Aluminium tungsten carbide hard alloy sintered body

A cemented carbide and tungsten carbide aluminum technology, which is applied in the field of preparing tungsten carbide aluminum cemented carbide sintered bodies by vacuum hot pressing sintering technology, can solve the problems such as difficult to achieve high-density sintering, and achieve excellent oxidation resistance, convenient operation, and low cost. effect of density

Inactive Publication Date: 2006-12-13
CHANGZHOU INST OF ENERGY STORAGE MATERIALS &DEVICES
View PDF0 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Powder metallurgy sintering is the basic method of powder sintering into blocks, but due to the high melting point and high temperature resistance of tungsten carbide aluminum cemented carbide, it is difficult to achieve high-density sintering by general powder metallurgy methods
The synthesis technology of tungsten carbide aluminum alloy powder is still in its infancy, so far, there is no report about the alloy sintered body at home and abroad

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Aluminium tungsten carbide hard alloy sintered body

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0013] Embodiment 1: with 30 grams of (W 0.9 Al 0.1 ) C and 3 grams of cobalt powder are mixed and put into graphite moulds, and the weight ratio of the two is 10; 1, at 10 -1 MPa~10 -2 Sintering under MPa vacuum condition, the sintering temperature is 1600°C, the pressure is 37.5MPa, the sintering time is 30 minutes, the sample is polished, and the relative density is 98%. Microhardness 2200Kg / cm 3 , Bending strength 1573MPa.

Embodiment 2

[0014] Embodiment 2: the weight is 25 grams (W 0.75 Al 0.25 ) C and a quality of 2.50 grams of cobalt powder are mixed and put into graphite moulds. -1 MPa~10 -2 Sintering under MPa vacuum condition, the sintering temperature is 1500°C, the pressure is 35.5MPa, and the sintering time is 25 minutes. The samples were polished and had a relative density of 97%. Microhardness 2035Kg / cm 3 , Bending strength 1421MPa.

Embodiment 3

[0015] Embodiment 3: the weight is 20 grams (W 0.5 Al 0.5 ) C and a quality of 2.00 grams of cobalt powder are mixed and put into graphite moulds. The proportioning ratio of the two weights is 10. -1 MPa~10 -2 Sintering under MPa vacuum condition, the sintering temperature is 1450°C, the pressure is 35.5MPa, and the sintering time is 30 minutes. The samples were polished and had a relative density of 98%. Microhardness 1650Kg / cm 3 , Bending strength 1337MPa.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
microhardnessaaaaaaaaaa
microhardnessaaaaaaaaaa
bending strengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to a tungsten-cemented aluminium carbide sintered body, and the expression is(W1-xAlx)C-Co, in which x=0.1-0.86, which is alloy block-shaped material with good crystalline shape and fine texture. Proved by X-ray powder diffraction analysis and scanning electron microscope analysis, the tungsten-cemented aluminium carbide sintered body is of stable structure, improved crystallinity and higher degree of compactness. The tungsten-cemented aluminium carbide sintered body of this invention not only has glass hard and high-wearing feature of tungsten carbide, but also has lightweight, oxidation resistance and fine ductility of aluminium, which makes the alloy have high hardness, high bending strength and lower density and develop into new carbide alloy with high hardness, high strength, good workability and high oxidation-resistance temperature. The said material is hoped to be used in mechanical tool, glass-cutting, bolt die, broaching die, bowl, well drill, mine drill, cutting drill and electrical contact material.

Description

Technical field: [0001] The invention belongs to a tungsten carbide aluminum cemented carbide sintered body, in particular to preparing a tungsten carbide aluminum cemented carbide sintered body by using tungsten carbide aluminum powder as a raw material and cobalt as a binder phase through vacuum hot pressing sintering technology. Background technique: [0002] Tungsten carbide aluminum cemented carbide is an emerging technical material researched and developed in recent years. Tungsten carbide aluminum refers to a substitutional solid solution alloy formed by part of Al atoms entering the tungsten site in the WC lattice. On the basis of high hardness and high wear resistance of tungsten carbide, it also has the light weight, oxidation resistance and excellent ductility of aluminum, so that the alloy has high hardness (microhardness greater than 1200Kg / cm 3 ), high bending strength (above 1100MPa) and low density (the density of rich aluminum alloy can reach 3.0g / cm 3 ), i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C29/06
Inventor 马贤锋乔竹辉汤华国赵伟蔡曙光赵波
Owner CHANGZHOU INST OF ENERGY STORAGE MATERIALS &DEVICES
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com