A kind of rare earth garnet scintillation crystal and its production method

A technology of scintillation crystals and production methods, applied in crystal growth, single crystal growth, single crystal growth, etc., can solve the problems of low transparency, low density of rare earth garnet scintillation crystals, poor chemical stability, etc., and achieve high melting point and radiation conversion Effects of efficiency, good chemical and photochemical stability, ease of doping with rare earth ions

Active Publication Date: 2022-04-22
安徽晶宸科技有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Rare earth garnet scintillation crystals prepared in the prior art usually have defects such as low density, low transparency, poor chemical stability and mechanical strength.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of rare earth garnet scintillation crystal and its production method
  • A kind of rare earth garnet scintillation crystal and its production method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] A rare earth garnet scintillation crystal, which has the following chemical formula: Y 3 sc 2 Al 3 o 12 ;

[0029] Wherein, the effective segregation coefficient of Y in the rare earth garnet scintillation crystal is 0.31, the effective segregation coefficient of Sc is 0.33, and the effective segregation coefficient of Al is 0.38.

[0030] A kind of production method of rare earth garnet scintillation crystal comprises the following steps:

[0031] S1: Weigh 1250g Y in proportion 2 o 3 , 1250g Sc 2 o 3 and 700g Al 2 o 3 , and add 75g of sintering aid, after mixing evenly, raise the temperature to 1425°C at a heating rate of 5°C / min and keep it warm for 1.25h to obtain a mixed powder;

[0032] Among them, the sintering aid is made of the following percentages of raw materials: SiO 2 The mass fraction of MgO accounts for 60%, and the mass fraction of MgO accounts for 40%;

[0033] S2: The mixed powder is made into 40mm particles, and then isostatically pressed...

Embodiment 2

[0036] A rare-earth garnet scintillation crystal with the following chemical formula: Cd 3 sc 2 Ga 3 o 12 ;

[0037] Wherein, the effective segregation coefficient of Cd in the rare earth garnet scintillation crystal is 0.3, the effective segregation coefficient of Sc is 0.33, and the effective segregation coefficient of Ga is 0.36.

[0038] A kind of production method of rare earth garnet scintillation crystal comprises the following steps:

[0039] S1: Weigh 1000g Cd in proportion 2 o 3 , 1000g Sc 2 o 3 and 500g Ga 2 o 3, and add 50g of sintering aid, after mixing evenly, raise the temperature to 1400°C at a heating rate of 5°C / min and keep it warm for 1h to obtain a mixed powder;

[0040] Among them, the sintering aid is made of the following percentages of raw materials: SiO 2 The mass fraction of MgO accounts for 55%, and the mass fraction of MgO accounts for 35%;

[0041] S2: The mixed powder is made into 35mm particles, and then isostatically pressed under a...

Embodiment 3

[0044] A rare-earth garnet scintillation crystal with the following chemical formula: Lu 3 sc 2 In 3 o 12 ;

[0045] Wherein, the effective segregation coefficient of Lu in the rare earth garnet scintillation crystal is 0.32, the effective segregation coefficient of Sc is 0.33, and the effective segregation coefficient of In is 0.4.

[0046] A kind of production method of rare earth garnet scintillation crystal comprises the following steps:

[0047] S1: Weigh 1500g Lu in proportion 2 o 3 , 1500g Sc 2 o 3 and 900g In 2 o 3 , and add 100g of sintering aid, after mixing evenly, raise the temperature to 1450°C at a heating rate of 5°C / min and keep it warm for 1.5h to obtain a mixed powder;

[0048] Among them, the sintering aid is made of the following percentages of raw materials: SiO 2 The mass fraction of MgO accounts for 65%, and the mass fraction of MgO accounts for 45%;

[0049] S2: The mixed powder is made into 45mm particles, and then isostatically pressed und...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a rare earth garnet scintillation crystal and a production method thereof. The rare earth garnet scintillation crystal has the following chemical formula: A 3 sc 2 B 3 o 12 ; Wherein, A is a kind of in rare earth elements such as Y, Cd, Lu, and B is a kind of in Al, Ga or In, and the effective segregation coefficient of A in this rare earth garnet scintillation crystal is 0.3-0.32, and Sc The effective segregation coefficient is 0.33, and the effective segregation coefficient of B is 0.36‑0.4. The molecular formula obtained in the present invention is A 3 sc 2 B 3 o 12 The rare earth garnet scintillation crystal has excellent characteristics such as high density, high effective atomic coefficient, high melting point, high thermal conductivity, high hardness, low thermal expansion coefficient, high transparency, good chemical stability, and high mechanical strength.

Description

technical field [0001] The invention relates to the technical field of scintillation crystals, in particular to a rare earth garnet scintillation crystal and a production method thereof. Background technique [0002] Inorganic scintillation crystal materials have a wide range of applications in polymer detection, nuclear physics, and medical imaging equipment. In recent decades, the urgent need for high-resolution cleaning imaging in modern medical diagnostic techniques has stimulated research interest in scintillation materials with high density, high light output, and fast decay. Garnet originally refers to the equiaxed silicate minerals in the shape of pomegranate seeds that exist in nature, but the artificially synthesized garnet crystals are mainly silicate, and the rare earth garnet scintillation crystals are formed by doping rare earth elements in garnet crystals. , which is the material of choice for solid-state lasers. [0003] Scintillation crystals typically inc...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C01F17/10C01F17/32C01F17/34C30B29/28
CPCC01F17/34C01F17/32C01F17/10C30B29/28
Inventor 马孙明彭方郭玉勇窦仁勤毛炯陈仪翔张庆礼
Owner 安徽晶宸科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More