Zinc-magnesium titanate series ceramic dielectric material and prepared ceramic capacitor

A technology of ceramic capacitors and ceramic dielectrics, applied in the direction of laminated capacitors, fixed capacitor electrodes, fixed capacitor dielectrics, etc., can solve problems such as harmful to the environment and human body, thermal stability, and insufficient dielectric properties

Inactive Publication Date: 2009-02-25
GUANGDONG FENGHUA ADVANCED TECH HLDG
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Traditional high-frequency dielectric ceramic materials usually have insufficient performance in terms of thermal stability and dielectric properties, and all contain harmful elements such as lead (Pb), arsenic (As), cadmium (Cd), which are harmful to the environment and human body

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Zinc-magnesium titanate series ceramic dielectric material and prepared ceramic capacitor
  • Zinc-magnesium titanate series ceramic dielectric material and prepared ceramic capacitor
  • Zinc-magnesium titanate series ceramic dielectric material and prepared ceramic capacitor

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] Raw materials with a purity of 99.5 or more, with 0.999 moles of Mg(OH) 2 , 0.001 mole of ZnO and 1 mole of TiO 2 Mixing ratio, ball milling and mixing evenly, pre-calcine the mixture at 1080-1130°C for 2.5 hours to obtain the main agglomerate zinc magnesium titanate Mg (1-x) Zn x TiO 3 (x=0.001).

[0028] Raw materials with a purity of 99.5 or more, with 1.999 moles of Mg(OH) 2 , 0.001 mole of ZnO and 1 mole of SiO 2 Mixing ratio, ball milling and mixing evenly, pre-calcine the mixture at 1140-1180°C for 2.5 hours to obtain the main agglomerate zinc magnesium silicate Mg (2-y) Zn y SiO 4 (y=0.001).

[0029] Then, auxiliary components were added to the main components in predetermined proportions, as shown in Table 1. Make ceramic materials according to the conventional material production process; then, according to the production process of chip MLCC, add organic binders and ethanol and other solvents to form a slurry, and make the slurry flow into a 20-micro...

Embodiment 2

[0037] Raw materials with a purity of 99.5 or more, with 0.999 moles of Mg(OH) 2 , 0.001 mol ZnO and 1 mol TiO 2 Mixing ratio, ball milling and mixing evenly, pre-calcine the mixture at 1080-1130°C for 2.5 hours to obtain the main agglomerate zinc magnesium titanate Mg (1-x) Zn x TiO 3 (x=0.001).

[0038] Raw materials with a purity of 99.5 or more, with 1.999 moles of Mg(OH) 2 , 0.001 mol ZnO and 1 mol SiO 2 Mixing ratio, ball milling and mixing evenly, pre-calcine the mixture at 1140-1180°C for 2.5 hours to obtain the main agglomerate zinc magnesium silicate Mg (2-y) Zn y SiO 4 (y=0.001).

[0039] Raw materials with a purity of 99.5 or more, mixed with ZnO and H in a predetermined ratio 3 BO 3 , ball milled evenly, and then pre-calcined the mixture for 2.5 hours, thus obtaining a uniform auxiliary component ZnO and B2O3 mixture.

[0040] Then add auxiliary components to the main components according to a predetermined ratio, as shown in Table 3, manufacture and te...

Embodiment 3

[0047] Raw materials with a purity of 99.5 or more, with 0.995 moles of Mg(OH) 2 , 0.005 mol ZnO and 1 mol TiO 2 Mixing ratio, ball milling and mixing evenly, pre-calcine the mixture at 1080-1130°C for 2.5 hours to obtain the main agglomerate zinc magnesium titanate Mg (1-x) Zn x TiO 3 (x=0.005).

[0048] Raw materials with a purity of 99.5 or more, with 1.98 moles of Mg(OH) 2 , 0.02 mol ZnO and 1 mol SiO 2 Mixing ratio, ball milling and mixing evenly, pre-calcine the mixture at 1140-1180°C for 2.5 hours to obtain the main agglomerate zinc magnesium silicate Mg (2-y) Zn y SiO 4 (y=0.02).

[0049] Raw materials with a purity of 99.5 or more, mixed with ZnO and H in a predetermined ratio 3 BO 3 , ball milled evenly, and then pre-calcined the mixture for 2.5 hours, thus obtaining a uniform auxiliary component ZnO and B2O3 mixture.

[0050] Then add auxiliary components to the main components in a predetermined proportion, as shown in Table 5, manufacture and test accor...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
Login to View More

Abstract

This invention discloses a high frequency thermal stable ceramic material and its ceramic capacitor. The material comprises the main component and assistant components, wherein the main components are 40-55% of Mg(1-x)ZnxTiO3(0.0001<=X<=0.05) and 20-25% of Mg(2-y)ZnySiO4(0.0001<=X<=0.05); the assistant components are 10-15% of ZnO and 3.0-7.0% of Al2O3 and 2.0-6.0% of SrO. The assistant components also comprise the following: 1.0-2.5% of B2O3,0.5-2.0% of Nd2O5,0.1-0.5% of MnO2,0.1-0.4% of Co3O4 and one or more materials from K2O,Fe2O3,CeO2 and SnO.

Description

technical field [0001] The present invention relates to a ceramic dielectric material with high frequency and low dielectric heat stability and the obtained ceramic capacitor, more specifically, the present invention relates to a zinc-magnesium titanate-based ceramic dielectric that does not contain harmful elements such as lead, arsenic, and cadmium Materials and resulting ceramic capacitors. Background technique [0002] MLCC is widely used in the manufacturing process of electronic equipment due to its small size, high reliability, and convenient placement. The market's demand for high-frequency capacitors is also increasing, and the requirements are higher, and the use frequency is developing to hundreds of megahertz or even several gigahertz microwave bands. Traditional high-frequency dielectric ceramic materials usually have insufficient performance in terms of thermal stability and dielectric properties, and all contain harmful elements such as lead (Pb), arsenic (As...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01G4/12H01G4/30H01G4/008H01B3/12C04B35/462
Inventor 魏汉光李文君付振晓王作华周志珍张火光韩建宏
Owner GUANGDONG FENGHUA ADVANCED TECH HLDG
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com