Preparation method of cerium oxide microspheres

A technology of ceria and microspheres, which is applied in the field of nanomaterials and achieves the effects of simple preparation method, mild reaction conditions and easy control.

Inactive Publication Date: 2014-03-05
INNER MONGOLIA UNIV OF SCI & TECH
View PDF4 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] This gas-phase diffusion method is used for barium carbonate and calcium carbonate more, but the gas-phase diffusion method is used for the preparation of cerium oxide and has not been reported yet.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of cerium oxide microspheres
  • Preparation method of cerium oxide microspheres
  • Preparation method of cerium oxide microspheres

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] (1) Dissolve industrial cerium carbonate with nitric acid to obtain cerium nitrate, remove impurities and filter to obtain 282.62g / L cerium nitrate mother liquor with high purity.

[0035] Take 42.6mL of cerium nitrate mother liquor in a beaker filled with 457.4mL of water, stir evenly with a glass rod, and then vibrate with ultrasonic waves for 5min; in addition, dissolve 0.5g / L polyelectrolyte PSS in 500mL of water, stir evenly with a glass rod, Also use ultrasonic vibration for 5 minutes; then slowly pour the PSS aqueous solution into the cerium nitrate aqueous solution, adjust the pH to 4, continue stirring until uniform, use ultrasonic vibration for 15 minutes, seal the mouth of the beaker with plastic wrap, and pierce 3 holes on the plastic wrap ,stand-by;

[0036] (2) Take 20.2 g of ground ammonium carbonate, put it into a petri dish, seal it with plastic wrap, and make 3 holes.

[0037] (3) Put the petri dish containing ammonium carbonate in (2) into the bottom...

Embodiment 2

[0041] (1) Dissolve industrial cerium carbonate with nitric acid to obtain cerium nitrate, remove impurities and filter to obtain 282.62g / L cerium nitrate mother liquor with high purity. Take 9.74mL of cerium nitrate mother liquor in a beaker containing 491.26mL of water, stir evenly with a glass rod, then oscillate with an ultrasonic wave for 5min; dissolve 0.5g / L PAH in 500mL of water, stir evenly with a glass rod, Ultrasonic oscillation for 5 minutes; then slowly pour the polyelectrolyte PAH aqueous solution into the cerium nitrate aqueous solution, adjust the pH to 4, continue stirring until uniform, use ultrasonic oscillation for 15 minutes, seal the mouth of the beaker with plastic wrap, and pierce 3 holes on the plastic wrap ,stand-by;

[0042] (2) Take 3.8g of ground ammonium bicarbonate, put it into a petri dish, seal it with plastic wrap, and make 3 holes.

[0043] (3) Put the petri dish containing ammonium bicarbonate in (2) into the bottom of the desiccator, add a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
particle sizeaaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of cerium oxide microspheres, which comprises the following steps: preparing spherical cerous carbonate by a vapor phase diffusion process by using polyelectrolyte as a shape control agent; and carrying out high-heat treatment to obtain the CeO2 microspheres with high specific area. The particle size of the CeO2 microspheres is 300-500nm, and the specific area reaches more than 110 m<2> / g after the CeO2 microspheres are roasted at 500 DEG C. The vapor phase diffusion process is utilized for the first time to prepare the cerium oxide microspheres, and the whole reaction process is carried out at room temperature, so that the invention has the advantages of mild reaction conditions and simple preparation method and is easy to control. The polyelectrolyte is used as the shape control agent for the first time to regulate the shape of the cerous carbonate, thereby regulating the shape of the cerium oxide. Cations and anions of the polyelectrolyte in the water solution can regulate the aggregation of ions and control the shape and size of the cerous carbonate, thereby controlling the shape and size of the cerium oxide. The cerium oxide with high specific area has important applications in catalytic materials of automobile exhaust catalytic purification, petroleum cracking, chemical engineering and the like.

Description

Technical field [0001] The present invention involves a method of preparing a micro -balls. Specifically, it is in the gas phase diffusion device, and the use of organic matter as a template to regulate powder preparation is the field of nanomaterials technology. Background technique [0002] The oxidation is currently widely used in various fields, CEOs 2 Aerobic dysfunction (CE 3+ / CE 4+ ), Therefore has a unique oxidation reduction performance, that is, higher storage and release of oxygen capacity, which is widely used in multi -phase catalytic reactions, especially CEO 2 It is a catalyst of the assistant or carrier. It shows good catalytic performance in solid oxide fuel batteries, car tail gas purification, hydrophilic transformation, constitutionaldehyde, ethanol, and CO completely oxidized and alcohol -reorganized hydrogen reactions. [0003] Generally speaking, small size and large -scale surface area CEO 2 Granules show high catalytic activity and selectivity, namely th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C01F17/00B01J23/10B01J35/08
Inventor 胡艳宏李梅柳召刚王觅堂刘翠翠张永强
Owner INNER MONGOLIA UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com