Graphene modified unsaturated polyester resin adhesive and production method thereof

A technology of graphene modification and polyester resin, which is applied in the direction of polyester coatings, coatings, anti-corrosion coatings, etc., can solve the problems of lack of corrosion resistance, easy aging, high brittleness, etc., and achieve convenient operation, easy production, good flexibility

Inactive Publication Date: 2020-03-24
扬州润友复合材料有限公司
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, compared with resins such as epoxy resin and furan resin, unsaturated polyester resin is still lacking in corrosion resistance. In addition, it also has defects such as high brittleness and easy aging.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Graphene modified unsaturated polyester resin adhesive and production method thereof
  • Graphene modified unsaturated polyester resin adhesive and production method thereof
  • Graphene modified unsaturated polyester resin adhesive and production method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] A graphene-modified unsaturated polyester resin glue is composed of a component and a component B. The parts by mass of component A and component B are as follows:

[0027]

[0028] The unsaturated polyester resin is a bisphenol A type unsaturated polyester resin, and its viscosity at 25° C. is 450 mPa·s.

[0029] The calcium sulfate whisker has an aspect ratio of 50 and an average diameter of 3 μm.

[0030] The modified nano glass fiber powder has an alkali metal oxide content of 14% and a particle diameter of 80nm.

[0031] Described modified graphene, its specific surface area is 2400m 2 / g.

[0032] Component B is methyl ethyl ketone peroxide.

[0033] A kind of preparation method of graphene modified unsaturated polyester resin glue, comprises the following steps:

[0034] (1) Component A:

[0035] ① Add 1 mass part of graphene and 50 mass parts of a mixture of concentrated sulfuric acid and concentrated nitric acid with a volume ratio of 3:1 into the cont...

Embodiment 2

[0046] A graphene-modified unsaturated polyester resin glue is composed of a component and a component B. The parts by mass of component A and component B are as follows:

[0047]

[0048] The unsaturated polyester resin is a bisphenol A type unsaturated polyester resin, and its viscosity at 25° C. is 300 mPa·s.

[0049] The calcium sulfate whiskers have an aspect ratio of 30 and an average diameter of 1 μm.

[0050] The modified nano glass fiber powder has an alkali metal oxide content of 13% and a particle diameter of 60nm.

[0051] Described modified graphene, its specific surface area is 1800m 2 / g.

[0052] Component B is methyl ethyl ketone peroxide.

[0053] A kind of preparation method of graphene modified unsaturated polyester resin glue, comprises the following steps:

[0054] (1) Component A:

[0055]① Add 1 mass part of graphene and 40 mass parts of a mixture of concentrated sulfuric acid and concentrated nitric acid with a volume ratio of 3:1 into the con...

Embodiment 3

[0066] A graphene-modified unsaturated polyester resin glue is composed of a component and a component B. The parts by mass of component A and component B are as follows:

[0067]

[0068]

[0069] The unsaturated polyester resin is a bisphenol A type unsaturated polyester resin, and its viscosity at 25° C. is 600 mPa·s.

[0070] The calcium sulfate whisker has an aspect ratio of 70 and an average diameter of 5 μm.

[0071] The modified nano glass fiber powder has an alkali metal oxide content of 15% and a particle size of 100nm.

[0072] Described modified graphene, its specific surface area is 3000m 2 / g.

[0073] Component B is methyl ethyl ketone peroxide.

[0074] A kind of preparation method of graphene modified unsaturated polyester resin glue, comprises the following steps:

[0075] (1) Component A:

[0076] ① Add 1 mass part of graphene and 60 mass parts of a mixture of concentrated sulfuric acid and concentrated nitric acid with a volume ratio of 3:1 into...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
viscosityaaaaaaaaaa
diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to a graphene modified unsaturated polyester resin adhesive, which comprises a component A and a component B, wherein the component A is prepared from a unsaturated polyester resin, tung oil, sodium diethyldithiocarbamate, calcium sulfate whiskers, modified nanometer glass fiber powder, modified graphene and cobalt naphthenate, and the component B is methyl ethyl ketone peroxide. According to the invention, the graphene modified unsaturated polyester resin adhesive is easy to produce and manufacture, can be directly brushed and the like only by uniformly mixing the component A and the component B during use, can further be used for producing glass fiber reinforced plastics and other subsequent products, and is convenient to operate; and the graphene modified unsaturated polyester resin adhesive can resist the erosion of chemical mediums in a use process, and has the characteristics of good flexibility, no cracking, aging resistance and the like.

Description

technical field [0001] The invention relates to a graphene-modified unsaturated polyester resin glue and a preparation method thereof, belonging to the technical field of polymer materials and environmental protection. Background technique [0002] Unsaturated polyester resin is generally a linear polymer compound with ester bonds and unsaturated double bonds formed by polycondensation of unsaturated dibasic acid diols or saturated dibasic acid diols. Unsaturated polyester resin has the characteristics of low price and wide application, and has been widely used, especially in my country, which is a big country in the production and use of unsaturated polyester resin. Unsaturated polyester resin has been widely used in construction, anti-corrosion, yacht, furniture coating and other fields. [0003] However, compared with resins such as epoxy resin and furan resin, unsaturated polyester resin is still lacking in corrosion resistance. In addition, it also has defects such as ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D167/06C09D5/08C09D7/61C09D7/62C09D7/63C09D7/65
CPCC08K2201/011C09D5/08C09D167/06C09D7/61C09D7/62C09D7/63C09D7/65C09D7/70C08L91/005C08K13/06C08K9/04C08K9/06C08K7/14C08K3/042C08K7/08C08K5/39C08K5/14C08K5/098
Inventor 徐致伟邹华维
Owner 扬州润友复合材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More