A kind of preparation method based on aramid fiber 1414 fiber composite material

A technology of fiber composite materials and aramid fibers, which is applied in fiber processing, spinning solution preparation, wet spinning, etc., can solve the problems of restricting market development, high performance and stability requirements, and achieve sufficient dissolution, strength, and The effect of improving performance

Active Publication Date: 2021-04-27
BLUESTAR CHENGDU NEW MATERIALS
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Because the aramid 1414 composite material has high requirements on the performance and stability of the aramid 1414 precursor, and requires good adhesion between the fiber and the epoxy resin or rubber matrix, the currently produced aramid 1414 fiber composite material cannot meet the requirements. Actual demand, which also limits its market development in high-end applications

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method based on aramid fiber 1414 fiber composite material
  • A kind of preparation method based on aramid fiber 1414 fiber composite material
  • A kind of preparation method based on aramid fiber 1414 fiber composite material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] A preparation method based on aramid fiber 1414 fiber composite material, comprising the steps of:

[0038] A. polymerization

[0039] First, weigh the raw material poly-p-phenylene terephthalamide (PPDA) and raw material terephthaloyl chloride (TPC); dissolve poly-p-phenylene terephthalamide in NMP / CaCl 2 In the process, the premix is ​​obtained, and then placed in the prepolymer mixer; secondly, 50% terephthaloyl chloride is also placed in the prepolymer mixer, and the two are reacted to obtain the prepolymer, and then the The prepolymer and the remaining 50% of terephthaloyl chloride were mixed in a polymerization mixer to obtain a mixture; finally, the mixture was placed in a polymerization reactor for 6 minutes to obtain a polymer;

[0040] Grinding, beating, washing, purifying and drying the polymer, storing it for later use;

[0041] B. spinning

[0042] Put the polymer obtained in step A in a dissolving mixer, and at the same time, pass sulfuric acid into t...

Embodiment 2

[0046] On the basis of Embodiment 1, the difference of this embodiment is:

[0047] In step A, the reaction 7min of the mixture in the polymerization reactor;

[0048] In step B, after passing sulfuric acid into the dissolution mixer, it was mixed and dissolved at 85°C for 60 minutes;

[0049] In step B, heat treatment at 170°C for 0.8s;

[0050] In step C, in the oiling treatment, the oil content is controlled to 0.75%.

Embodiment 3

[0052] On the basis of embodiment 1-2, the difference of this embodiment is:

[0053] In step A, the reaction 7min of the mixture in the polymerization reactor;

[0054] In step B, after passing sulfuric acid into the dissolution mixer, it was mixed and dissolved at 80°C for 40 minutes;

[0055] In step B, heat treatment at 150°C for 0.5s;

[0056] In step C, in the oiling treatment, the oil content is controlled to 0.68%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
elongation at breakaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of aramid fiber 1414 fiber composite material, which belongs to the technical field of artificial fiber and composite material. The present invention uses poly-p-phenylene terephthalamide and terephthaloyl chloride as raw materials, and through polymerization, spinning and post-treatment, the temperature, viscosity, time, content, spinning speed, tension and other condition parameters in the production process are adjusted. The strict control can effectively ensure the stable production process based on aramid 1414 fiber composite materials, and at the same time, improve the quality of the target composite materials to meet market demand.

Description

technical field [0001] The invention relates to a method for preparing a composite material based on aramid 1414 fibers, in particular to a method for preparing a high-strength composite material based on aramid 1414 fibers, and belongs to the technical field of artificial fibers and composite materials. Background technique [0002] Aramid 1414 composite materials are widely used in the fields of national defense, military industry and modern industry because of their characteristics of high tensile strength, light weight, and fatigue resistance. The material market has a large capacity. [0003] At present, my country has a huge demand for aramid 1414 composite materials. For example, the Military Supplies Department of the General Logistics Department needs more than 500 tons per year, which are mainly used to equip the troops with bulletproof vests, bulletproof vests, and bulletproof helmets; the aerospace sector needs dozens of tons every year. For rocket engine casings...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L63/00C08L21/00C08L77/10D01F6/60C08G69/32C08G69/04D01D1/02D01D5/06D01D10/02D06B3/04D06M15/53D06M13/224
Inventor 毛亚丽崔晓静孙潜殷小吉黄昱
Owner BLUESTAR CHENGDU NEW MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com