, continue to react at 40~50℃ for 10~15min;

[0060] 4) Step 3) After the reaction is over, add deionized water under rapid stirring to stir and emulsify evenly. After emulsifying evenly, continue to add f...

Embodiment 1

[0062] The preparation method of aqueous polyurethane synthetic leather slurry comprises the following steps:

[0063] 1) First take each component by the following parts by weight;

[0064] 5 parts diphenylmethane diisocyanate (MDI)

[0065] Toluene diisocyanate (TDI) 5 parts:

[0066] 10 parts of polyethylene glycol;

[0067] 5 parts of polypropylene glycol;

[0068] 5 parts of polyethylene adipate glycol;

[0069] 10 parts of polypropylene adipate;

[0070] Phosphoric acid 0.006 parts;

[0071] 0.01 part of dibutyltin dilaurate;

[0072] 0.04 parts of dimethylolbutyric acid;

[0073] 0.04 parts of 1,2-diamino-β-propanesulfonate;

[0074] Sodium hydroxide 0.008 part;

[0075] Hexamethylenediamine 0.07 part;

[0076] Sodium alkylbenzene sulfonate 0.01 part;

[0077] 0.01 part of sodium alkyl polyoxyethylene ether sulfate;

[0078] 20 parts of deionized water;

[0079] 8 parts wood flour;

[0080] 0.1 parts of titanium dioxide;

[0081] 0.05 part of phthalocyani...

Embodiment 2

[0088] The preparation method of aqueous polyurethane synthetic leather slurry comprises the following steps:

[0089] 1) First take each component by the following parts by weight;

[0090] 5 parts of isophorone diisocyanate (IPDI);

[0091] Hexamethylene diisocyanate (HDI) 5 parts;

[0092] 10 parts of polytetrahydrofuran diol;

[0093] 10 parts of polyoxytetramethylene glycol;

[0094] 10 parts of polybutylene adipate;

[0095] 20 parts of polyhexamethylene adipate;

[0096] Phosphoric acid 0.007 parts;

[0097] 0.1 part of stannous octoate;

[0098] Ethylenedihydroxyethanesulfonate 0.01 part;

[0099] 0.009 parts of sodium carbonate;

[0100] Hexamethylenediamine 0.02 part;

[0101] Ethylenediamine 0.01 part;

[0102] 0.02 part of sodium alkylsulfonate;

[0103] 0.02 part of sodium alkyl polyoxyethylene ether carboxylate;

[0104] 60 parts of deionized water;

[0105] 30 parts of light calcium carbonate;

[0106] Phthalocyanine pigment 0.1 part;

[0107] Dib...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
hydroxyl valueaaaaaaaaaa
acid valueaaaaaaaaaa
Login to View More

Abstract

The invention discloses a water-borne polyurethane synthetic leather size and a preparation method and an application thereof. The water-borne polyurethane synthetic leather size comprises diisocyanate, poly dibasic alcohol, phosphoric acids, catalysts, hydrophilic chain extenders, neutralizers, small molecule chain extenders or cross-linking agents, surface active agents and the like. The preparation method of the water-borne polyurethane synthetic leather size includes (1) polymerizing the diisocyanate, the poly dibasic alcohol and the phosphoric acids under the action of the catalysts; (2) adding the hydrophilic chain extenders for chain extension; (3) cooling and neutralizing a reaction solution, and continuing the reaction by adding the small molecule chain extenders or cross-linking agents and the surface active agents; and (4) emulsifying and adding auxiliaries to uniformly stir. According to the water-borne polyurethane synthetic leather size and the preparation method and the application thereof, the phosphoric acids are added in the formula, the wettability of the ultimately prepared synthetic leather size and non-woven fabrics is improved, further the process for preparing the synthetic leather can be simplified, properties of the prepared synthetic leather are improved, simultaneously the feed ratio of the diisocyanate and the poly dibasic alcohol is strictly controlled, and the ultimately prepared synthetic leather has the advantages that the peel strength and the hand feeling are good, and the rebound resilience is moderate.

Description

technical field [0001] The invention relates to a water-based polyurethane synthetic leather slurry, a preparation method of the water-based polyurethane synthetic leather slurry, and a preparation method and application of the water-based polyurethane synthetic leather slurry for synthesizing polyurethane synthetic leather. Background technique [0002] Polyurethane synthetic leather was produced in the late 1970s and developed in the 1990s. In the traditional production process of polyurethane synthetic leather, organic solvent polyurethane resin is used as its basic raw material. This type of polyurethane resin uses dimethylformamide, butanone, xylene, toluene, acetone, ethyl acetate, etc. The main solvent is obtained by solvent polymerization. These organic solvents, which account for more than 60% of the entire resin composition, have large toxic and side effects, not only cause environmental pollution, endanger the health of operators, but also are flammable and explo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08G18/66C08G18/48C08G18/42C08K13/02C08K5/521C08L75/06C08L75/08D06N3/14
Inventor 陈建福黄慧珍林祥福苏火煌
Owner ZHANGZHOU INST OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com