An organic cathode material for lithium ion battery and its application

A technology for lithium ion batteries and cathode materials, which is applied in the field of lithium ion cathode material preparation, can solve the problems of low output voltage, restricting the energy density of organic lithium ion batteries, etc., so as to improve the energy density, improve the cycle stability, and the preparation process is green and environmentally friendly. Effect

Active Publication Date: 2021-05-18
HUAZHONG UNIV OF SCI & TECH
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Carbonyl materials generally have low output voltage (2.0-2.5V, vs Li / Li + ), which undoubtedly greatly restricts the energy density of organic lithium-ion batteries

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • An organic cathode material for lithium ion battery and its application
  • An organic cathode material for lithium ion battery and its application
  • An organic cathode material for lithium ion battery and its application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0053] The synthesis of conjugated aromatic fused ring P-1 is shown below

[0054]

[0055] Dissolve 1.6-dibromopyrene in N-methylpyrrolidone (NMP), add anhydrous sodium sulfide, and carry out polycondensation reaction. After the reaction was completed, centrifuged, washed, dried, and Soxhlet extracted and purified to obtain the conjugated aromatic fused ring derivative polythiopyrene P-1 of the material. The polymer was calculated to be 11 through elemental analysis and halogen content determination.

[0056] Mix 30mg of polythiopyrene, 24mg of Super-P and 6mg of polyvinylidene fluoride thoroughly, add 0.5ml of N-methylpyrrolidone, grind again to obtain a homogeneous slurry, evenly coat it on aluminum foil, and then vacuum at 80°C Dry for 12 hours to prepare an electrode film. In a dry argon glove box, use the prepared electrode film as the positive electrode, glass fiber as the separator, 1.0mol / L lithium perchlorate propylene carbonate solution as the electrolyte, and m...

Embodiment 2

[0059] The synthesis of the conjugated aromatic fused ring P-8 is shown below:

[0060]

[0061] Dissolve pyrene diboronic acid ester in a mixed solution of dioxane and water (volume ratio, 1:1), add an equivalent amount of 2,5-dibromothiophene, add a palladium catalyst, and heat up for 24 hours after deoxygenation . After the reaction is completed, the reaction solution is poured into methanol, the precipitate is precipitated, centrifuged, washed, and purified by Soxhlet extraction to obtain the conjugated aromatic fused ring derivative thienylpyrene polymer of the material, and the polymer is between 8- Between 20.

[0062] Mix 30mg of thienylpyrene polymer, 24mg of Super-P and 6mg of polyvinylidene fluoride thoroughly, add 0.5ml of N-methylpyrrolidone, and grind again to obtain a homogeneous slurry, which is evenly coated on aluminum foil, and then at 80 °C for 12 hours in vacuum to prepare an electrode film. In a dry argon glove box, use the prepared electrode film a...

Embodiment 3

[0065] The synthesis of the conjugated aromatic fused ring P-14 is shown below:

[0066]

[0067] Dissolve pyrene diboronic acid ester in the mixed solution of dioxane and water (volume ratio, 1:1), add equivalent 3,7-dibromo-N methylphenothiazine, add palladium catalyst, remove Oxygen post-heating reaction for 24 hours. After the reaction is completed, the reaction solution is poured into methanol, the precipitate is precipitated, centrifuged, washed, and purified by Soxhlet extraction to obtain the conjugated aromatic condensed ring derivative phenothiazine pyrene polymer, the polymer of which is between 8 Between -20.

[0068] Mix 30mg of phenothiazine pyrene polymer, 24mg of Super-P and 6mg of polyvinylidene fluoride thoroughly, add 0.5ml of N-methylpyrrolidone, and grind again to obtain a homogenate, which is evenly coated on aluminum foil, and then placed on Vacuum drying at 80°C for 12 hours to prepare an electrode film. In a dry argon glove box, use the prepared ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
current efficiencyaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the field of preparation of positive electrode materials for lithium ion batteries, and more specifically relates to an organic positive electrode material for lithium ion batteries, a preparation method and application thereof. It is a polymer formed by copolymerization of pyrene or pyrene derivatives as comonomers; the organic positive electrode material uses the conjugated aromatic fused ring of pyrene as the electrochemical redox site, based on the anion intercalation mechanism of the conjugated aromatic fused ring , increase the potential of the redox electrode, increase the output voltage of the lithium-ion battery, thereby increasing the energy density of the positive electrode material. The lithium ion battery made of the material provided by the invention has high energy density, good cycle stability and rate performance, and is expected to be used in next-generation high energy density, environment-friendly and sustainable energy storage batteries.

Description

technical field [0001] The invention belongs to the field of preparation of lithium ion cathode materials, and more specifically relates to an organic cathode material for lithium ion batteries, a preparation method and application thereof. Background technique [0002] Lithium-ion batteries are widely used in portable electronic devices due to their high energy density and power density. In recent years, with the further deepening of research technology and the expansion of application fields, there is a huge demand for lithium-ion batteries in the field of electric vehicles and even large-scale energy storage. [0003] How to further improve the performance of lithium-ion batteries is a research hotspot in the field of energy storage. The quality of the positive electrode material of lithium-ion battery determines the level of battery capacity. Traditional lithium-ion battery cathode materials are lithium-containing inorganic metal oxides or phosphates, etc., whose price...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01M4/60H01M4/137H01M10/0525
CPCH01M4/1399H01M4/608H01M10/0525H01M2004/028Y02E60/10
Inventor 王成亮唐蜜刘视远吴艳超陈远姜澄
Owner HUAZHONG UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com