Mold surface strengthening treatment process and system

A surface strengthening and treatment system technology, applied in heat treatment furnaces, heat treatment equipment, heat treatment process control, etc., can solve problems such as oil pollution, product shape and quality not up to standard, oxidation, etc.

Inactive Publication Date: 2021-09-10
上海恩耀机电有限公司
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] As an important process equipment in the manufacturing industry, the mold is widely used to produce products of the same shape and quality; the use of the mold has a service life, and after a period of use, the mold will have problems such as wear, oxidation or oil pollution, resulting in The shape and quality of the produced products cannot meet the standards, resulting in the scrapping of the mold

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Mold surface strengthening treatment process and system
  • Mold surface strengthening treatment process and system
  • Mold surface strengthening treatment process and system

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0040] The following is attached Figure 1-4 The application is described in further detail.

[0041] The embodiment of the present application discloses a mold surface strengthening treatment process and system.

[0042] refer to figure 1 , mold surface strengthening treatment process and system, including the following steps:

[0043] S1, cleaning the surface of the mold with a strong cleaning solvent of Methacron to remove surface impurities;

[0044] S2, using quartz sand to blast the surface of the mold with an air gun, sandblasting the mold in a dry and non-liquid medium, and removing rust, scale, and oil on the surface of the mold to enhance surface adhesion Effect;

[0045] S3, the mold is placed in the molten borax mixture, and the metal carbide coating is formed on the surface of the mold by diffusion at a high temperature of 900-1100 ° C. The metal carbide coating can be carbide of vanadium, chromium, tantalum or titanium, A layer of high-hardness metal carbide...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a mold surface strengthening treatment process and system, in particular to the field of molds. The mold surface strengthening treatment process comprises the following steps: cleaning the surface of a mold; performing sand blasting treatment on the surface of the mold by using quartz sand through an air pressure gun; placing the mold in a molten borax mixture, and forming a metal carbide coating on the surface of the mold through diffusion action at the high temperature of 900-1100 DEG C; adjusting the position of a heat radiation heating contact on a hanging bracket according to the model of the corresponding processing mold, placing the mold subjected to coating treatment on the hanging bracket, feeding the hanging bracket into a tempering furnace at a uniform speed, and closing a furnace cover; and carrying out tempering treatment in a vacuum atmosphere, heating the tempering furnace to 500-650 DEG C, carrying out tempering heat preservation for 2-3 hours, cooling to 250-500 DEG C, carrying out tempering heat preservation for 1-2 hours, and carrying out uniform temperature control cooling to room temperature along with the furnace. The process and the system have the effect of uniformly regulating and controlling the surface temperature of the mold.

Description

technical field [0001] The present application relates to the field of molds, in particular to a mold surface strengthening treatment process and system. Background technique [0002] As an important process equipment in the manufacturing industry, the mold is widely used to produce products of the same shape and quality; the use of the mold has a service life, and after a period of use, the mold will have problems such as wear, oxidation or oil pollution, resulting in The shape and quality of the produced products cannot meet the standards, resulting in the scrapping of the mold. [0003] A Chinese patent with the patent application number 201611050063.3 discloses a surface strengthening treatment process for automobile molds, which includes the following steps: cleaning the surface of the mold; grinding the surface of the mold with sandpaper; spraying and welding the strengthening powder on the surface of the mold after grinding ; Send the mold after spray welding into th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C21D1/18C21D1/773C21D7/06C21D9/00C21D11/00C23C8/02C23C8/44
CPCC21D1/18C21D9/0068C21D1/773C21D7/06C21D9/0025C23C8/44C23C8/02C21D11/00
Inventor 谭辉李建军
Owner 上海恩耀机电有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap